- Polymer Property : Melt Temperature = 250 °C
Polymer Property : Melt Temperature = 250 °C Product List
Processing PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Plastcom SLOVAMID 6 GF 10 GB 20 PA6, 10% glass fibre FeaturesPA 6 for injection moulding, chemically strengthened with 10% glass fibre. Application: impacted mouldings and mouldings with high strength applied in automotive, electrical, engineering and.. |
|||
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | |
| Plastcom SLOVAMID 6 GF 15 T 25 LTS PA6, 15% glass fibre, 25% mineral filling FeaturesGood anisotropy of the manufacturing shrinkage. The talc is added to get the material shrinkage identical in both directions. Application for flat products in disc form /no screw after cooli.. |
|||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Plastcom SLOVAMID® 6 GF 30 FRG 2 PA6 reinforced with glass fiber, flame retarded PA 6 for injection molding, reinforced with 30 % glass fiber, flame retarded with halogen free flame retardant. Main features: flammability in accordance with UL 94 5 at 3.2 mm. Application for the .. |
|||
| Melt Temperature | 250 °C | 482 °F | Optimum |
| DuPont Performance Polymers Crastin® CE2055 NC010 PBT
(Unverified Data**) Crastin® CE2055 NC010 is an unreinforced, low viscosity polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers |
|||
| Melt Temperature | 250 °C | 482 °F | Optimum |
| DuPont Performance Polymers Crastin® S600F10 BK851 PBT
(Unverified Data**) Crastin® S600F10 BK851 is an unreinforced, lubricated, medium high viscosity, black polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers |
|||
| Melt Temperature | 250 °C | 482 °F | |
| Shell Carilon® DP R1130 Polyketone, 30% Glass Fiber Reinforced
(discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON® Thermoplastic Polymer DP R1130 is a 30 percent glass fiber reinforced compound based on a developmental e.. |
|||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Injection Molding |
| Eastman Eastar GN102 Copolyester
(discontinued **) Eastar GN102 copolyester is a glycol modified polyethylene terephthalate (PET) that contains an ultraviolet inhibitor and mold release. Eastar GN102 copolyester will not crystallize and thus offers .. |
|||
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| LG Chemical LUMID GP2130AE PA6+GF13%, General Purpose Feature: Injection Molding, PA6+GF13%, General PurposeApplication: Industrial MaterialCAS No. 25038-54-4 and 65997-17-3Information provided by LG Chemical |
|||
| Melt Temperature | 250 °C | 482 °F | Injection Molding |
| Ineos ABS Lustran® 752 Key Features:UnfilledHigh impact or high impact modifiedSuitable processing methods:Sheet extrusionThermoforming |
|||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection Molding |
| LG Chemical LUPOY HR5007A PC/ABS, Heat Resistance, High Impact Description: Injection Molding, PC/ABS, Heat Resistance, High Flow, High Impact.Application: Automotive (Interior), E&E (housing)CAS: 103598-77-2 and 9003-56-9Information provided by LG Chemical |
|||
| Melt Temperature | 250 °C | 482 °F | for test specimens; ISO 294 |
| Lanxess Pocan® DP C 1502 000000 PBT + PC PBT + PC, non-reinforced, injection molding, improved impact strength, low tendency to warp, UV-stabilizedInformation provided by LANXESS. |
|||
| Melt Temperature | 250 - 265 °C | 482 - 509 °F | |
| Lanxess Pocan® DP C 1502 000000 PBT + PC PBT + PC, non-reinforced, injection molding, improved impact strength, low tendency to warp, UV-stabilizedInformation provided by LANXESS. |
|||
| Melt Temperature | 250 °C | 482 °F | Injection Molding; ISO 294 |
| Lanxess Pocan® B 2505 000000 PBT PBT, non-reinforced, injection molding, flame retardant |
|||
| Melt Temperature | 250 - 265 °C | 482 - 509 °F | |
| Lanxess Pocan® C 1202 000000 PET + PC PBT + PC, non-reinforced, injection molding, improved impact strength, low tendency to warp, UV-stabilizedInformation provided by LANXESS. |
|||
| Melt Temperature | 250 - 290 °C | 482 - 554 °F | |
| LATI Laticonther 62 GR/50 PA 6, 50% Graphite Reinforced High thermal conductivity product based on Polyamide 6 (PA6). Graphite.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Te.. |
|||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Sax Polymers SAXAMID 136Q32 Nylon 6, Injection Molding Grade SAXAMID 136Q32 is a high impact-modified polyamide 6 injection-molding-grade.Information provided by SAX Polymers |
|||
| Melt Temperature | <= 250 °C | <= 482 °F | |
| Supreme Petrochem SP 555 Flame Retardant Polystyrene Characteristics Very good flow properties Good balance of toughness and rigidity Available in any dark colors Processing MoldingApplications Large size T.V. Cabinets VCR cabinets Electrical boxe.. |
|||
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| A. Schulman VOLOY™ 461 Glass Reinforced, Flame Retardant PBT Alloy Information provided by A. Schulman. |
|||
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| A. Schulman SCHULADUR® A GF30 30% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| CP-Polymer-Technik Wellamid® 6000 GS 30 HWUVCP 30% Glass Sphere Filled Nylon 6, UV Stabilized, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | |
| CP-Polymer-Technik Wellamid® 6000 GVZ 30 HWCP 30% Glass Fiber Z-Qualities Nylon 6, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | |
| CP-Polymer-Technik Wellamid® 6000 GVZ 30 HWCP 30% Glass Fiber Z-Qualities Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Injection-molding/Extrusion |
| BASF Ultramid® C3UG4 20% Glass Filled PA6/66 (Dry) Description: Halogen-free and phosphorus-free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire .. |
|||
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | Injection-molding |
| BASF Ultradur® B 4330 G6 HR 30% Glass Filled PBT Description: Is a PBT-I, injection-molding grade with 30% glass fibers, for rigid, tough and dimensionally stable technical parts with increased requirements on hydrolysis resistance and toughness, .. |
|||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection-molding |
| BASF Ultradur® S 4090 G6 High Speed 30% Glass Filled PBT Description: Is a PBT + ASA, easy-flowing injection-molding grades with 30% glass fibers; for rigid, tough and dimensionally stable technical parts.Applications: Housings, consoles, contact carriers.. |
|||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| BASF Ultradur B 6550 L PBT Ultradur B 6550 L is a high viscosity PBT extrusion grade.Applications; Used for loose buffer tubes for optical fibers, semi-finished products fro machining, profiles and pipes. |
|||