Mechanical Properties	Metric	English	Comments
Shear Strength	18.6 - 22.1 MPa	2700 - 3200 psi
ND Industries SuperGlue Ethyl 320 Very low viscosity for pre-assembled componentsMeets military spec Mil-A-46050C Type II Class I
Shear Strength	18.6 - 22.1 MPa	2700 - 3200 psi
ND Industries SuperGlue Ethyl 325 Low-Medium Viscosity - General purposeMeets military spec Mil-A-46050C Type II Class I
Shear Strength	>= 18.6 MPa	>= 2700 psi	Al/Al, Tensile lap
Master Bond EP21TDCHTND Versatile, toughened two component epoxy for bonding, sealing and coating Product Description: Master Bond EP21TDCHTND is a two component epoxy adhesive, sealant and coating featuring high performance, versatility and exceptional user friendliness. It has a very forgiving..
Shear Strength	18.6 MPa	2700 psi	Tensile lap, Al to Al
Master Bond EP41S-1HT Solvent Resistant Adhesive, Sealant and Coating Description: Master Bond EP41S-1HT is a two component epoxy resin system for high performance bonding, sealing, coating and encapsulating. It has a 100 to 30 mix ratio by weight and is formulated to..
Shear Strength	18.6 MPa	2700 psi	Tensile lap, Al to Al
Master Bond EP41S-1HTND Non-Drip, High Performance Epoxy Adhesive Description: Master Bond EP41S-1HTND is a two component epoxy resin system for high performance bonding, sealing and coating. It has a 100 to 30 mix ratio by weight and its viscosity is a smooth pas..
Shear Strength	>= 18.6 MPa	>= 2700 psi	Tensile lap, Al to Al
Master Bond Supreme 10AOHT-LO High Shear and Peel Strength Epoxy Description: Master Bond Supreme 10AOHT-LO has a combination of properties consisting of excellent thermal conductivity, superior electrical insulation, great adhesion to a wide variety of substrate..
Shear Strength	18.6 MPa @Temperature -55.0 °C	2700 psi @Temperature -67.0 °F	Overlap
3M Scotch-Weld™ DP110 Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M
Shear Strength	18.6 MPa	2700 psi	Overlap, CRS MEK/abrade/MEK
3M Scotch-Weld™ DP420 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M
Shear Strength	18.6 MPa	2700 psi	Overlap, Cold Rolled Steel (oily)
3M Scotch-Weld™ DP805 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP805 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability ..
Shear Strength	18.6 MPa	2700 psi	Overlap, FR-4/FR-4 tested after 120°C/2 wks
3M Scotch-Weld™ DP805 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP805 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability ..
Shear Strength	18.6 MPa	2700 psi	Overlap at 2 hrs after bonding
3M Scotch-Weld™ DP810 Black Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre..
Shear Strength	18.6 MPa	2700 psi	Overlap, CRS - MEK/abraded/MEK, Cohesive failure; ASTM D1002
3M Scotch-Weld™ DP920 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP920 is a two-part, 2:1 mix ratio, toughened epoxy structural adhesive with a 20 minute work life. It exhibits excellent shear and peel strengths along with good i..
Shear Strength	18.6 MPa @Temperature 24.0 °C	2700 psi @Temperature 75.2 °F	Solvent Wiped Cold Rolled Steel Overlap
3M Scotch-Weld™ EC-2086 Structural Adhesive 3M™ Scotch-Weld™ Structural Adhesive EC-2086 is a one-part, 100% solids thermosetting liquid adhesives.Information provided by 3M
Shear Strength	18.6 MPa	2700 psi	Overlap, Aluminum-Anodized-Cohesion Failure; ASTM D1002
3M Scotch-Weld™ LSB90 Flexible Epoxy 3M™ Scotch-Weld™ Epoxy Adhesive LSB90 is a high performance, two-part, flexible epoxy adhesive offering high shear and peel adhesion and very high levels of durability. It has a 90 minute worklife..
Shear Strength	18.6 MPa @Temperature 23.0 °C	2700 psi @Temperature 73.4 °F	Aluminum, Overlap; ASTM D1002
3M Scotch-Weld™ LSB90 Flexible Epoxy 3M™ Scotch-Weld™ Epoxy Adhesive LSB90 is a high performance, two-part, flexible epoxy adhesive offering high shear and peel adhesion and very high levels of durability. It has a 90 minute worklife..
Shear Strength	18.6 MPa	2700 psi	ASTM D1002-94
Aremco Aremco-Bond™ 2220 High Performance Epoxide Ceramic-Filled, High Chemical Resistance, Machinable. For Repairing Deeply-Corroded Parts.
Shear Strength	18.6 MPa	2700 psi	Overlap, Aluminum, Adhesive Failure
3M Scotch-Weld™ Thick Instant Wood Adhesives and Surface Activator 3M™ Scotch-Weld™ Instant Wood Adhesives an Surface Activator are single component, room temperature-curing adhesives that provides cure and speed and shear strength for demanding applications in t..
Shear Strength	18.6 MPa	2700 psi	cured, lap, Alum to Alum
Atom Adhesives AA-BOND F253 Epoxy Adhesive AA-BOND F253 is a low viscosity, high temperature, two-part epoxy formulation that changes color during the curing process to indicate cure status.Appearance: Unmixed-Light Yellow; Mixed – Greenish..
Shear Strength	18.6 MPa	2700 psi	Overlap, after salt spray 30 days @ 23°C
3M Scotch-Weld™ DP100 FR Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP100 FR is a two-part flame retardant (self-extinguishing) version of Scotch-Weld DP100. It meets the UL94 V-O Burn Test requirements and has a work life of 4-8 mi..
Shear Strength	18.6 MPa	2700 psi	Overlap, FRP(Red)-IPA/abrade/IPA, Substrate Failure
3M Scotch-Weld™ LSB60 Toughened Epoxy Adhesives 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LBS60 is a high performance, two-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of f..
Shear Strength	18.6 MPa	2700 psi	Overlap, Etched Al, Tap water at RT for 30 days
3M Scotch-Weld™ 2216 B/A Tan NS Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 2216 B/A is a flexible, two-part, room temperature curing epoxy with high peel and shear strength. Scotch-Weld epoxy adhesive 2216 B/A is identical to 3M Scotch-Wel..