Polymer Resources TP-FR-IM Polybutylene Terephthalate, Impact Modified, Flame Retardant, Low Flow

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant , Polybutylene Terephthalate (PBT), Impact Grade
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources TP-FR-IM Polybutylene Terephthalate, Impact Modified, Flame Retardant, Low Flow.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polybutylene Terephthalate, Impact Modified, Flame Retardant, Low FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.34 g/cc
1.34 g/cc
ASTM D792
Linear Mold Shrinkage 0.010 - 0.014 cm/cm
0.010 - 0.014 in/in
ASTM D955
Melt Flow 3.0 - 9.0 g/10 min

@Load 2.16 kg,
Temperature 250 °C
3.0 - 9.0 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 44.8 MPa
6500 psi
ASTM D638
Tensile Strength, Yield 44.8 MPa
6500 psi
ASTM D638
Flexural Strength 77.57 MPa
11250 psi
ASTM D790
Flexural Modulus 2.00 GPa
290 ksi
ASTM D790
Izod Impact, Notched 5.34 J/cm

@Temperature 22.8 °C
10.0 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Gardner Impact 36.2 J
26.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 132 °C
270 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 87.8 °C
190 °F
ASTM D648
UL RTI, Electrical 130 °C

@Thickness 0.851 mm
266 °F

@Thickness 0.0335 in
UL 746
130 °C

@Thickness 1.60 mm
266 °F

@Thickness 0.0630 in
UL 746
130 °C

@Thickness 3.00 mm
266 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 130 °C

@Thickness 0.851 mm
266 °F

@Thickness 0.0335 in
UL 746
130 °C

@Thickness 1.60 mm
266 °F

@Thickness 0.0630 in
UL 746
130 °C

@Thickness 3.00 mm
266 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 85.0 °C

@Thickness 0.851 mm
185 °F

@Thickness 0.0335 in
UL 746
85.0 °C

@Thickness 1.60 mm
185 °F

@Thickness 0.0630 in
UL 746
110 °C

@Thickness 3.00 mm
230 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 V-0

@Thickness 0.850 mm
V-0

@Thickness 0.0335 in
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
ASTM D257
Dielectric Strength 27.2 kV/mm
690 kV/in
ASTM D149
Comparative Tracking Index >= 600 V
>= 600 V
UL 746
Hot Wire Ignition, HWI 7.0 - 15 sec

@Thickness 0.851 mm
7.0 - 15 sec

@Thickness 0.0335 in
UL 746
15 - 30 sec

@Thickness 1.60 mm
15 - 30 sec

@Thickness 0.0630 in
UL 746
30 - 60 sec

@Thickness 3.00 mm
30 - 60 sec

@Thickness 0.118 in
UL 746
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.851 mm
>= 120 arcs

@Thickness 0.0335 in
UL 746
>= 120 arcs

@Thickness 1.60 mm
>= 120 arcs

@Thickness 0.0630 in
UL 746
>= 120 arcs

@Thickness 3.00 mm
>= 120 arcs

@Thickness 0.118 in
UL 746
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 238 - 254 °C
460 - 490 °F
Middle Barrel Temperature 243 - 260 °C
470 - 500 °F
Front Barrel Temperature 249 - 266 °C
480 - 510 °F
Melt Temperature 232 - 260 °C
450 - 500 °F
Mold Temperature 43.3 - 82.2 °C
110 - 180 °F
Drying Temperature 116 - 121 °C
240 - 250 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments