Ascend Performance Materials Vydyne® 909 Nylon 66/6, 25% Glass Reinforced, Ignition Resistant, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 30% Glass Fiber Reinforced
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 909 Nylon 66/6, 25% Glass Reinforced, Ignition Resistant, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® 909 is halogenated, 25% glass-filled, flame-retardant PA66/6 copolymer with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has an Underwriters Laboratories UL 94 flammability classification of V-0 at 0.4 mm (0.016”) thick.Availability:Asia PacificEuropeNorth AmericaAdditive:HalogenLubricantFeatures:Good Crack ResistanceGood Mold ReleaseGood ToughnessHalogenatedHigh RigidityHigh StrengthIgnition ResistanceLubricatedUses:AppliancesAutomotive ElectronicsBobbinsConnectorsElectrical HousingElectrical PartsElectrical/Electronic ApplicationsFastenersIndustrial ApplicationsLighting ApplicationsLiving HingesPrinted Circuit BoardsSwitchesAppearance: Natural ColorForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend
Physical Properties Metric English Comments
Specific Gravity 1.47 g/cc
1.47 g/cc
ISO 1183
Water Absorption 0.70 %
0.70 %
24 hrs; ISO 62
Moisture Absorption at Equilibrium 1.5 %
1.5 %
50%rh; ISO 62
Linear Mold Shrinkage 0.0040 cm/cm

@Thickness 2.00 mm
 0.0040 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Thickness 2.00 mm
 0.010 in/in

@Thickness 0.0787 in
 ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 132 MPa
19100 psi
ISO 527-2
Elongation at Break 2.2 %
2.2 %
ISO 527-2
Tensile Modulus 9.10 GPa
1320 ksi
ISO 527-2
Flexural Strength 193 MPa
28000 psi
ISO 178
Flexural Modulus 9.30 GPa
1350 ksi
ISO 178
Poissons Ratio 0.37
0.37
ISO 527-2
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
ISO 180
Charpy Impact Unnotched 3.50 J/cm²

@Temperature -30.0 °C
 16.7 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
4.00 J/cm²

@Temperature 23.0 °C
 19.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.940 J/cm²

@Temperature 23.0 °C
 4.47 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
0.950 J/cm²

@Temperature -30.0 °C
 4.52 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 2.00 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
 1.11 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
 5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
 ISO 11359-2
Melting Point 250 °C
482 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 230 °C
446 °F
ISO 75-2/A
UL RTI, Electrical 65.0 °C

@Thickness 4.00 mm
 149 °F

@Thickness 0.157 in
 UL 746B
130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
 UL 746B
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
 UL 746B
130 °C

@Thickness 0.750 mm
 266 °F

@Thickness 0.0295 in
 UL 746B
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.400 mm
 149 °F

@Thickness 0.0157 in
 UL 746B
65.0 °C

@Thickness 0.750 mm
 149 °F

@Thickness 0.0295 in
 UL 746B
95.0 °C

@Thickness 1.50 mm
 203 °F

@Thickness 0.0591 in
 UL 746B
95.0 °C

@Thickness 3.00 mm
 203 °F

@Thickness 0.118 in
 UL 746B
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.400 mm
 149 °F

@Thickness 0.0157 in
 UL 746B
110 °C

@Thickness 1.50 mm
 230 °F

@Thickness 0.0591 in
 UL 746B
110 °C

@Thickness 3.00 mm
 230 °F

@Thickness 0.118 in
 UL 746B
110 °C

@Thickness 0.750 mm
 230 °F

@Thickness 0.0295 in
 UL 746B
Flammability, UL94 V-0

@Thickness 0.400 - 3.00 mm
 V-0

@Thickness 0.0157 - 0.118 in
5VA

@Thickness 1.50 mm
 5VA

@Thickness 0.0591 in
Oxygen Index 32 %
32 %
ASTM D2863
Glow Wire Test 750 °C

@Thickness 0.750 mm
 1380 °F

@Thickness 0.0295 in
 Ignition Temp; IEC 60695-2-12
750 °C

@Thickness 1.50 mm
 1380 °F

@Thickness 0.0591 in
 Ignition Temp; IEC 60695-2-12
800 °C

@Thickness 3.00 mm
 1470 °F

@Thickness 0.118 in
 Ignition Temp; IEC 60695-2-12
930 °C

@Thickness 0.400 mm
 1710 °F

@Thickness 0.0157 in
 Ignition Temp; IEC 60695-2-12
960 °C

@Thickness 0.400 mm
 1760 °F

@Thickness 0.0157 in
 Flammability Index; IEC 60695-2-12
960 °C

@Thickness 0.750 mm
 1760 °F

@Thickness 0.0295 in
 Flammability Index; IEC 60695-2-12
960 °C

@Thickness 1.50 mm
 1760 °F

@Thickness 0.0591 in
 Flammability Index; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Arc Resistance 60 - 119 sec

@Thickness 3.00 mm
 60 - 119 sec

@Thickness 0.118 in
 ASTM D496
Comparative Tracking Index 250 - 399 V

@Thickness 3.00 mm
 250 - 399 V

@Thickness 0.118 in
 IEC 60112
Hot Wire Ignition, HWI >= 120 sec

@Thickness 0.750 mm
 >= 120 sec

@Thickness 0.0295 in
 UL 746A
>= 120 sec

@Thickness 1.50 mm
 >= 120 sec

@Thickness 0.0591 in
 UL 746B
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
 >= 120 arcs

@Thickness 0.0295 in
 UL 746A
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 UL 746B
High Voltage Arc-Tracking Rate, HVTR 80.1 - 150 mm/min

@Thickness 3.00 mm
 3.15 - 5.91 in/min

@Thickness 0.118 in
 UL 746A
Processing Properties Metric English Comments
Rear Barrel Temperature 240 - 270 °C
464 - 518 °F
Middle Barrel Temperature 240 - 270 °C
464 - 518 °F
Front Barrel Temperature 240 - 270 °C
464 - 518 °F
Nozzle Temperature 240 - 270 °C
464 - 518 °F
Melt Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 65.0 - 95.0 °C
149 - 203 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Suggest Max Regrind 25%