Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 9.65 MPa @Temperature 100 °C, Time 2700 sec |
1400 psi @Temperature 212 °F, Time 0.750 hour |
Lap |
Parker Chomerics CHO-BOND 360-208 Conductive Epoxy Low cost, electrically conductive epoxy adhesive that combines the good adhesive characteristics as epoxy, and the superior electrical conductivity of silver. It is recommended as a thermo-setting E.. |
|||
Shear Strength | 9.66 MPa @Temperature 116 °C, Time 900 sec |
1400 psi @Temperature 240 °F, Time 0.250 hour |
Lap |
Parker Chomerics CHO-BOND 589-29 Conductive Epoxy Low cost, highly conductive adhesive system which combines the strong adhesion characteristics of an epoxy with the superior conductivity of silver. CHO-BOND 589-29 adhesive meets the most exacting .. |
|||
Shear Strength | >= 9.65 MPa | >= 1400 psi | Cured; ASTM D1002 |
Parker Chomerics Tecknit® 72-08116 Silver-Filled Epoxy System Description: This is a silver filled epoxy system designed for maximum performance and lowest volume resistivity. It is easily mixed 1:1 by volume or weight, from the two one-ounce jars. Its consist.. |
|||
Shear Strength | 9.65 MPa | 1400 psi | Cured 1 hour at 125°C, Al/Al |
Resin Technology Group TIGA 908 Gold Bonder - Low Stress Silver Conductive 100 parts resin to 6 parts hardener.TIGA 908 is a low stress, conductive silver filled epoxy adhesive. It is recommended for bonding, and sealing electronic applications which require bonding to gol.. |
|||
Shear Strength | 9.65 - 11.0 MPa | 1400 - 1600 psi | |
ITW Plexus Plexusâ„¢ MA1023 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.Low shrinkage, low odor, all purpose.Information provided by Illinois Tool Works. |
|||
Shear Strength | >= 9.65 MPa | >= 1400 psi | Tensile lap, Al to Al |
Master Bond EP51FL Toughened and Flexible Adhesive Compound Master Bond EP51FL is a two component epoxy system for high performance bonding sealing and coating. It combines superior toughness with user friendly handling properties, along with unusually fast .. |
|||
Shear Strength | 9.65 MPa | 1400 psi | Lap |
Epoxy Technology EPO-TEK® H31LV Electrically Conductive, Silver Epoxy Product Description: EPO-TEK® H31LV is a single component, silver-filled, electrically conductive epoxy designed for semiconductor die attach applications found in hybrids, JEDEC, and opto-electron.. |
|||
Shear Strength | 9.65 MPa @Temperature -55.0 °C |
1400 psi @Temperature -67.0 °F |
Overlap, Aluminum FPL Etch; ASTM D1002-72 |
3M Scotch-Weld™ 1751 B/A Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 1751 B/A is a gray, aluminum filled, two-part, room temperature curing structural adhesive.Information provided by 3M |
|||
Shear Strength | 9.65 MPa | 1400 psi | Overlap, Fiber Reinforced Polyester/Fiber Reinforced Polyester |
3M Scotch-Weld™ DP110 Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M |
|||
Shear Strength | 9.65 MPa | 1400 psi | Overlap, CRS |
3M Scotch-Weld™ DP190 Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP190 Gray is a 1:1 mix ratio similar to Scotch-Weld™ Epoxy Adhesive 2216 B/A Gray and exhibits good peel, shear and environmental aging properties.Information pro.. |
|||
Shear Strength | 9.65 MPa | 1400 psi | Overlap, Isopropyl Alcohol Wipe surface prep, SBR/Steel |
3M Scotch-Weld™ DP420 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 9.65 MPa | 1400 psi | Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, SBR/Steel |
3M Scotch-Weld™ DP420 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 9.65 MPa | 1400 psi | Overlap, Isopropyl Alcohol Wipe surface prep, Phenolic |
3M Scotch-Weld™ DP460 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP460 Off-White and DP460 NS are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion and very high levels of durability.Informat.. |
|||
Shear Strength | 9.65 MPa | 1400 psi | Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, Phenolic |
3M Scotch-Weld™ DP460 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP460 Off-White and DP460 NS are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion and very high levels of durability.Informat.. |
|||
Shear Strength | 9.65 MPa @Time 3600 sec |
1400 psi @Time 1.00 hour |
Aluminum, Overlap |
3M Scotch-Weld™ DP460 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP460 Off-White and DP460 NS are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion and very high levels of durability.Informat.. |
|||
Shear Strength | 9.65 MPa | 1400 psi | Overlap, Fiberglass |
3M Scotch-Weld™ DP-105 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP105 Clear is a fast setting, very flexible 1:1 mix ratio epoxy adhesive/sealant. Its flexibility when cured makes it ideal for applications involving dissimilar s.. |
|||
Shear Strength | 9.65 MPa | 1400 psi | Overlap, PVC, Substrate Failure |
3M Scotch-Weld™ DP825 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP825 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact, durability and.. |
|||
Shear Strength | 9.65 MPa | 1400 psi | Overlap, Fiber Reinforced Polyester/Fiber Reinforced Polyester |
3M Scotch-Weld™ DP110 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M |
|||
Shear Strength | 9.65 MPa | 1400 psi | Overlap, Sanded Aluminum |
3M Scotch-Weld™ DP125 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP125 Translucent is a faster curing version of 3M Scotch-Weld Epoxy Adhesive 2216 Translucent B/A. The worklife and cure time has been reduced from hours and days .. |
|||
Shear Strength | 9.65 MPa | 1400 psi | Overlap, Isopropyl Alcohol Wipe surface prep, SBR/Steel |
3M Scotch-Weld™ DP420 Black Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 9.65 - 11.7 MPa | 1400 - 1700 psi | |
ITW Plexus Plexus™ MA922 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.All purpose, low odor, medium open time.Information provided by Illinois Tool Works. |
|||
Shear Strength | 9.65 - 11.7 MPa | 1400 - 1700 psi | |
ITW Plexus Plexus™ MA925 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.All purpose, low odor, long open time.Information provided by Illinois Tool Works. |