- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 92.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 92.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycoloy® CP8320 PC+ABS Cycoloy Medium Heat Plating Grade for Automotive |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Ravago Manufacturing Americas Hybrid S493 ABS + Polycarbonate Alloy Medium Impact, Enhanced Heat PerformanceEntecs proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin fa.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 - 129 °C | 198 - 265 °F | Average value: 109 °C Grade Count:21 |
| Overview of materials for Polycarbonate/ABS Alloy, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/ABS Alloy, Carbon Fiber Filled". Each property range of values reported is minimum and max.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP 9X06483 PA 46 LNP* Lubricomp* 9X06483 is a compound based on a Nylon 4/6 containing PTFE. Added feature of this grade is: Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Kolon KOCETAL® EL302 Toughened Grade Acetal Resin Flexible grade. Applications: Flexible products. Information provided by API-Kolon. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ASTM D648 |
| LG Chemical LUPOY GP-5000FQ General Purpose PC/ABS Alloy, Unreinforced, Excellent Flow Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 92.0 °C @Thickness 6.40 mm |
>= 198 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical 90HR SAN, High Transparency, Heat Resistance, Chemical Resistance Feature: Injection Molding, SAN, High Transparency, Heat Resistance, Chemical ResistanceApplication: Battery Case, Light CoverCAS No. 9003-54-7Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP KL002L Acetal LNP* LUBRICOMP* KL002L is a compound based on Acetal Copolymer resin containing 10% PTFE. Added features of this grade include: Wear Resistant, Low Extractible. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KP002 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Stat-kon NX03602 PC+ABS (Asia Pacific) LNP* STAT-KON* NX03602 is a compound based on PC+ABS Blend resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supplied by.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Xenoy® 1731J PBT+PC (Europe-Africa-Middle East) PBT+PC, Impact/chemical resistant. UV-Stabilized. Excellent physical property retention in automotive exteriors and OVAD.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP CX05470 PS LNP* THERMOCOMP* CX05470 is a compound based on Polystyrene resin containing 20% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ISO 75 |
| Teijin Multilon DN-3520F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It has improved stiffness through the addition of 20 % filler. Improved stiffness and high flowability realizes a thin w.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 6.40 mm |
198 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® NH-1014S PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL WCV072 PPE+PP Flexible, halogen free mPPE extrusion grade material for applications such as automotive wire insulation. Low specific gravity with good flame retardant and very good scrape abrasion resistance. De.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP AF002XXC ABS LNP THERMOCOMP* AF002XXC is a compound based on ABS resin containing 10% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL EXNL0353 PPE+HIPS EXNL0353 resin is a modified PPE + PS blend with an excellent balance of non-halogenated flame retardance, hydrolytic stability, impact and heat resistance, good flow, and low specific gravity for l.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Sax Polymers SAXLAC 310U Acrylonitrile Butadiene Styrene Saxalac 310U is an antistatic, high impact resistant and light stabilized ABS injection molding grade, characterized by good processability and high stiffness.Mechanical property data tested at 50% .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ISO 75/Af |
| Solvay TECHNYL® 2710IR PA66, DRY Description: TECHNYL® 2710 IR is an unfilled polyamide 6.6, impact modified, for injection molding. The product is available in natural color, and in colors on request.Benefits: This product, use.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Eastman Tritan MX811 Copolyester Applications:Blood TherapyDialyzer HousingsIV ComponentsKey Attributes:Ease of processingExcellent clarityExcellent hydrolytic stabilityFast drying timesGood chemical resistanceGood heat resistanceO.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Eastman Tritan TX2000 Copolyester Eastman Tritan TX2000 is an amorphous copolyester with excellent appearance and clarity. Its most outstanding features are excellent toughness, hydrolytic stability, and heat and chemical resistanc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 127UV BK701 Acetal (POM)
(Unverified Data**) UV Stabilized High Viscosity Acetal Homopolymer Delrin 127UV BK701 is a high viscosity UV stabilized acetal homopolymer. It has excellent impact strength UV resistance and thermal stability. It is w.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 527UV BK701 Acetal (POM)
(Unverified Data**) UV Stabilized Medium Viscosity Acetal HomopolymerDelrin 527UV BK701 is a medium viscosity black acetal homopolymer resin with UV stabilizers developed for automotive interior applications. It has im.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ISO 75-1/-2 |
| Barlog Plastics KEBALLOY EP 23 ABS/PC, unreinforced, electro platable grade ABS+PCInformation provided by BARLOG plastics GmbH. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron IM-11BM ABS Injection Molding Grade High Impact Strength, Medium Flow, High Fatigue ResistanceInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron SE-32 ABS Sheet Extrusion Grade Super high and Very High Impact Sheeting grades for Automobile & Luggage ApplicationsInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 6.40 mm |
198 °F @Thickness 0.252 in |
Method A; ASTM D648 |
| Bhansali Engineering Abstron SE32 FR IS15061 Flame Retardant ABS Flame Retardant- IS 15061 conformedInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 6.35 mm |
198 °F @Thickness 0.250 in |
ASTM D-648 |
| Chevron Phillips EA3025 Crystal Polystyrene
(discontinued **) High heat crystal polystyrene.Applications:Foam egg cartonsFoam meat traysInsulation boardBi-axially oriented sheetFeatures:Ultra-high molecular weight homopolymerHigh Vicat softening temperatureNar.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron SE-45 ABS Sheet Extrusion Grade Super high and Very High Impact Sheeting grades for Automobile & Luggage ApplicationsInformation provided by Bhansali |
|||