PTS Trilac® ABS-HS6500 High Impact ABS Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Trilac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Trilac® ABS-HS6500 High Impact ABS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Melt Flow | 15 g/10 min @Load 10.0 kg, Temperature 220 °C |
15 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 101 | 101 | ASTM D785 |
| Tensile Strength, Yield | 46.9 MPa | 6800 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Flexural Yield Strength | 73.1 MPa | 10600 psi | ASTM D790 |
| Flexural Modulus | 2.25 GPa | 326 ksi | ASTM D790 |
| Izod Impact, Notched | 2.94 J/cm @Thickness 6.35 mm |
5.51 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 3.47 J/cm @Thickness 3.17 mm |
6.50 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 °C | 380 °F | |
| Middle Barrel Temperature | 216 °C | 420 °F | |
| Front Barrel Temperature | 227 °C | 440 °F | |
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | Nozzle temp not greater than stock |
| Mold Temperature | 48.9 - 65.6 °C | 120 - 150 °F | |
| Drying Temperature | 87.8 - 93.3 °C | 190 - 200 °F | |
| Dry Time | 2 - 24 hour | 2 - 24 hour | |
| Injection Pressure | 68.9 - 82.7 MPa | 10000 - 12000 psi | |
| Back Pressure | 0.689 MPa | 100 psi | |
| Screw Speed | 50 - 60 rpm | 50 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Fill Speed | Slow to Moderate |
Users viewing this material also viewed the following:
- RheTech Products G13P100-00 13% Glass Fiber Reinforced Polypropylene, Natural
- Huntsman PE2018 Injection Molding Polyethylene (discontinued **)
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 20 PHR Hi-Sil 233 Filler
- Flint Hills P4G2Z-026 Homopolymer Polypropylene
- H.C. Starck Amperit® 720.054 Blended Chromium Oxide-Aluminum Oxide-Titanium Oxide 80-17-3 (Cr2O3-Al2O3-TiO2)
- Samsung Cheil Industries Starex® VG-4920F ABS, Glass Filled FR
- SABIC Innovative Plastics NORYL PX1112 PPE+HIPS (Europe-Africa-Middle East)
- Vyncolit X655 Novolac Phenolic
- ELASTO UK Dryflex® 500700S SEBS Based Material, Unfilled Qualities, 70A Hardness, Translucent
- ChevronTexaco 8-T White Oil
Copyright © lookpolymers.com All Rights Reserved