Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | >= 3.45 MPa | >= 500 psi | Lap, Kaptona |
Resin Technology Group TIGA 920H Flexible Silver Conductive 100 parts resin to 115 parts hardener.TIGA 920-H is a flexible, conductive silver filled epoxy adhesive. It is recommended for bonding, and sealing electronic applications that require high flexibil.. |
|||
Shear Strength | >= 3.45 MPa | >= 500 psi | Plate Shear, L Direction, min |
Hexcel® HexWeb® CR III 3/8-5052-.005 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR.. |
|||
Shear Strength | >= 3.45 MPa | >= 500 psi | Plate Shear, L Direction, min |
Hexcel® HexWeb® CR-PAA™ 3/8-5052-0.005 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa.. |
|||
Shear Strength | 3.45 MPa | 500 psi | silicone property; ASTM D1002 |
Arlon Thermabond® 99180T010 Silicone Rubber/Fiberglass Laminate Low outgassing, thermally conductive, electrically insulating, Thermabond®. Bonds with primer. Liner: 1 mil FEP; Product: uncured silicone rubber; Carrier: 3 mil PTFE coated fiberglass. |
|||
Shear Strength | 3.45 MPa | 500 psi | Lap Shear Strength; ASTM D1002 |
Arlon Thermabond® 99730N015 0.015" (0.381 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier Description: Electrically Conductive - Thermabond®. Bonds with primer.Design/Construction: Liner: FEP Product: Uncured Silicone Rubber Carrier: PTFE Coated FiberglassRecommended Primers: Dow Coring.. |
|||
Shear Strength | 3.45 MPa @Temperature 82.0 °C |
500 psi @Temperature 180 °F |
Overlap, Aluminum FPL Etch; ASTM D1002-72 |
3M Scotch-Weld™ 1751 B/A Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 1751 B/A is a gray, aluminum filled, two-part, room temperature curing structural adhesive.Information provided by 3M |
|||
Shear Strength | 3.45 MPa @Temperature 82.0 °C |
500 psi @Temperature 180 °F |
Aluminum Overlap; ASTM D1002 |
3M Scotch-Weld™ 183 B/A Green Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 1838 B/A is a controlled flow product. This epoxy adhesives are two-part, room temperature curing structural adhesives with high shear strengths and excellent envir.. |
|||
Shear Strength | 3.45 MPa | 500 psi | Overlap, Etched Aluminum, 14 days in 5% salt spray @ 35°C |
3M Scotch-Weld™ DP110 Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M |
|||
Shear Strength | 3.45 MPa | 500 psi | Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, ABS PVC |
3M Scotch-Weld™ DP420 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 3.45 MPa | 500 psi | Overlap, Isopropyl Alcohol Wipe surface prep, PVC |
3M Scotch-Weld™ DP460 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP460 Off-White and DP460 NS are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion and very high levels of durability.Informat.. |
|||
Shear Strength | 3.45 MPa | 500 psi | Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, Polycarbonate |
3M Scotch-Weld™ DP460 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP460 Off-White and DP460 NS are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion and very high levels of durability.Informat.. |
|||
Shear Strength | 3.45 MPa | 500 psi | |
3M Scotch-Weld™ DP5003 Structural Adhesive Non-sag and Vertical applicationsInformation provided by 3M |
|||
Shear Strength | 3.45 MPa | 500 psi | Overlap, Polycarbonate, Adhesive/Cohesive Failure |
3M Scotch-Weld™ DP810 Black Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 3.45 MPa @Temperature 82.0 °C |
500 psi @Temperature 180 °F |
Overlap |
3M Scotch-Weld™ DP810 Black Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 3.45 MPa | 500 psi | Overlap at 10 minutes after bonding |
3M Scotch-Weld™ DP810NS Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 3.45 MPa | 500 psi | Overlap, Polycarbonate, Adhesive/Cohesive Failure |
