- RheTech Products FT1004-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black
RheTech Products FT1004-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black
| Category | Polymer , Thermoplastic , Polyolefin |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products FT1004-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Step padsHitch padsScuff platesInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.930 g/cc | 0.930 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 4 % | 4 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0115 cm/cm | 0.0115 in/in | ASTM D955 |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 230 °C |
13 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 62 | 62 | ASTM D2240 |
| Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 0.758 GPa | 110 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm @Temperature 23.0 °C |
15.0 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 18.0 J | 13.3 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 76.7 °C | 170 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 188 - 216 °C | 370 - 420 °F | |
| Middle Barrel Temperature | 193 - 221 °C | 380 - 430 °F | |
| Front Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Nozzle Temperature | 204 - 216 °C | 400 - 420 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- LyondellBasell Microthene® G MN70100 Low Density Polyethylene
- ICE Mullite, 3Al2O3-SiO2
- Techmer ES HiFill® PA4/6 GF33 HS NAT 33% Glass Filled (Conditioned)
- Chase Plastics CP Pryme® PC320GR Polycarbonate (Utility Grade), 20% Glass Fiber Reinforced, Mold Release
- Chevron Phillips Marlex® HHM 5502 LD High Density Ethylene Hexene Copolymer with Antistat
- Aclo Accutech Polypropylene Homopolymer HP0339G25M5CL Glass/Mineral Reinforced Coupled
- 3M FL012 Lexan Label Product
- Resinlab® TL5090 Anaerobic Threadlocking Compound
Copyright © lookpolymers.com All Rights Reserved