- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- Styrolution Terluran® HH-112 ABS
Styrolution Terluran® HH-112 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Styrolution |
| Trade Name | Terluran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Terluran® HH-112 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Terluran HH-112 is an injection molding grade of ABS with very high heat resistance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | ASTM Data; MD |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM Test |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | 50mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | 2 in/min; ASTM Test | |
| Elongation at Break | 8.0 % | 8.0 % | 50mm/min, Nominal strain; ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | 2 in/min; ASTM Test |
| 3.1 % | 3.1 % | 50mm/min; ISO 527 | |
| Tensile Modulus | 2.70 GPa | 392 ksi | 1mm/min; ISO 527 |
| 2.80 GPa | 406 ksi | ASTM Test | |
| Flexural Strength | 81.0 MPa | 11700 psi | ISO Data |
| 88.0 MPa | 12800 psi | ASTM Test | |
| Flexural Modulus | 2.70 GPa | 392 ksi | ASTM Test |
| Izod Impact, Notched | 0.550 J/cm @Temperature -30.0 °C |
1.03 ft-lb/in @Temperature -22.0 °F |
ASTM Test |
| 1.00 J/cm @Thickness 3.17 mm |
1.87 ft-lb/in @Thickness 0.125 in |
ASTM Test | |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | 14.0 J/cm² | 66.6 ft-lb/in² | ISO 179 |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179 |
| 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 109 °C | 228 °F | ISO 75 |
| Vicat Softening Point | 112 °C | 234 °F | Rate "A" Loading 2 (50 degC/h 50N); ASTM Test |
| 112 °C | 234 °F | (50 °C/h / 50N) - B/50; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Dielectric Strength | 41.0 kV/mm | 1040 kV/in | IEC 60243-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 °C | 482 °F | Injection molding |
| Mold Temperature | 105 °C | 221 °F | Ejection temperature |
| Injection Velocity | 60.0 mm/sec | 2.36 in/sec | Injection molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | North America and Europe | |
| Form | Pellets | |
| Impact Modified | Yes | |
| NSF Std. 51 | No | |
| NSF Std. 61 | No | |
| Primary Processing Technique | Injection Molding | |
| Processing | Injection Molding | |
| Special characteristic | Platable | |
| UL.UL-C | Yes | |
| USP Class VI | No |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics GELOY CR8510 ASA
- NOVA Chemicals Sclair® 14K3 Octene LMDPE Film Resin (discontinued **)
- Gromax CFG33-RN13N1 Nylon 6 33% Glass Filled (Dry)
- Solvay Specialty Polymers Amodel® A-1133 L WH 015 Polyphthalamide (PPA), 33% Glass Fiber
- Solvay AG-RHOâ„¢ GPA Surfactant
- A. Schulman POLYBATCH™ Orange 1046E Concentrate Based In Polyethylene
- Formosa Plastics Formolene® 4142R Injection Molding Polypropylene
- Arlon 51250R016 0.016" (0.406 mm) Uncured Silicone Rubber with Fiberglass Substrate
- ExxonMobil Escorene® HD-8761 LHDPE Rotational Molding Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved