- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 495 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 495 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | ISO 75, ASTM D648 |
| Nilit Nilamid A3 H G10 50% Glass Reinforced PA66 Description: Nilamid A3 H G10 (50% Glass Reinforced) is a high strength material, that is used for structural applications. It is easy to mould, and shows outstanding stiffness and creep resistance,.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | ASTM D648 |
| Polymer Resources NY66-G50 Nylon 66, 50% Glass Reinforced Nylon 66, 50% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are test.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | ASTM D648 |
| Polymer Resources NY66-G60 Nylon 66, 60% Glass Reinforced Nylon 66, 60% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are test.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
Annealed; 2 hours at 200°C; ASTM D648 |
| Solvay Specialty Polymers AvaSpire® AV-848 GF30 Polyaryletherketone (PAEK)
(Unverified Data**) AvaSpire AV-848 GF30 is a 30% glass fiber-reinforced, high-temperature, polyaryletherketone (PAEK) that has been specifically formulated to provide several performance advantages over comparable gra.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP OFL36 PPS - Linear LNP* LUBRICOMP* OFL36 is a compound based on PPS - Linear resin containing 30% Glass Fiber, 15% PTFE. Added features of this grade include: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | ISO 75/Af |
| Solvay TECHNYLSTARâ„¢ AFX 218 V60 PA6, 60% glass filled, DRY Description: TECHNYLSTARâ„¢ AFX 218 V60 is based on a patented high flow polyamide 66 resin (Technylstar), heat stabilized, reinforced with 60% of glass fiber, for injection molding.Benefits: Due.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RX06480 PA 66 (Asia Pacific) LNP* LUBRICOMP* RX06480 is a compound based on Nylon 66 resin containing PTFE, Glass Fiber, Silicone. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Unannealed; ASTM D648 |
| Techmer ES Electrablend® PA6/6 CF30 BK 30% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 30% Filler by WeightAdditive: LubricantFeatures: Electrically Conductive and LubricatedAppearance: BlackInf.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Annealed; ASTM D648 |
| Solvay Specialty Polymers AvaSpire® AV-848 CF30 Polyaryletherketone (PAEK), 30% Carbon Fiber AvaSpire® AV-848 CF30 is a 30% carbon fiber-reinforced, high-temperature, polyaryletherketone (PAEK) that has been specifically formulated to provide several performance advantages over comparabl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Solvay Specialty Polymers AvaSpire® AV-848 GF30 Polyaryletherketone (PAEK), 30% Glass Fiber AvaSpire® AV-848 GF30 is a 30% glass fiber-reinforced, high-temperature, polyaryletherketone (PAEK) that has been specifically formulated to provide several performance advantages over comparable.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | ASTM D648 |
| Techmer ES Electrafil® J-1/CF/40 BK PA66 |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | ASTM D648 |
| Techmer ES Electrafil® J-1/CF/40 NAT PA66 |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF33 BK024 33% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: LubricantFeatures: Lubricated Appearance: BlackInformation provided by TP Comp.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF55 L BK 55% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 55% Filler by WeighAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedUL File Nu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF60 HS UV BK 60% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 60% Filler by WeightAdditive: Lubricant, UV Stabilizer and Heat StabilizerFeatures: Lubricated, Good UV Resi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF60 L BK 60% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 60% Filler by WeightAdditive: Lubricant Features: Lubricated Appearance: BlackInformation provided by TP Com.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 LGF60 HS L BK 12 mm Availability: North AmericaForms: PelletsFiller/Reinforcement: Long Glass FiberAdditive: Lubricant and Heat StabilizerFeatures: Lubricated, Heat Stabilized and Good MoldabilityAppearance: BlackProce.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP RC006XXH PA 66 LNP* THERMOCOMP* RC006XXH is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF60 HS L 60% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 60% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedUL File N.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF60 TL10 60% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 60% Filler by WeightAdditive: Lubricant Features: Lubricated Appearance: BlackTPCI# 8575101Information provi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF70 HS L BK 70% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 70% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedUL File N.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 LGF60 HS L BK 12 mm Availability: North AmericaForms: PelletsFiller/Reinforcement: Long Glass FiberAdditive: Lubricant, UV Stabilized and Heat StabilizerFeatures: Lubricated and Heat StabilizedProcessing Method: Inject.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C @Thickness 6.40 mm |
495 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL GTX APS440 PPE+PPS (Asia Pacific) PPE+PPS, GF40%, FR V-0 |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | ASTM D648 |
| Clariant Renol PA111G20CF10BK Nylon 66, 20% Glass and 10% Carbon Filled Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 624 Nylon 6/6, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.43% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 754 Glass Reinforced, Flow Enhanced, PPS Alloy, UL Data provided by the manufacturer, ComAlloy International Company.40% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 753 Glass Reinforced, Flow Enhanced, PPS Alloy, UL Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | ASTM D648 |
| LATI LARTON GCE/60 60% Mixed Glass Fiber and Special Mineral Filled Polyphenylene sulfide (PPS)
(discontinued Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| LNP Verton™ UF-700-12 Polyphthalamide, Long Glass Fiber Filled
(discontinued **) LNP™ Verton™ UF-700-12 HS EXP is a compound based on Polyphthalamide resin containing Long Glass Fiber. Added features of this material include: Heat Stabilized.Information provided by LNPThis dat.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP VERTON RX06097 PA 66 (Europe-Africa-Middle East) LNP* VERTON* RX06097 is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Easy Molding, UV-Stabilized. |
|||