Polymer Resources NY66-G60 Nylon 66, 60% Glass Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 60% Glass Fiber Filled
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources NY66-G60 Nylon 66, 60% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nylon 66, 60% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.71 g/cc
1.71 g/cc
ASTM D792
Linear Mold Shrinkage 0.0030 - 0.012 cm/cm
0.0030 - 0.012 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 227 MPa
32900 psi
ASTM D638
Tensile Strength, Yield 227 MPa
32900 psi
ASTM D638
Flexural Strength 341 MPa
49500 psi
ASTM D790
Flexural Modulus 19.13 GPa
2775 ksi
ASTM D790
Izod Impact, Notched 1.33 J/cm

@Temperature 22.8 °C
2.50 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 257 °C
495 °F
ASTM D648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0626 in
HB

@Thickness 3.17 mm
HB

@Thickness 0.125 in
Processing Properties Metric English Comments
Rear Barrel Temperature 266 - 288 °C
510 - 550 °F
Middle Barrel Temperature 271 - 293 °C
520 - 560 °F
Front Barrel Temperature 277 - 299 °C
530 - 570 °F
Melt Temperature 285 - 304 °C
545 - 580 °F
Mold Temperature 93.3 - 110 °C
200 - 230 °F
Drying Temperature 73.9 - 85.0 °C
165 - 185 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.0005