DuPont Performance Polymers Zytel® RS 3061HSL BK039A Nylon 610  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer DuPont Performance Polymers
Trade Name Zytel® RS
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® RS 3061HSL BK039A Nylon 610  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced Renewably Sourced Polyamide 610 Developed for Injection Molding Zytel RS 3061HSL BK039A is a renewably sourced polyamide 610 resin containing a minimum of 60% renewably sourced ingredient by weight. It is an unreinforced heat stabilized luInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.08 g/cc
0.0390 lb/in³
DAM; ISO 1183
Water Absorption 3.8 %

@Thickness 2.00 mm
 3.8 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.70 %

@Thickness 2.00 mm
 1.70 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity 77500 cP

@Shear Rate 5000 1/s,
Temperature 270 °C
 77500 cP

@Shear Rate 5000 1/s,
Temperature 518 °F
 ISO 11403-1 -2
94600 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
 94600 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
103900 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
 103900 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
215900 cP

@Shear Rate 500 1/s,
Temperature 270 °C
 215900 cP

@Shear Rate 500 1/s,
Temperature 518 °F
 ISO 11403-1 -2
294000 cP

@Shear Rate 500 1/s,
Temperature 250 °C
 294000 cP

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
349300 cP

@Shear Rate 500 1/s,
Temperature 240 °C
 349300 cP

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.012 cm/cm
0.012 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.012 cm/cm
0.012 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Stress 0.0800 MPa

