Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 88.9 °C | 192 °F | Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
Network Polymers SAN 279 Water White Color Description: SAN - Styrene Acrylonitrile Transparent Engineering ThermoplasticInformation provided by Network Polymers Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 6.40 mm |
192 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Cycoloy® CM6140 PC+ABS (Asia Pacific) Cycoloy resin grade CM6140 is a flame retardant, filled PC/ABS blend. It is of non-brominated & non-chlorinated FR system to meet UL94 V0 at 0.8mm. Key features include thin wall FR, higher stiffnes.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS (Europe-Africa-Middle East) Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection mol.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 3.20 mm |
192 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Cycoloy® CX7211 PC+ABS Cycoloy* CX7211 PC/ABS resin is a non-filled, injection moldable grade which has UL 94 rating at 2.5 mm 5VA. Cycoloy CX7211 resin provides all color options and features an excellent balance of flo.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 3.20 mm |
192 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Cycoloy® CX7211 PC+ABS (Asia Pacific) Cycoloy* CX7211 PC/ABS resin is a non-filled, injection moldable grade which has UL 94 rating at 2.5 mm 5VA. Cycoloy CX7211 resin provides all color options and features an excellent balance of flo.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 3.20 mm |
192 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Cycoloy® CX7240 PC+ABS Cycoloy* CX7240 resin is an injection moldable PC/ABS blend. It contains non-brominated and non-chlorinated flame retardant systems to meet UL-94 V0 at 0.75mm, V1 at 0.6mm, V2 at 0.2mm and 5VB at 1... |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 3.20 mm |
192 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
SABIC Innovative Plastics Cycoloy® CX7240U PC+ABS (Europe-Africa-Middle East) Cycoloy* CX7240U resin is an injection moldable PC/ABS blend with a UV stabilization package. It contains non-brominated and non-chlorinated flame retardant systems to meet thin wall flame resistanc.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics GELOY CR8510 ASA (Asia Pacific) ASA with outstanding UV exposure performance for both exterior and interior applications. F1 Rated. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 3.20 mm |
192 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics GELOY XP7550 ASA+PC (Asia Pacific) Injection molding ASA-PC Blend suitable for exterior applications featuring outdoor weatherability, toughness, good heat performance and excellent flow. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 - 177 °C | 192 - 350 °F | Average value: 149 °C Grade Count:38 |
Overview of materials for Acetal Copolymer, 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% ar.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | |
Polimeri Europa SINKRAL B23 ABS, Heat Stabilized
(discontinued **) Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,105-04-16-25 High heat resistant grade with good impact resistance. Suitable for injection moulding and extrusi.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 3.20 mm |
192 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS LNP LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% PTFE. Added features of this material include: Internally Lubricated. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 6.40 mm |
192 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
LG Chemical MP220 ABS, High Adhesion, Heat Resistance Feature: Injection Molding, High Adhesion, Metal PlatingApplication: Automobiles Radiator Grill, MoldingCAS No. 9003-56-9 and 9003-54-7Information provided by LG Chemical |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | ASTM D648 |
GRECO ISOPAK 547 ABS Resin High Impact GradeInformation provided by Greater Eastern Resins Industrial Co., Ltd. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP LUBRICOMP RL0019 PA 66 LNP LUBRICOMP* RL0019 is a compound based on Nylon 66 resin containing 5% PTFE. Added features of this material include: Flame Retardant, Wear Resistant. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 3.20 mm |
192 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
SABIC Innovative Plastics LNP Lubriloy D20001 PC LNP LUBRILOY* D20001 is a compound based on Polycarbonate resin containing Flame Retardant, Proprietary Lubricant. Added features of this material include: Flame Retardant.This data was supplied by.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 6.40 mm |
192 °F @Thickness 0.252 in |
ASTM D648 |
Samsung Cheil Industries Starex® BF-0370 MABS, Unreinforced Scratch Resistant Scratch resistant material that is used in the exterior of electric products and household appliancesInformation provided by Samsung Cheil Industries. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 6.40 mm |
192 °F @Thickness 0.252 in |
ASTM D648 |
Samsung Cheil Industries Starex® LX-0970 MS ABS, Unreinforced Metallic-Look Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP Thermocomp MH0500A PP (Asia Pacific) LNP THERMOCOMP* MH0500A is a compound based on Polypropylene resin. Added features of this material include: High Specific Gravity.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 6.40 mm |
192 °F @Thickness 0.252 in |
ASTM D648 |
Samsung Cheil Industries Starex® WX-9300UV ASA, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 6.40 mm |
192 °F @Thickness 0.252 in |
ASTM D648 |
Samsung Cheil Industries Infino® NE-1050 PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 6.40 mm |
192 °F @Thickness 0.252 in |
ASTM D648 |
Samsung Cheil Industries Starex® ES-0173 ABS, Extrusion Grade Extrusion ABS for the interior of refrigerator with HCFC-141b, down gauging characteristicInformation provided by Samsung Cheil Industries. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 6.40 mm |
192 °F @Thickness 0.252 in |
ASTM D648 |
Samsung Cheil Industries Starex® LX-0970 MS ABS, Unreinforced Metallic-Look Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | Annealed; ASTM D648 |
Lubrizol Isoplast® 2530 Engineering Thermoplastic Polyurethane Resin for Medical Applications Features: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | annealed; ISO 75 |
Chi Mei Polyrex® PH-88 Polystyrene - High Impact High impact |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | unannealed; ISO 75 |
Chi Mei Polylac® PA-756 ABS - High Flow High rigid, high flow |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | ASTM D648 |
Ashley Polymers Ashlene® ABS Resin F-214 General purpose, medium impact resin.Data provided by the manufacturer |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | 90 Minute UV Cure + Thermal; ASTM D648 |
3D Systems Accura® SI 40 Plastic for the SLA® 500 System Accura 40 "Ar" or "Hc" type materials - for the SLA 500 system. Mimics Nylon 6:6ApplicationsHigh temperature testing:Under hood bolt-on testingWind tunnel testingHVAC testingPrototyping and testing .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | ASTM D648 |
Resirene Resirene® HH-107 General Purpose Polystyrene Features:Medium FlowHigh HeatHigh Molecular WeightHigh ProductivityFDA Rating: 21 CFR 177.1640Mechanical StrengthApplications:Thin Wall ApplicationsExtrusionGPPS/HIPS BlendsCD CasesCassette CasesInf.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | 80*10*4 s=60mm; ISO 75-1 a |
Sax Polymers SAXATEC 4115 Acrylonitrile Styrene Acrylate SAXATEC 4115 is a medium viscosity, weatherable ASA injection molding grade, characterized by high impact strength, high stiffness and good resistance to heat distortion.Information provided by SAX .. |