- Polymer Property : Tensile Strength at Break = 60.0 MPa
Polymer Property : Tensile Strength at Break = 60.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa @Temperature 275 °C |
8700 psi @Temperature 527 °F |
ISO 527 |
| Victrex® PEEK 150CA30 30% Carbon Fiber Reinforced Product Description: High performance thermoplastic material, 30% carbon fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding, easy flow, FDA food contact c.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 175 °C |
8700 psi @Temperature 347 °F |
ISO 527 |
| Victrex® PEEK 450GL30 30% Glass Fiber Reinforced Product Description: High performance thermoplastic material, 30% glass fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and extrusion, standard flow, F.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 175 °C |
8700 psi @Temperature 347 °F |
Result based on 450GL30; ISO 527 |
| Victrex® PEEK 450GL30 Polyetheretherketone, 30% Glass Fiber, Black Product Description: High performance thermoplastic material, 30% glass fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, Standard viscos.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 225 °C |
8700 psi @Temperature 437 °F |
ISO 527 |
| Victrex® PEEK 90GL30 BLACK EU 30% Glass Fiber Filled, PolyEtherEtherKetone High performance thermoplastic material, 30% glass fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding, very easy flow, FDA and EU food contact compliant, .. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 90.0 °C |
8700 psi @Temperature 194 °F |
|
| LATI Larpeek 50 PEEK Polyetheretherketone (PEEK). Unfilled. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe;.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 90.0 °C |
8700 psi @Temperature 194 °F |
|
| LATI Lastil G/25-V0 SAN, 25% Glass Fiber Reinforced, Flame Retardant Styrene-Acrylonitrile copolymer (SAN) based compound. Glass fibers. UL94 V-0 classified, with brominated flame retardants. Very high dimensional stability.Availability: Africa & Middle East; Asia Pa.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 23.0 °C |
8700 psi @Temperature 73.4 °F |
|
| LATI Lastilac RT K/10 ABS, 10% Carbon Fiber Reinforced Acrylonitrile-Butadiene-Styrene copolymer (ABS) based compound. Carbon fiber. High dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInforma.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 60.0 °C |
8700 psi @Temperature 140 °F |
|
| LATI Lastilac SP G/17 ABS, Glass Fiber Reinforced Acrylonitrile-Butadiene-Styrene copolymer (ABS) based compound. Glass fibers. High dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInforma.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 90.0 °C |
8700 psi @Temperature 194 °F |
|
| LATI Kelon® B FR H CETG/250-V0 PA 6, Glass/Mineral Reinforced, Flame Retardant, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers / Mineral filler. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free.Availability: Africa & Middle East; Asia Pacifi.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 60.0 °C |
8700 psi @Temperature 140 °F |
|
| LATI Kelon® B H CETG/300 PA 6, Glass/Mineral Reinforced, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers / Mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati I.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 60.0 °C |
8700 psi @Temperature 140 °F |
|
| LATI Laril 13 G/20 PPOm, 20% Glass Fiber Reinforced Modified Polyphenylene Oxide (PPOm) based compound. Glass fibers. Low thermal expansion coefficient. Good thermal properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; .. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 23.0 °C |
8700 psi @Temperature 73.4 °F |
|
| LATI Lastilac 11 G/10 ABS/PC, 10% Glass Fiber Reinforced ABS/PC Blend (ABS/PC) based compound. Glass fibers. Good surface appearance. Good impact resistance. Good thermal properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; .. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 90.0 °C |
8700 psi @Temperature 194 °F |
|
| LATI Latamid 12 H2 G/30 PA 12, 30% Glass Fiber Reinforced, Heat Stabilized Polyamide 12 (PA12) based compound. Heat stabilized. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termop.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 60.0 °C |
8700 psi @Temperature 140 °F |
|
| LATI Latamid 6 H2 G/20-V2HF PA 6, 20% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. UL94 V-2 classified, halogens-based flame retardants and red phosphorous free. Availability: Africa & Middle East; Asia Pacific; Euro.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 90.0 °C |
8700 psi @Temperature 194 °F |
|
| LATI Latamid 66 B G/20-V PA 66, 20% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 66 (PA66) based compound. High fluidity. Glass fibers. Flame retardant, non classifiable, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific;.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 120 °C |
