Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 230 MPa | 33400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers Opnyl OP6GF33 Nylon 6, 33% Glass Reinforced, Dry Nylon 6 - Glass reinforced (33 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the m.. |
|||
Flexural Yield Strength | 230 MPa @Temperature 90.0 °C |
33400 psi @Temperature 194 °F |
ISO 178, ASTM D790 |
Nilit Nilamid A3 H G10 50% Glass Reinforced PA66 Description: Nilamid A3 H G10 (50% Glass Reinforced) is a high strength material, that is used for structural applications. It is easy to mould, and shows outstanding stiffness and creep resistance,.. |
|||
Flexural Yield Strength | 230 MPa | 33400 psi | ISO 178, ASTM D790 |
Nilit Nilamid A3 H6 G5 25% Glass Reinforced PA66 Description: Nilamid A3 H6 G5 is a 25% glass fiber reinforced NYLON 66 with a special stabilization system against hot oil and grease. As a result of this stabilization, the material has a brown nat.. |
|||
Flexural Yield Strength | 230 MPa | 33400 psi | ISO 178, ASTM D790 |
Nilit Nilamid B3 H G6 30% Glass Fiber Reinforced PA6 Description: Nilamid B3 H G6 is a general purpose, 30% glass fiber reinforced NYLON 6 with a combination of good mechanical performance, impact strength and processability. It is one of the most wid.. |
|||
Flexural Yield Strength | 230 MPa | 33400 psi | DIN 53 452 |
Albis Plastics Tedur® L V 9400-1 PPS, 15% Carbon Fiber
(discontinued **) High Electrical and Thermal Conductivity, Long-term Anti-static Properties. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Clutch Components, BushingsProcessing: Inje.. |
|||
Flexural Yield Strength | 230 MPa | 33400 psi | ASTM D790 |
Solvay Specialty Polymers Ryton® R-4-230NA Polyphenylene Sulfide Compound
(Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® R-4-230NA is an advanced 40% fiberglass reinforced polyphenylene sulfide compound which provides reduced flash and improved processability compare.. |
|||
Flexural Yield Strength | 230 MPa @Strain 3.50 % |
33400 psi @Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A |
Lanxess Durethan® ECO BV 30 H2 900500 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, injection molding, heat-ageing stabilized, contains 30% pre-consumer recycled materialInformation provided by LANXESS. |
|||
Flexural Yield Strength | 230 MPa | 33400 psi | ASTM D790 |
Samyang Tripet® 2500G30 Polyethylene Terephthalate, 30% Glass Fiber Reinforced TRIPET® has excellent heat resistance, good surface, chemical resistance and high electrical performance.Applications:Coil BobbinConnectorMotor HousingLamp HousingRelay BaseIron bodyAll informati.. |
|||
Flexural Yield Strength | 230 MPa | 33400 psi | ASTM D790 |
Cheng Yu Plastic N6GV20 Flame Retardant Nylon 6, 20% Glass Filled |
|||
Flexural Yield Strength | 230 MPa | 33400 psi | 2 mm/min; ISO 178 |
Eurostar Staramide ACF2 PA66, 10% Carbon Fiber Reinforced, Heat stabilized, Injection Molding Staramide ACF2 is a 10% Carbon Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Yield Strength | 230 MPa | 33400 psi | ASTM D790 |
E-Polymers Tekaster® F615GFR , Flame Retardant, 30% Glass Reinforced PET 30% Glass Fiber Reinforced, Flame RetardantInformation provided by E-Polymers Co. Ltd. |
|||
Flexural Yield Strength | 230 MPa | 33400 psi | ASTM D790 |
E-Polymers TEKAMID® TB120G30 , 30% Glass Fiber Reinforced PA6, DAM 30% Glass Fiber Reinforced, Good impact resistanceInformation provided by E-Polymers Co. Ltd. |
|||
Flexural Yield Strength | 230 MPa | 33400 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON OE003A PPS - BRANCHED (Europe-Africa-Middle East) LNP* STATKON* OE003A is a compound based on PPS ( branched ) resin containing Carbon Fiber. Added features include: Electrically Conductive. |
|||
Flexural Yield Strength | 230 MPa | 33400 psi | ASTM D790 |
Solvay Specialty Polymers Amodel® AF-1133 V0 Polyphthalamide (PPA) Resin, 33% Glass Reinforced, at 50% RH
(di AMODEL AF-1133 V0 resin in a 33% glass reinforced, flame retarded polyphthalamide (PPA) which exhibits a high deflection temperature, tensile strength, and flexural modulus. The material has good d.. |