SABIC Innovative Plastics Valox® SHF4340 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® SHF4340 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% GF Super High Flow PBT
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.15 % | 0.15 % | ISO 62 |
| Melt Index of Compound | 40 g/10 min @Load 2.16 kg, Temperature 250 °C |
40 g/10 min @Load 4.76 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 110 MPa | 16000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.70 GPa | 972 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.60 GPa | 812 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 38.0 kJ/m² | 18.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature -40.0 - 40.0 °C |
55.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 204 °C | 399 °F | Rate B/50; ISO 306 |
| 204 °C | 399 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Pyrotek M-3 High-Temperature Felt
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, Hardness 64A
- Kinetics MIM 4605 Low Alloy Steel (Quenched + Tempered)
- SABIC Innovative Plastics LNP Thermocomp DFZ22E PC
- SABIC Innovative Plastics NORYL PN235 PPE+PS
- Teknor Apex Monprene® MP-2880E Thermoplastic Elastomer
- A. Schulman POLYFORT™ FPP 1236-2939 Fiberglass Reinforced Homopolymer Polypropylene
- A. Schulman PP 1404-01 Polypropylene High Impact Polypropylene
- Constellium PLAN 5754 Aluminum Rolled Plate
- Austin Novel Materials Texalan® 770A PCL TPU
Copyright © lookpolymers.com All Rights Reserved