3M Scotch-Weld™ DP810NS Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 3.45 MPa @Temperature 82.0 °C |
500 psi @Temperature 180 °F |
Overlap |
3M Scotch-Weld™ DP810NS Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 3.45 MPa @Temperature 177 °C |
500 psi @Temperature 351 °F |
Etched Aluminum Overlap |
3M Scotch-Weld™ EC-2086 Structural Adhesive 3M™ Scotch-Weld™ Structural Adhesive EC-2086 is a one-part, 100% solids thermosetting liquid adhesives.Information provided by 3M |
|||
Shear Strength | 3.45 MPa | 500 psi | Overlap, Wood/Wood |
3M Fastbond™ 4213-NF Industrial Adhesive 3M™ Fastbond™ Industrial Adhesive 4213-NF is a white, water dispersed adhesive for bonding many fabrics, supported vinyl, wood, leather and most porous materials. Exhibits outstanding clarity when.. |
|||
Shear Strength | 3.45 MPa @Temperature 66.0 °C |
500 psi @Temperature 151 °F |
Overlap, HDPE, Cohesive Failure |
3M Scotch-Weld™ DP8005 Translucent Structural Adhesive 3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8005 is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of polypropyl.. |
|||
Shear Strength | 3.45 MPa @Temperature 82.0 °C |
500 psi @Temperature 180 °F |
Overlap |
3M Scotch-Weld™ DP810 Tan Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 3.45 - 6.89 MPa | 500 - 1000 psi | Lap; ASTM D1002 |
3M Scotch-Weld™ GM10 Gasket Maker Anaerobic Adhesive 3M™ Scotch-Weld™ Gasket Maker Anaerobic Adhesives are one-component anaerobic sealants formulated to replace pre-cut gaskets or used as form-in-place gaskets that cure at room temperature and seal.. |
|||
Shear Strength | 3.45 MPa | 500 psi | Overlap, Polyurethane Finish, Adhesive Failure |
3M Scotch-Weld™ Medium Instant Wood Adhesives and Surface Activator 3M™ Scotch-Weld™ Instant Wood Adhesives an Surface Activator are single component, room temperature-curing adhesives that provides cure and speed and shear strength for demanding applications in t.. |
|||
Shear Strength | 3.45 MPa | 500 psi | Overlap, Etched Al, Salt Spray at RT for 30 days |
3M Scotch-Weld™ 2216 B/A Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 2216 B/A is a flexible, two-part, room temperature curing epoxy with high peel and shear strength. Scotch-Weld epoxy adhesive 2216 B/A is identical to 3M Scotch-Wel.. |
|||
Shear Strength | 3.45 MPa @Temperature 82.0 °C, Time 3.46e+6 sec |
500 psi @Temperature 180 °F, Time 960 hour |
Overlap, Cured for 7 days at 24°C |
3M Scotch-Weld™ 2216 B/A Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 2216 B/A is a flexible, two-part, room temperature curing epoxy with high peel and shear strength. Scotch-Weld epoxy adhesive 2216 B/A is identical to 3M Scotch-Wel.. |
|||
Shear Strength | 3.45 MPa | 500 psi | On Douglas Fir |
3M Scotch-Weld™ 3750 Tan Hot Melt Adhesive Low viscosity for high flow rate, increased production and Good hot tack, quick grab for packaging and woodworkingInformation provided by 3M |
|||
Shear Strength | 3.45 MPa | 500 psi | On Douglas Fir |
3M Scotch-Weld™ 3755LM Low Melt Adhesive “Delayed-tack” applied in thin-glue-line ribbon for paper, corrugated, chipboard, displays, exhibits and Use with low melt applicator onlyInformation provided by 3M |
|||
Shear Strength | 3.45 MPa | 500 psi | Overlap, ABS/ABS Plastic |
3M Scotch-Weld™ DP110 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M |
|||
Shear Strength | 3.45 MPa | 500 psi | Overlap, Etched Aluminum, 14 days in 5% salt spray @ 35°C |
3M Scotch-Weld™ DP110 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M |
|||
Shear Strength | 3.45 - 6.89 MPa | 500 - 1000 psi | Lap; ASTM D1002 |
3M Scotch-Weld™ GM15 Gasket Maker Anaerobic Adhesive 3M™ Scotch-Weld™ Gasket Maker Anaerobic Adhesives are one-component anaerobic sealants formulated to replace pre-cut gaskets or used as form-in-place gaskets that cure at room temperature and seal.. |