- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 250 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 250 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Nilit FRIANYL A63 GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Nilit FRIANYL A63 W-GV25 Nylon 6.6, std. viscosity for injection molding, 25% glass fiber reinforced Nylon 6.6, std. viscosity for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C @Thickness 3.20 mm |
482 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics EXTEM XH1015 TPI Resin (Asia Pacific) Thermoplastic Polyimide Extem* XH1015 Resin. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | 120°C/h; ISO 75/1 |
| Polykemi AB SCANAMID 66 A13^ F15 Nylon 66, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | Unannealed; ISO 75-2/B |
| PolyOne Bergamid™ A70 G30 U Polyamide 66 (Nylon 66) Information provided by PolyOne |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | Unannealed; ISO 75-2/B |
| PolyOne Bergamid™ A70 G50 HW SO Polyamide 66 (Nylon 66) Information provided by PolyOne |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DIN 53461 |
| Polyram PE322G22 PET, 22% Glass Fiber
(discontinued **) 22% Glass fiber reinforced, flame retardant PET for injection molding applications.Information provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75, ASTM D648 |
| Nilit Nilamid A G5 FR C4 25% Glass Fiber Reinforced, Flame Retardant PA66 (with Halogens) Description: Nilamid A G5 FR C4 combines excellent mechanical performance with flame retardancy. The halogenated flame retardant system used in this product allows a wide range of colors. This produ.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Nilit FRIANYL A63 HS-GV35 Nylon 6.6 for injection molding, 35% glass fiber reinforced Nylon 6.6 for injection molding, high impact resistance.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Nilit FRIANYL A63 HS-GV40 Nylon 6.6 for injection molding, 40% glass fiber reinforced Nylon 6.6 for injection molding, high impact resistance.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| DSM Akulon® S223-HPG8U (Dry) 43% Glass Reinforced, Impact Modified Nylon 66 (North America)
(discontinued **) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 - 271 °C | 482 - 520 °F | Average value: 261 °C Grade Count:6 |
| Overview of materials for Polyphenylene Sulfide (PPS) Alloy, Glass Reinforced, Flow Enhanced This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) Alloy, Glass Reinforced, Flow Enhanced". Each property range of values repor.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Lanxess Durethan® AKV 30 G H2.0 SR1 900051 Nylon 66, 30% Glass Fiber PA 66, injection molding grade, 30% glass fibers, better surface than AKV 30 H2.0, good heat-ageing resistance |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Lanxess Durethan® AKV 35 H3.0 000000 Nylon 66, 35% Glass Fiber PA 66, injection molding grade, 35% glass fibers, good heat-ageing resistance |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Lanxess Durethan® AKV 50 H2.0 901510 Nylon 66, 50% Glass Fiber PA 66, injection molding grade, 50% glass fibers, good heat-ageing resistance |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | |
| LATI Latamid 66 MDT05-01 PA 66 Polyamide 66 (PA66) based compound. Magnetic detectable filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplas.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Polyram PlusTek PA301G2 Nylon 6.6 for Injection Molding, 10% Glass Fiber Reinforced, Heat Stabilized Heat stabilized, 10% Glass fiber reinforced Nylon 6.6 for injection molding applications.Information provided by Polyram. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DIN 53461 |
| Polyram PlusTek PA301G6 Nylon 6.6, Heat Stabilized, 30% Glass Fiber Heat stabilized, 30% glass fiber reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DIN 53461 |
| Polyram PlusTek PA341G9 Nylon 6.6, 45% Glass Fiber 45% glass fiber reinforced, high stiffness and extreme cold environment, UV stabilized polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DIN 53461 |
| Polyram PlusTek PA840G3 Nylon 6.6, 15% Glass Fiber 15% glass fiber reinforced, impact modified polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 179 |
| CP-Polymer-Technik Wellamid® 6600 GV 30 HW 30% Glass Fiber Nylon 66, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 179 |
| CP-Polymer-Technik Wellamid® 6600 GV 40 HWCP 40% Glass Fiber Nylon 66, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ASTM D648 |
| Ashley Polymers Ashlene® 528L-30G Nylon 66, 30% Glass Reinforced General purpose glass fiber reinforced Nylon 66 designed for parts requiring excellent thermal and dimensional stability and higher strength than conventional resins.Data provided by the manufacture.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ASTM D648 |
| Cheng Yu Plastic FR200GV15 Flame Retardant Nylon 66, 15% Glass Fiber |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | |
| LATI Latiohm 66-04 PD01 G/25-V0CT1 PA66, 25% Glass Fiber Reinforced, Flame Retardant Semiconductive/dissipative product based on Polyamide 66 (PA66). Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific;.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 756 Carbon Fiber Reinforced, Flow Enhanced, PPS Alloy Data provided by the manufacturer, ComAlloy International Company.20% Carbon Fiber Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||