@Strain 0.0300 %,
Temperature -40.0 °C
 11.6 psi

@Strain 0.0300 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
0.290 MPa

@Strain 0.0300 %,
Temperature -20.0 °C
 42.1 psi

@Strain 0.0300 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
0.350 MPa

@Strain 0.0400 %,
Temperature -40.0 °C
 50.8 psi

@Strain 0.0400 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
0.530 MPa

@Strain 0.180 %,
Temperature 150 °C
 76.9 psi

@Strain 0.180 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
0.530 MPa

@Strain 0.0400 %,
Temperature 0.000 °C
 76.9 psi

@Strain 0.0400 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
0.740 MPa

@Strain 0.160 %,
Temperature 90.0 °C
 107 psi

@Strain 0.160 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
0.750 MPa

@Strain 0.170 %,
Temperature 150 °C
 109 psi

@Strain 0.170 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
0.800 MPa

@Strain 0.160 %,
Temperature 90.0 °C
 116 psi

@Strain 0.160 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
0.880 MPa

@Strain 0.0600 %,
Temperature -20.0 °C
 128 psi

@Strain 0.0600 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
1.48 MPa

@Strain 0.200 %,
Temperature 40.0 °C
 215 psi

@Strain 0.200 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
2.32 MPa

@Strain 0.0700 %,
Temperature 23.0 °C
 336 psi

@Strain 0.0700 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
2.81 MPa

@Strain 0.130 %,
Temperature -40.0 °C
 408 psi

@Strain 0.130 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
2.90 MPa

@Strain 0.100 %,
Temperature 0.000 °C
 421 psi

@Strain 0.100 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
3.10 MPa

@Strain 0.150 %,
Temperature -20.0 °C
 450 psi

@Strain 0.150 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
3.11 MPa

@Strain 0.140 %,
Temperature -40.0 °C
 451 psi

@Strain 0.140 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
3.65 MPa

@Strain 0.170 %,
Temperature 0.000 °C
 529 psi

@Strain 0.170 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
5.21 MPa

@Strain 0.220 %,
Temperature -40.0 °C
 756 psi

@Strain 0.220 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
5.93 MPa

@Strain 0.250 %,
Temperature -40.0 °C
 860 psi

@Strain 0.250 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
7.09 MPa

@Strain 0.300 %,
Temperature -20.0 °C
 1030 psi

@Strain 0.300 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
14.65 MPa

@Strain 0.570 %,
Temperature -20.0 °C
 2125 psi

@Strain 0.570 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
14.67 MPa

@Strain 18.87 %,
Temperature 150 °C
 2128 psi

@Strain 18.87 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
18.09 MPa

@Strain 18.27 %,
Temperature 150 °C
 2624 psi

@Strain 18.27 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
22.65 MPa

@Strain 16.81 %,
Temperature 90.0 °C
 3285 psi

@Strain 16.81 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
24.05 MPa

@Strain 0.970 %,
Temperature 23.0 °C
 3488 psi

@Strain 0.970 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
25.73 MPa

@Strain 17.16 %,
Temperature 90.0 °C
 3732 psi

@Strain 17.16 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
28.02 MPa

@Strain 45.85 %,
Temperature 90.0 °C
 4064 psi

@Strain 45.85 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
34.93 MPa

@Strain 18.59 %,
Temperature 40.0 °C
 5066 psi

@Strain 18.59 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
36.68 MPa

@Strain 44.32 %,
Temperature 40.0 °C
 5320 psi

@Strain 44.32 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
39.37 MPa

@Strain 1.65 %,
Temperature 0.000 °C
 5710 psi

@Strain 1.65 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
60.69 MPa

@Strain 2.60 %,
Temperature -40.0 °C
 8802 psi

@Strain 2.60 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
66.89 MPa

@Strain 4.33 %,
Temperature 0.000 °C
 9702 psi

@Strain 4.33 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
80.09 MPa

@Strain 3.73 %,
Temperature -40.0 °C
 11620 psi

@Strain 3.73 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
85.03 MPa

@Strain 8.73 %,
Temperature -20.0 °C
 12330 psi

@Strain 8.73 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
85.27 MPa

@Strain 4.35 %,
Temperature -20.0 °C
 12370 psi

@Strain 4.35 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
Tensile Strength, Yield 55.0 MPa
7980 psi
50%RH; ISO 527-1/-2
65.0 MPa
9430 psi
DAM; ISO 527-1/-2
Elongation at Yield 4.5 %
4.5 %
DAM; ISO 527-1/-2
25 %
25 %
50%RH; ISO 527-1/-2
Tensile Modulus 1.38 GPa
200 ksi
50%RH; ISO 527-1/-2
2.40 GPa
348 ksi
DAM; ISO 527-1/-2
Shear Strength 0.017675 MPa

@Shear Rate 50.0 1/s,
Temperature 270 °C
 2.5635 psi

@Shear Rate 50.0 1/s,
Temperature 518 °F
 ISO 11403-1 -2
0.02448 MPa

@Shear Rate 50.0 1/s,
Temperature 250 °C
 3.551 psi

@Shear Rate 50.0 1/s,
Temperature 482 °F
 ISO 11403-1 -2
0.032465 MPa

@Shear Rate 50.0 1/s,
Temperature 240 °C
 4.7087 psi

@Shear Rate 50.0 1/s,
Temperature 464 °F
 ISO 11403-1 -2
0.10795 MPa

@Shear Rate 500 1/s,
Temperature 270 °C
 15.657 psi

@Shear Rate 500 1/s,
Temperature 518 °F
 ISO 11403-1 -2
0.147 MPa

@Shear Rate 500 1/s,
Temperature 250 °C
 21.3 psi

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
0.17465 MPa

@Shear Rate 500 1/s,
Temperature 240 °C
 25.331 psi

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
0.3875 MPa

@Shear Rate 5000 1/s,
Temperature 270 °C
 56.20 psi

@Shear Rate 5000 1/s,
Temperature 518 °F
 ISO 11403-1 -2
0.473 MPa

@Shear Rate 5000 1/s,
Temperature 250 °C
 68.6 psi

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
0.5195 MPa

@Shear Rate 5000 1/s,
Temperature 240 °C
 75.35 psi

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
DAM; ISO 180/1A
6.30 kJ/m²
3.00 ft-lb/in²
50%RH; ISO 180/1A
Charpy Impact Unnotched 3.40 J/cm²
16.2 ft-lb/in²
DAM; ISO 179/1eU
Charpy Impact, Notched 0.470 J/cm²
2.24 ft-lb/in²
DAM; ISO 179/1eA
0.850 J/cm²
4.04 ft-lb/in²
50%RH; ISO 179/1eA