SABIC Innovative Plastics NORYL FP6130 PPE+PS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL FP6130 PPE+PS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl* FP6130 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating at 1.5 mm with a specific density of 1.1 g/cm^3. Noryl FP6130 may be an excellent material candidate for Flat Panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance, low density and thin wall flame resistance.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D792
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Moisture Absorption 0.0200 %
0.0200 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.13 %
0.13 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Index of Compound 15 g/10 min

@Load 1.20 kg,
Temperature 280 °C
15 g/10 min

@Load 2.65 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
34 g/10 min

@Load 2.16 kg,
Temperature 280 °C
34 g/10 min

@Load 4.76 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 49.0 MPa
7110 psi
Type I, 50 mm/min; ASTM D638
53.0 MPa
7690 psi
50 mm/min; ISO 527
Tensile Strength, Yield 52.0 MPa
7540 psi
Type I, 50 mm/min; ASTM D638
61.0 MPa
8850 psi
50 mm/min; ISO 527
Elongation at Break 7.3 %
7.3 %
Type I, 50 mm/min; ASTM D638
8.0 %
8.0 %
50 mm/min; ISO 527
Elongation at Yield 3.5 %
3.5 %
50 mm/min; ISO 527
3.6 %
3.6 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.51 GPa
364 ksi
1 mm/min; ISO 527
3.14 GPa
455 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 89.0 MPa
12900 psi
2 mm/min; ISO 178
98.0 MPa
14200 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.42 GPa
351 ksi
2 mm/min; ISO 178
2.77 GPa
402 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.380 J/cm
0.712 ft-lb/in
ASTM D256
0.270 J/cm

@Temperature -30.0 °C
0.506 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 74.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
74.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 74.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
74.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 92.0 °C
198 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
90.0 °C

@Thickness 3.20 mm
194 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 110 °C
230 °F
Rate B/50; ASTM D1525
111 °C
232 °F
Rate B/50; ISO 306
114 °C
237 °F
Rate B/120; ISO 306
UL RTI, Electrical 65.0 °C
149 °F
UL 746B
UL RTI, Mechanical with Impact 65.0 °C
149 °F
UL 746B
UL RTI, Mechanical without Impact 65.0 °C
149 °F
UL 746B
Flammability, UL94 V-1

@Thickness 1.50 mm
V-1

@Thickness 0.0591 in
UL 94
Oxygen Index 30 %
30 %
ISO 4589
Glow Wire Test 725 °C
1340 °F
IEC 60695-2-13
725 °C
1340 °F
IEC 60695-2-13
725 °C
1340 °F
IEC 60695-2-13
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 4.00e+16 - 4.50e+16 ohm-cm
4.00e+16 - 4.50e+16 ohm-cm
ASTM D257
4.00e+16 - 4.50e+16 ohm-cm
4.00e+16 - 4.50e+16 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 - 1.50e+14 ohm
1.00e+14 - 1.50e+14 ohm
ASTM D257
1.00e+14 - 1.50e+14 ohm
1.00e+14 - 1.50e+14 ohm
ROA; IEC 60093
Dielectric Constant 2.7

@Frequency 1.00e+6 Hz
2.7

@Frequency 1.00e+6 Hz
ASTM D150
2.7

@Frequency 1.00e+6 Hz
2.7

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 28.6 kV/mm

@Thickness 1.60 mm
726 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
Dissipation Factor 0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
ASTM D150
0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 175 - 250 V
175 - 250 V
UL 746A
250 V
250 V
IEC 60112
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
Descriptive Properties Value Comments
Instrumented Impact Total Energy, 23°C naJ
ASTM D3763