Polymer Property : Flexural Strength = 81.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	81.0 MPa	11700 psi	ASTM D790
Plaskolite Optix® CA-41 General Purpose Acrylic Resin Injection Molding Grade Pellets only. Lowest Heat Resistance and maximum flow.
Flexural Strength	81.0 - 85.0 MPa	11700 - 12300 psi	ASTM D790
Prodways PLASTCure Cast 100 3D Printing Polymer High reactivity and low viscosity. Excellent dimensional stability.Fulfills the high demands place on digital process chain.Information provided by Genistar.
Flexural Strength	81.0 MPa	11700 psi	ISO 178
SABIC Innovative Plastics LNP COLORCOMP D1000P PC (Asia Pacific) LNP* Colorcomp* D1000P is a compound based on Polycarbonate resin containing Unfilled Custom Color. Added features of this material include: Exceptional Processing.
Flexural Strength	81.0 MPa	11700 psi	ISO 178
SABIC Innovative Plastics LNP FARADEX PS003E PA 6 LNP* FARADEX* PS003E is a compound based on Nylon 6 resin containing 15% Stainless Steel. Added features of this material include: EMI/RFI Shielding.
Flexural Strength	81.0 MPa	11700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DX07404H PC LNP* LUBRICOMP* DX07404H is a compound based on Polycarbonate containing Proprietary Fillers. Added features of this grade are: Healthcare, Wear Resistant.
Flexural Strength	81.0 MPa	11700 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DX94375H PC LNP* LUBRICOMP* DX94375H is a compound based on Polycarbonate resin containing Proprietary Fillers. Added features of this material include: Healthcare, Wear Resistant.
Flexural Strength	81.0 MPa	11700 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP WI001 PBT LNP* LUBRICOMP* WI001 is a compound based on PBT containing 2% Silicone. Added feature of this grade is: Wear Resistant.
Flexural Strength	81.0 MPa	11700 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DX09402 PC LNP* THERMOCOMP* DX09402 is a compound based on Polycarbonate containing Proprietary Filler(s).
Flexural Strength	81.0 MPa	11700 psi	ISO 178
Styrolution NovodurÂ® HH-112 ABS Novodur HH-112 is a high heat injection molding grade. It provides good heat resistance combined with enhanced stiffness.Information provided by Styrolution
Flexural Strength	81.0 MPa	11700 psi	ISO 178
Styrolution TerluranÂ® HH-112 Q109 ABS Description: Injection-molding grade with highest heat resistance, high rigidity and medium impact strength.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
Flexural Strength	81.0 MPa	11700 psi	ISO 178
Styrolution TerluranÂ® HH-112 Q42 Gray 10072 ABS Description: Injection-molding grade with highest heat resistance, high rigidity and medium impact strength.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
Flexural Strength	81.0 MPa	11700 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp PH0600A PA 6 LNP THERMOCOMP* PH0600A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength	81.0 MPa	11700 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP WH0270B PBT LNP THERMOCOMP* WH0270B is a compound based on Polybutylene Terephalate resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Flexural Strength	81.0 MPa	11700 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP WH0270B PBT (Asia Pacific) LNP THERMOCOMP* WH0270B is a compound based on Polybutylene Terephalate resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Flexural Strength	81.0 MPa	11700 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP D7002IXH PC LNP* THERMOCOMP* D7002IXH is a compound based on Polycarbonate siloxane copolymer resin containing proprietary antimicrobial additives. Designed for touch surfaces, housings, etc., in healthcare an..
Flexural Strength	81.0 MPa	11700 psi	ASTM D790
Plenco 2000 Phenolic, Granular, Injection Molded PLENCO 02000 is a versatile general purpose, organic filled phenolic molding compound, offering optimum cure characteristics and an excellent balance of molding properties. UL recognized under compo..
Flexural Strength	81.0 MPa	11700 psi	ASTM D790
Plenco 2535 Phenolic, Granular, Injection Molded PLENCO 02535 is a general purpose, organic filled phenolic molding compound offering optimized cure characteristics and excellent electrical properties. Type ASTM 5948 CFG, and UL recognized under c..
Flexural Strength	81.0 MPa	11700 psi	DIN EN ISO 178
Wolf Kunststoff ZEDEX® ZX-530 A5D Polymer Alloy Main Characteristics: Low Creep; Low moisture absorption; Flame retardant; Low impurity ions; Good machinability; FDA compliant LABS; Extremely low outgassing; Less expensive than PEEK; Stress resis..
Flexural Strength	81.0 MPa	11700 psi	ASTM D790
Plenco 7476 Phenolic, Granular, Transfer Molded PLENCO 07476 is a cotton flock filled resole phenolic molding compound, with improved physical strength, crack resistance, and is resistant to soap and detergent solutions at elevated temperatures. ..
Flexural Strength	81.0 MPa	11700 psi	ASTM D790
Unitika FUN-8000 Characteristics: High impact strength High chemical resistance Transparency as high as polycarbonateInformation provided by Unitika Ltd.
Flexural Strength	81.0 MPa	11700 psi	ASTM D790
Eastman Eastar EN067 Copolyester, Natural Eastar Copolyester EN067 is a copolymer PET with good color. This product is supplied as a crystalline pellet that has improved flowability characteristics. Due to slower crystallization kinetics, t..
Flexural Strength	81.0 MPa @Temperature 23.0 °C	11700 psi @Temperature 73.4 °F	EN ISO 178
Ensinger TECASINT 3012 Polyimide, Ochre Brown (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel..
Flexural Strength	81.0 MPa @Temperature 23.0 °C	11700 psi @Temperature 73.4 °F	EN ISO 178
Ensinger TECASINT 3022 Polyimide, Black, 15% Graphite (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel..
Flexural Strength	81.0 MPa	11700 psi	ISO 178
Ascend Performance Materials Vydyne® 49 Nylon 66, Impact Modified, DAM Vydyne® 49 is general-purpose, impact-modified PA66 resin. Available in natural, is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact s..
Flexural Strength	81.0 MPa	11700 psi	ASTM D790
Plaskolite West Optix® CA-41 General Purpose Acrylic Resin Injection Molding Grade Pellets only. Lowest Heat Resistance and maximum flow.
Flexural Strength	81.0 MPa	11700 psi
Poco Graphite Glassmate® HT Graphite This high strength material has an oxidation inhibitor that raises the oxidation threshold. Service temperature can be raised to 600°C; graphites are subject to oxidation above 450°C
Flexural Strength	81.0 MPa	11700 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DL002 PC LNP LUBRICOMP* DL002 is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength	81.0 MPa	11700 psi	ASTM D790
Plenco 2000 Phenolic, Granular, Transfer Molded PLENCO 02000 is a versatile general purpose, organic filled phenolic molding compound, offering optimum cure characteristics and an excellent balance of molding properties. UL recognized under compo..
Flexural Strength	81.0 MPa	11700 psi	ISO 178
Polyplastics Duracon® M25-44/M25S Acetal Co-polymer (POM), Standard, High viscosity DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..
Flexural Strength	81.0 MPa	11700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP PH0800A PA 6 LNP* THERMOCOMP* PH0800A is a compound based on Nylon 6 resin. Added feature of this material is: High Specific Gravity.