NOVA Chemicals Sclair® 14K3 Octene LMDPE Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Linear Medium Density Polyethylene (LMDPE), Film
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Sclair® 14K3 Octene LMDPE Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Film Properties. Features: Low gel, excellent optics, good moisture barrier.Applications: Cast overwrap film.Data provided by the manufacturer.
Physical Properties Metric English Comments
Density 0.936 g/cc
0.0338 lb/in³
ASTM D792
Melt Flow 4.8 g/10 min

@Load 2.16 kg,
Temperature 190 °C
4.8 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 58
58
ASTM D2240
Film Tensile Strength at Yield, MD 16.0 MPa
2320 psi
ASTM D882
Film Tensile Strength at Yield, TD 15.0 MPa
2180 psi
ASTM D882
Film Elongation at Break, MD 850 %
850 %
ASTM D882
Film Elongation at Break, TD 1100 %
1100 %
ASTM D882
Secant Modulus, MD 0.280 GPa
40.6 ksi
ASTM D882
Secant Modulus, TD 0.310 GPa
45.0 ksi
ASTM D882
Elmendorf Tear Strength, MD 2.00 g/micron
50.8 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 12.0 g/micron
305 g/mil
ASTM D1922
Dart Drop 1.00 g/micron
25.4 g/mil
F 50; ASTM D1709/A
Film Tensile Strength at Break, MD 42.0 MPa
6090 psi
ASTM D882
Film Tensile Strength at Break, TD 30.0 MPa
4350 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 119 °C
246 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 3.0 %

@Thickness 0.0250 mm
3.0 %

@Thickness 0.000984 in
ASTM D1003
Gloss 85 %
85 %
45°; 1 mil; ASTM D1894
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F