Polymer Property : Shear Strength = 1.03 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	>= 1.03 MPa	>= 149 psi	Lap
Parker Chomerics CHO-BOND® 1121 General Purpose Adhesive-Sealant Silver Silicone Description: Xylene-free version of CHO-BOND 1038; rec. bond line thickness: > 0.18 mm; primer promotes adhesion CHO-BOND® 1121 is an electrically conductive, one-component silicone adhesive-sealan..
Shear Strength	>= 1.03 MPa	>= 149 psi
Parker Chomerics Tecknit® 0002 Highly Conductive Adhesive-Sealant Silver Silicone Description: TECKNIT® 0002 is a pure silver filled, one component RTV silicone adhesive-sealant. It is ready to use without mixing and cures quickly at room temperature on exposure to moisture in ..
Shear Strength	>= 1.03 MPa	>= 149 psi	Cured; ASTM D1002
Parker Chomerics Tecknit® 72-00151 Silver-Filled Flexible Resin Caulking System Description: TECKNIT standard electrically conductive caulks consist of four one-component resin systems filled with silver plated glass or copper particles. These systems are formulated to provide ..
Shear Strength	>= 1.03 MPa	>= 149 psi	Cured; ASTM D1002
Parker Chomerics Tecknit® 72-00152 Silver-Filled Flexible Resin Caulking System Description: TECKNIT standard electrically conductive caulks consist of four one-component resin systems filled with silver plated glass or copper particles. These systems are formulated to provide ..
Shear Strength	>= 1.03 MPa	>= 149 psi	Cured; ASTM D1002
Parker Chomerics Tecknit CON/RTV-I One Part: Silver-Filled Silicone RTV Description: TECKNIT CON/RTV-I system is a pure silver loaded, one component RTV silicone adhesive sealant. It is ready to use without mixing and cures quickly at room temperature on exposure to moi..
Shear Strength	1.03 - 1.38 MPa	150 - 200 psi	Tensile, Al to Al
Master Bond MasterSil 707FR Flame Retardant Silicone Adhesive Description: MasterSil 707FR is a one component, high performance RTV silicone that is mainly used for its flame retardancy. It is UL listed with a flame classification for 94V-1 for thicknesses of ..
Shear Strength	1.03 - 1.38 MPa	150 - 200 psi	Tensile, Al to Al
Master Bond MasterSil 708FR One Part, Flame Resistant Silicone Description: MasterSil 708FR is a one component, high performance RTV silicone that is mainly used for its flame retardancy. It is UL listed with a flame classification for 94V.1 for thicknesses of ..
Shear Strength	1.03 MPa	150 psi	Plate Shear, W Direction, typ
Hexcel® HexWeb® CR III 3/16-5056-.001 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR..
Shear Strength	>= 1.03 MPa	>= 150 psi	Plate Shear, W Direction, min
Hexcel® HexWeb® CR III 3/8-5052-.003 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR..
Shear Strength	1.03 MPa	150 psi	Plate Shear, W Direction, typ
Hexcel® HexWeb® HRH-327 - 3/8 - 4.0 Fiberglass Reinforced Polyimide Honeycomb Designation: Material-Cell Size (inches)-DensityHexWeb® HRH-327 is a glass-fabric, bias weave reinforced plastic honeycomb that incorporates a polyimide resin system for the node adhesive as well a..
Shear Strength	>= 1.03 MPa	>= 150 psi	Plate Shear, W Direction, min
Hexcel® HexWeb® HRP - 3/8 - 4.5 Fiberglass/Phenolic Honeycomb Designation: Material-Cell Size (inches)-DensityHexWeb HRP is a glass fabric reinforced honeycomb in which a heat-resistant phenolic resin is used both for initial and final impregnations. This prod..
Shear Strength	1.03 MPa	150 psi	Plate Shear, W Direction, typ
Hexcel® HexWeb® HRP/OX - 3/8 - 3.2 Fiberglass/Phenolic Honeycomb Designation: Material-Cell Size (inches)-DensityHexWeb HRP is a glass fabric reinforced honeycomb in which a heat-resistant phenolic resin is used both for initial and final impregnations. This prod..
Shear Strength	1.03 MPa	150 psi	Plate Shear, W Direction, typ
Hexcel® HexWeb® CR-PAA™ 3/16-5056-0.001 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa..
Shear Strength	>= 1.03 MPa	>= 150 psi	Plate Shear, W Direction, min
Hexcel® HexWeb® CR-PAA™ 3/8-5052-0.003 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa..
