EPICHEM Epiryl G2 PPO 20GF Polyphenylene oxide, 20% Glass Fiber

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 20% Glass Filled
Manufacturer EPICHEM srl
Trade Name Epiryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF EPICHEM Epiryl G2 PPO 20GF Polyphenylene oxide, 20% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics: 20% glass fibre filled
Physical Properties Metric English Comments
Density 1.20 - 1.25 g/cc
0.0434 - 0.0452 lb/in³
ASTM D792, ISO 1183
Water Absorption <= 0.10 %

@Temperature 23.0 °C
<= 0.10 %

@Temperature 73.4 °F
24h; ASTM D570, ISO 62
Linear Mold Shrinkage 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 80
80
ASTM D785, ISO 2039/2
Tensile Strength, Yield 85.0 MPa
12300 psi
ASTM D638, ISO R527
Flexural Strength 140 MPa
20300 psi
ASTM D790, ISO 178
Flexural Modulus 5.50 GPa
798 ksi
ASTM D790, ISO 178
Izod Impact, Notched 0.600 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
1.12 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
ASTM D256, ISO 180/4a
0.700 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
1.31 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256, ISO 180/4a
0.700 J/cm

@Thickness 3.20 mm,
Temperature 0.000 °C
1.31 ft-lb/in

@Thickness 0.126 in,
Temperature 32.0 °F
ASTM D256, ISO 180/4a
Thermal Properties Metric English Comments
Hot Ball Pressure Test >= 120 °C
>= 248 °F
BS 3456, IEC 335
Deflection Temperature at 1.8 MPa (264 psi) 125 °C
257 °F
ASTM D648, ISO 75
Vicat Softening Point 130 °C

@Load 5.00 kg
266 °F

@Load 11.0 lb
120°C/min; ASTM D1525/B, ISO 306/B
140 °C

@Load 0.999 kg
284 °F

@Load 2.20 lb
120°C/min; ASTM D1525/A, ISO 306/A
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Glow Wire Test 650 °C

@Thickness 3.20 mm
1200 °F

@Thickness 0.126 in
VDE 0471/P2-4, IEC 695
650 °C

@Thickness 2.00 mm
1200 °F

@Thickness 0.0787 in
VDE 0471/P2-4, IEC 695
Electrical Properties Metric English Comments
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
ASTM D257, IEC 93
Dielectric Constant 3.0

@Frequency 1000 Hz
3.0

@Frequency 1000 Hz
ASTM D150, IEC 250
Dielectric Strength 70.0 kV/mm
1780 kV/in
ASTM D149, IEC 243
Dissipation Factor 0.0030

@Frequency 1000 Hz
0.0030

@Frequency 1000 Hz
ASTM D150, IEC 250
Comparative Tracking Index 250 V
250 V
VDE 0303-P1, IEC 112