Polymer Resources PC-FR2-TFE Polycarbonate, Flame Retardant, 5% PTFE

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, PTFE Filled , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PC-FR2-TFE Polycarbonate, Flame Retardant, 5% PTFE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polycarbonate, Improved Flame Retardant, 5% PTFE LubricantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc
1.26 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.010 cm/cm
0.0050 - 0.010 in/in
ASTM D955
Melt Flow 9.0 - 16 g/10 min

@Load 1.20 kg,
Temperature 300 °C
9.0 - 16 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 56.9 MPa
8250 psi
ASTM D638
Tensile Strength, Yield 56.9 MPa
8250 psi
ASTM D638
Elongation at Yield 10 %
10 %
ASTM D638
Flexural Strength 82.7 MPa
12000 psi
ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Izod Impact, Notched 1.17 J/cm

@Temperature 22.8 °C
2.20 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Gardner Impact 36.2 J
26.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 135 °C
275 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
265 °F
ASTM D648
UL RTI, Electrical 80.0 °C

@Thickness 1.50 mm
176 °F

@Thickness 0.0591 in
UL 746
80.0 °C

@Thickness 3.00 mm
176 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 80.0 °C

@Thickness 1.50 mm
176 °F

@Thickness 0.0591 in
UL 746
80.0 °C

@Thickness 3.00 mm
176 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 80.0 °C

@Thickness 1.50 mm
176 °F

@Thickness 0.0591 in
UL 746
80.0 °C

@Thickness 3.00 mm
176 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 V-2

@Thickness 1.50 mm
V-2

@Thickness 0.0591 in
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 271 - 293 °C
520 - 560 °F
Middle Barrel Temperature 282 - 304 °C
540 - 580 °F
Front Barrel Temperature 293 - 316 °C
560 - 600 °F
Melt Temperature 288 - 316 °C
550 - 600 °F
Mold Temperature 76.7 - 98.9 °C
170 - 210 °F
Drying Temperature 118 - 124 °C
245 - 255 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.0005