Victrex® PEEK 90GL30 BLACK EU 30% Glass Fiber Filled, PolyEtherEtherKetone

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer Victrex
Trade Name PEEK
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Victrex® PEEK 90GL30 BLACK EU 30% Glass Fiber Filled, PolyEtherEtherKetone.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High performance thermoplastic material, 30% glass fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding, very easy flow, FDA and EU food contact compliant, color black.Typical Application Areas: Complex geometries with thinner cross sections or longer flow lengths where higher strength in a static system is required. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.Information Provided by VICTREX®
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
Crystaline; ISO 1183
Water Absorption at Saturation 0.30 %

@Temperature 23.0 °C
 0.30 %

@Temperature 73.4 °F
 immersion; ISO 62-1
0.45 %

@Temperature 100 °C
 0.45 %

@Temperature 212 °F
 immersion; ISO 62-1
Viscosity 200000 cP

@Temperature 400 °C
 200000 cP

@Temperature 752 °F
 melt; ISO 11443
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
370°C nozzle, 180°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
370°C nozzle, 180°C tool; ISO 294-4
Spiral Flow 18.5 cm

@Thickness 1.00 mm
 7.28 in

@Thickness 0.0394 in
 370°C nozzle, 180°C tool
22.0 cm

@Thickness 1.00 mm
 8.66 in

@Thickness 0.0394 in
 400°C nozzle, 200°C tool
Mechanical Properties Metric English Comments
Hardness, Shore D 87
87
ISO 868
Tensile Strength at Break 40.0 MPa

@Temperature 275 °C
 5800 psi

@Temperature 527 °F
 ISO 527
60.0 MPa

@Temperature 225 °C
 8700 psi

@Temperature 437 °F
 ISO 527
70.0 MPa

@Temperature 175 °C
 10200 psi

@Temperature 347 °F
 ISO 527
120 MPa

@Temperature 125 °C
 17400 psi

@Temperature 257 °F
 ISO 527
180 MPa

@Temperature 23.0 °C
 26100 psi

@Temperature 73.4 °F
 ISO 527
Elongation at Break 2.2 %
2.2 %
ISO 527
Tensile Modulus 12.0 GPa
1740 ksi
ISO 527
Flexural Strength 75.0 MPa

@Temperature 275 °C
 10900 psi

@Temperature 527 °F
 ISO 178
115 MPa

@Temperature 175 °C
 16700 psi

@Temperature 347 °F
 ISO 178
230 MPa

@Temperature 125 °C
 33400 psi

@Temperature 257 °F
 ISO 178
275 MPa

@Temperature 23.0 °C
 39900 psi

@Temperature 73.4 °F
 ISO 178
Flexural Modulus 11.5 GPa
1670 ksi
ISO 178
Compressive Strength 55.0 MPa

@Temperature 200 °C
 7980 psi

@Temperature 392 °F
 ISO 604
160 MPa

@Temperature 120 °C
 23200 psi

@Temperature 248 °F
 ISO 604
250 MPa

@Temperature 23.0 °C
 36300 psi

@Temperature 73.4 °F
 ISO 604
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
ISO 180/A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²
19.0 ft-lb/in²
ISO 180/U
Thermal Properties Metric English Comments
CTE, linear 45.0 µm/m-°C

@Temperature <=143 °C
 25.0 µin/in-°F

@Temperature <=289 °F
 Average below Tg; ASTM D696
110 µm/m-°C

@Temperature >=143 °C
 61.1 µin/in-°F

@Temperature >=289 °F
 Average above Tg; ASTM D696
CTE, linear, Parallel to Flow 20.0 µm/m-°C

@Temperature <=143 °C
 11.1 µin/in-°F

@Temperature <=289 °F
 Below Tg; ASTM D696
20.0 µm/m-°C

@Temperature >=143 °C
 11.1 µin/in-°F

@Temperature >=289 °F
 Above Tg; ASTM D696
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
Average; ISO 22007-4
0.350 W/m-K
2.43 BTU-in/hr-ft²-°F
Along flow; ISO 22007-4
Melting Point 343 °C
649 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 335 °C
635 °F
ISO 75A-f
Glass Transition Temp, Tg 143 °C
289 °F
ISO 11357
Glow Wire Test 960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 Fire Smoke Toxicity; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Dielectric Strength 21.5 kV/mm

@Thickness 2.00 mm
 546 kV/in

@Thickness 0.0787 in
 IEC 60243-1
Comparative Tracking Index 150 V
150 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature <= 100 °C
<= 212 °F
Hopper Temperature
Nozzle Temperature 370 °C
698 °F
Mold Temperature 170 - 200 °C
338 - 392 °F
Dry Time 3.00 hour

@Temperature 150 °C
 3.00 hour

@Temperature 302 °F
5.00 hour

@Temperature 120 °C
 5.00 hour

@Temperature 248 °F