8700 psi @Temperature 248 °F |
|
| LATI Latamid 66 H2 G/25-V0CT1 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific; Europe; Lat.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 150 °C |
8700 psi @Temperature 302 °F |
|
| LATI Latamid 66 H2 G/25-V0KB PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with red phosphorous. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaIn.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 150 °C |
8700 psi @Temperature 302 °F |
|
| LATI Latamid SP2 H2 G/35 PA 6.12, 35% Glass Fiber Reinforced, Heat Stabilized Polyamide 6.12 (PA6.12) based compound. Heat stabilized. Glass fibers. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provi.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 90.0 °C |
8700 psi @Temperature 194 °F |
|
| LATI Later 4 G/20 PBT, 20% Glass Fiber Reinforced Polybutylene Terephthalate (PBT) based compound. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplast.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 120 °C |
8700 psi @Temperature 248 °F |
|
| LATI Later 4 K/30 PBT, 30% Carbon Fiber Reinforced Polybutylene Terephthalate (PBT) based compound. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplasti.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 150 °C |
8700 psi @Temperature 302 °F |
|
| LATI Laticonther 80 GCE/650 PPS, Glass/Mineral Reinforced High thermal conductivity product based on Polyphenylene Sulfide (PPS). Glass fibers / Mineral filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformatio.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 90.0 °C |
8700 psi @Temperature 194 °F |
|
| LATI Latilon 28D G/20 PC, 20% Glass Fiber Reinforced Polycarbonate (PC) based compound. Glass fibers. Low smoke density and low toxicity index. High dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North A.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 120 °C |
8700 psi @Temperature 248 °F |
|
| LATI Latilon 28D G/20-V0 PC, 20% Glass Fiber Reinforced, Flame Retardant Polycarbonate (PC) based compound. Glass fibers. UL94 V-0 classified, brominated and chlorinated halogens-based flame retardants free. Low smoke density and low toxicity index. High dimensional stab.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 230 °C |
8700 psi @Temperature 446 °F |
3; ISO 527-2 |
| Solvay Specialty Polymers Amodel® A-4133 HH Polyphthalamide (PPA), 33% Glass Fiber (Dry) Amodel® A-4133 HH is a 33% glass fiber reinforced heat stabilized grade of polyphthalamide (PPA) that has been designed to provide outstanding property retention to thermal oxidative degradation .. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 230 °C |
8700 psi @Temperature 446 °F |
3; ISO 527-2 |
| Solvay Specialty Polymers Amodel® A-4145 HH Polyphthalamide (PPA), 45% Glass Fiber (Dry) Amodel® A-4145 HH is a 45% glass fiber reinforced heat stabilized grade of polyphthalamide (PPA) that has been designed to provide outstanding property retention to thermal oxidative degradation .. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 23.0 °C |
8700 psi @Temperature 73.4 °F |
ASTM D638 |
| DuPont Performance Polymers Crastin® T835FRUV NC010 PBT Crastin® T835FRUV NC010 is a 5% glass fiber reinforced, toughened, flame retardant polybutylene terephthalate resin for injection molding. (precommercial code = Crastin® CE2402)Information provide.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 150 °C |
8700 psi @Temperature 302 °F |
50%RH; ISO 527 |
| DuPont Performance Polymers Zytel® 84G33 BKB031 Nylon 66
(Unverified Data**) Zytel® 84G33 BKB031 is a 33% glass reinforced toughened polyamide 66 and polyamide 6 co-melt black cube blended resin. This resin was developed for applications requiring strength, stiffness and im.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 60.0 °C |
8700 psi @Temperature 140 °F |
|
| LATI Lastil G/30 SAN, 30% Glass Fiber Reinforced Styrene-Acrylonitrile copolymer (SAN) based compound. Glass fibers. High dimensional stability. High stiffness.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaI.. |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 23.0 °C |
8700 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| DuPont Performance Polymers Zytel® BM70G15HSLR BK537 Nylon 66 Zytel® BM70G15HSLR BK537 is a 15% glass fiber reinforced polyamide 66 for blow molding.Information provided by DuPont Performance Polymers |
|||
| Tensile Strength at Break | 60.0 MPa @Temperature 225 °C |
8700 psi @Temperature 437 °F |
ISO 527 |
| Victrex® PEEK 150GL30 Black Polyetheretherketone, 30% Glass Fiber Reinforced Product Description:High performance thermoplastic material, 30% glass fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA food contact co.. |
|||