Polymer Property : Tensile Strength at Break = 56.9 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	56.9 MPa	8250 psi	ASTM D638
Polymer Resources PC-FR2-TFE Polycarbonate, Flame Retardant, 5% PTFE Polycarbonate, Improved Flame Retardant, 5% PTFE LubricantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inform..
Tensile Strength at Break	56.9 MPa	8250 psi	ASTM D638
Polymer Resources PC-G5-IM Polycarbonate, 5% Glass Reinforced, Impact Modified, Foamable Polycarbonate, 5% Glass Reinforced, Impact Modified, FoamableProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inf..
Tensile Strength at Break	56.9 MPa	8250 psi	ASTM D638
Polymer Resources PPX-GP2 Modified PPO, General Purpose with HDT of 250 F (Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Tensile Strength at Break	56.9 MPa	8250 psi	50 mm/min; ASTM D638
Samsung Cheil Industries InfinoÂ® UF-1013 PC, Unreinforced FR Information provided by Samsung Cheil Industries.
Tensile Strength at Break	56.9 MPa	8250 psi	50 mm/min; ASTM D638
Samsung Cheil Industries InfinoÂ® UF-1013 PC, Unreinforced FR Information provided by Samsung Cheil Industries.