Nilit Nilamid A3 H6 G5 25% Glass Reinforced PA66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Nilit
Trade Name Nilamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Nilit Nilamid A3 H6 G5 25% Glass Reinforced PA66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Nilamid A3 H6 G5 is a 25% glass fiber reinforced NYLON 66 with a special stabilization system against hot oil and grease. As a result of this stabilization, the material has a brown natural color. It is used for applications which run in hot mineral oil, such as bearing cages, cam shafts and couplings. Because this material also demonstrates good hot air heat stability and has a low ionic content, it is also used for electrical applications such as bobbins.Key characteristics: Excellent heat stability and stability against hot oil and greaseGood overall mechanical performance up to 150°CBrown natural colorEasy processingInformation provided by NILIT.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
ASTM D792, ISO 1183
Water Absorption 0.80 %
0.80 %
23°C, 24h in H<sub>2</sub>O; sim. ISO 62
Water Absorption at Saturation 5.5 %
5.5 %
sim. ISO 62
Linear Mold Shrinkage, Flow 0.0035 cm/cm
0.0035 in/in
Euronil
Linear Mold Shrinkage, Transverse 0.0055 cm/cm
0.0055 in/in
Euronil
Mechanical Properties Metric English Comments
Tensile Strength, Yield 150 MPa
21800 psi
ISO 527, ASTM D638
Elongation at Break 3.0 %
3.0 %
ISO 527, ASTM D638
Flexural Yield Strength 230 MPa
33400 psi
ISO 178, ASTM D790
Flexural Modulus 7.80 GPa
1130 ksi
ISO 178, ASTM D790
4.50 GPa

@Temperature 90.0 °C
653 ksi

@Temperature 194 °F
ISO 178, ASTM D790
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Temperature 23.0 °C
3.81 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched 4.80 J/cm²
22.8 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 130 °C
266 °F
20,000 hr; IEC 216
Deflection Temperature at 0.46 MPa (66 psi) 255 °C
491 °F
ISO 75, ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 248 °C
478 °F
ISO 75, ASTM D648
Vicat Softening Point 250 °C
482 °F
49 N; ISO 306, ASTM D1525
255 °C
491 °F
9.8 N; ISO 306, ASTM D1525
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Oxygen Index 24 %
24 %
ASTM D2863
Glow Wire Test 650 °C

@Thickness 0.800 mm
1200 °F

@Thickness 0.0315 in
Glow Wire Flammability Index; IEC 694-2-12
650 °C

@Thickness 3.20 mm
1200 °F

@Thickness 0.126 in
Glow Wire Flammability Index; IEC 694-2-12
Electrical Properties Metric English Comments
Dielectric Strength 20.0 kV/mm

@Thickness 2.00 mm
508 kV/in

@Thickness 0.0787 in
ASTM D149
Comparative Tracking Index 350 V

@Thickness 3.20 mm
350 V

@Thickness 0.126 in
Sol. B; IEC 112, UL 746A
500 V

@Thickness 3.20 mm
500 V

@Thickness 0.126 in
Sol. A; IEC 112, UL 746A
Processing Properties Metric English Comments
Nozzle Temperature 280 - 295 °C
536 - 563 °F
Zone 1 270 - 290 °C
518 - 554 °F
hopper
Zone 2 275 - 290 °C
527 - 554 °F
Zone 3 280 - 295 °C
536 - 563 °F
Zone 4 280 - 295 °C
536 - 563 °F
Melt Temperature 275 - 300 °C
527 - 572 °F
Do not melt above 300°C
Mold Temperature 90.0 - 110 °C
194 - 230 °F
Preferred
Drying Temperature 80.0 - 85.0 °C
176 - 185 °F
Dry Time 4 hour
4 hour
Injection Pressure 70.0 - 100 MPa
10200 - 14500 psi
Descriptive Properties Value Comments
Clamping Force in tons, 0.7 times the projected surface area in cm2
Heat Resistance - Ball Test OK
at 125°C, IEC 309
OK
at 165°C, IEC 309
Holding Pressure 90 Mpa