Shear Strength	>= 1.03 MPa	>= 150 psi	Plate Shear, W Direction, min
Hexcel® HexWeb® HRH-10 - 1/8- 5.0 Aramid Fiber/Phenolic Resin Honeycomb Designation: Material-Cell Size-Density.Hexweb HRH-10 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the h..
Shear Strength	>= 1.03 MPa	>= 150 psi	Plate Shear, W Direction, min
Hexcel® HexWeb® HRH-10/F35 - 4.5 Nonmetallic Flex-Core Honeycomb Designation: Material/Cell Size (cells per lineal foot in W direction)-DensityHexcel manufactures two types of nonmetallic reinforced plastic HexWeb Flex-Core: HexWeb HRP - Fiberglasses cloth reinfo..
Shear Strength	1.03 MPa	150 psi	Plate Shear, W Direction, typ
Hexcel® HexWeb® HRH-10/OX - 3/16 - 4.0 Aramid Fiber/Phenolic Resin Honeycomb Designation: Material-Cell Size-Density.Hexweb HRH-10 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the h..
Shear Strength	1.03 MPa	150 psi	Overlap, Abraded Aluminum, 14 days in 5% salt spray @ 35°C
3M Scotch-Weld™ DP110 Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M
Shear Strength	1.03 MPa	150 psi	Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, Neoprene/Steel
3M Scotch-Weld™ DP420 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M
Shear Strength	1.03 MPa	150 psi	Overlap, Isopropyl Alcohol Wipe surface prep, Neoprene/Steel
3M Scotch-Weld™ DP420 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M
Shear Strength	1.03 MPa	150 psi	Overlap, Isopropyl Alcohol Wipe surface prep, SBR/Steel
3M Scotch-Weld™ DP460 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP460 Off-White and DP460 NS are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion and very high levels of durability.Informat..
Shear Strength	1.03 MPa	150 psi	Overlap, Acetal, Adhesive Failure
3M Scotch-Weld™ DP8010NS Structural Adhesive 3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8010NS is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of Polyprop..
Shear Strength	1.03 MPa @Temperature 66.0 °C	150 psi @Temperature 151 °F	Overlap, Polyurethane Finish, Adhesive Failure
3M Scotch-Weld™ Thin Instant Wood Adhesives and Surface Activator 3M™ Scotch-Weld™ Instant Wood Adhesives an Surface Activator are single component, room temperature-curing adhesives that provides cure and speed and shear strength for demanding applications in t..
Shear Strength	1.03 MPa	149 psi	Overlap, Acrylic, 50% RH
3M 5200 Marine Adhesive/Sealant Fast Cure A fast curing, one-part polyurethane that chemically reacts with moisture to deliver strong, flexible bonds with excellent adhesion to wood and fiberglass. Forms watertight, weather-resistant seals ..
Shear Strength	1.03 MPa @Temperature 82.0 °C	150 psi @Temperature 180 °F	Overlap
3M Scotch-Weld™ DP-105 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP105 Clear is a fast setting, very flexible 1:1 mix ratio epoxy adhesive/sealant. Its flexibility when cured makes it ideal for applications involving dissimilar s..
Shear Strength	1.03 MPa	150 psi
3M Scotch-Weld™ DP5105 Structural Adhesive Low temperature flexibility and Expansion joint sealsInformation provided by 3M
Shear Strength	1.03 MPa	150 psi	Lap; 2.5cm aluminum strips, 13mm overlap, 0.25mm thick adhesive layer
Parker Chomerics CHO-BOND 1038 Conductive Silicone RTV Adhesive Electrically conductive, one component silicone adhesive/sealant that may be used for bonding EMI gaskets or for providing EMI and environmental protection as a caulk. This material cures on exposur..
Shear Strength	1.03 MPa @Temperature 82.0 °C	150 psi @Temperature 180 °F	Steel Overlap; ASTM D1002
3M Scotch-Weld™ 3501 B/A Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 3501 B/A Gray is a rapid room temperature curing, two-part epoxy adhesives for use in bonding many metals, wood, and a variety of plastics. Equal parts by volume ar..
Shear Strength	1.03 MPa	150 psi	Overlap, Abraded Aluminum, 14 days in 5% salt spray @ 35°C
3M Scotch-Weld™ DP110 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M
Shear Strength	1.03 MPa @Temperature 82.0 °C	150 psi @Temperature 180 °F	Overlap
3M Scotch-Weld™ DP125 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP125 Translucent is a faster curing version of 3M Scotch-Weld Epoxy Adhesive 2216 Translucent B/A. The worklife and cure time has been reduced from hours and days ..