DuPont Performance Polymers Zytel® PLUS PLS95G50DH2 BK261 Nylon  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon
Manufacturer DuPont Performance Polymers
Trade Name Zytel® PLUS
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® PLUS PLS95G50DH2 BK261 Nylon  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zytel® PLS95G50DH2 BK261is a high flow 50% glass reinforced PA nylon resin using SHIELD Technology, only from DuPont providing exceptional Heat Resistance & High stiffness for automotive under hood applications like charge air cooler caps.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.59 g/cc
0.0574 lb/in³
DAM; ISO 1183
Filler Content 50 %
50 %
DAM
Water Absorption 1.3 %

@Temperature 23.0 °C
 1.3 %

@Temperature 73.4 °F
 Equilibrium 50%RH; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0030 cm/cm

@Thickness 2.00 mm
 0.0030 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0060 cm/cm

@Thickness 2.00 mm
 0.0060 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 175 MPa

@Temperature 23.0 °C
 25400 psi

@Temperature 73.4 °F
 50%RH; ISO 527
247 MPa

@Temperature 23.0 °C
 35800 psi

@Temperature 73.4 °F
 DAM; ISO 527
Tensile Stress 0.810 MPa

@Strain 0.000 %,
Temperature 220 °C
 117 psi

@Strain 0.000 %,
Temperature 428 °F
 DAM; ISO 11403-1/-2
1.04 MPa

@Strain 0.000 %,
Temperature 200 °C
 151 psi

@Strain 0.000 %,
Temperature 392 °F
 DAM; ISO 11403-1/-2
1.27 MPa

@Strain 0.000 %,
Temperature 180 °C
 184 psi

@Strain 0.000 %,
Temperature 356 °F
 DAM; ISO 11403-1/-2
1.29 MPa

@Strain 0.000 %,
Temperature 150 °C
 187 psi

@Strain 0.000 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
1.38 MPa

@Strain 0.000 %,
Temperature 150 °C
 200 psi

@Strain 0.000 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
1.41 MPa

@Strain 0.000 %,
Temperature 120 °C
 205 psi

@Strain 0.000 %,
Temperature 248 °F
 50%RH; ISO 11403-1/-2
1.48 MPa

@Strain 0.000 %,
Temperature 120 °C
 215 psi

@Strain 0.000 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
1.64 MPa

@Strain 0.000 %,
Temperature 90.0 °C
 238 psi

@Strain 0.000 %,
Temperature 194 °F
 50%RH; ISO 11403-1/-2
1.75 MPa

@Strain 0.000 %,
Temperature 90.0 °C
 254 psi

@Strain 0.000 %,
Temperature 194 °F
 DAM; ISO 11403-1/-2
1.76 MPa

@Strain 0.000 %,
Temperature 60.0 °C
 255 psi

@Strain 0.000 %,
Temperature 140 °F
 50%RH; ISO 11403-1/-2
1.76 MPa

@Strain 0.000 %,
Temperature 0.000 °C
 255 psi

@Strain 0.000 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1/-2
1.83 MPa

@Strain 0.000 %,
Temperature 40.0 °C
 265 psi

@Strain 0.000 %,
Temperature 104 °F
 50%RH; ISO 11403-1/-2
1.93 MPa

@Strain 0.000 %,
Temperature 0.000 °C
 280 psi

@Strain 0.000 %,
Temperature 32.0 °F
 DAM; ISO 11403-1/-2
2.00 MPa

@Strain 0.000 %,
Temperature 23.0 °C
 290 psi

@Strain 0.000 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1/-2
2.17 MPa

@Strain 0.000 %,
Temperature 60.0 °C
 315 psi

@Strain 0.000 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
2.37 MPa

@Strain 0.000 %,
Temperature 23.0 °C
 344 psi

@Strain 0.000 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
2.43 MPa

@Strain 0.000 %,
Temperature 40.0 °C
 352 psi

@Strain 0.000 %,
Temperature 104 °F
 DAM; ISO 11403-1/-2
2.70 MPa

@Strain 0.000 %,
Temperature -20.0 °C
 392 psi

@Strain 0.000 %,
Temperature -4.00 °F
 DAM; ISO 11403-1/-2
2.71 MPa

@Strain 0.000 %,
Temperature -20.0 °C
 393 psi

@Strain 0.000 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1/-2
3.30 MPa

@Strain 0.0600 %,
Temperature 220 °C
 479 psi

@Strain 0.0600 %,
Temperature 428 °F
 DAM; ISO 11403-1/-2
3.88 MPa

@Strain 0.0500 %,
Temperature -20.0 °C
 563 psi

@Strain 0.0500 %,
Temperature -4.00 °F
 DAM; ISO 11403-1/-2
3.93 MPa

@Strain 0.0400 %,
Temperature -20.0 °C
 570 psi

@Strain 0.0400 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1/-2
4.18 MPa

@Strain 0.0600 %,
Temperature 200 °C
 606 psi

@Strain 0.0600 %,
Temperature 392 °F
 DAM; ISO 11403-1/-2
4.39 MPa

@Strain 0.0400 %,
Temperature 0.000 °C
 637 psi

@Strain 0.0400 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1/-2
4.73 MPa

@Strain 0.0600 %,
Temperature 150 °C
 686 psi

@Strain 0.0600 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
4.75 MPa

@Strain 0.0600 %,
Temperature 180 °C
 689 psi

@Strain 0.0600 %,
Temperature 356 °F
 DAM; ISO 11403-1/-2
5.17 MPa

@Strain 0.0500 %,
Temperature 120 °C
 750 psi

@Strain 0.0500 %,
Temperature 248 °F
 50%RH; ISO 11403-1/-2
5.50 MPa

@Strain 0.0600 %,
Temperature 150 °C
 798 psi

@Strain 0.0600 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
5.53 MPa

@Strain 0.110 %,
Temperature 220 °C
 802 psi

@Strain 0.110 %,
Temperature 428 °F
 DAM; ISO 11403-1/-2
5.66 MPa

@Strain 0.0600 %,
Temperature 120 °C
 821 psi

@Strain 0.0600 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
6.06 MPa

@Strain 0.0500 %,
Temperature 90.0 °C
 879 psi

@Strain 0.0500 %,
Temperature 194 °F
 50%RH; ISO 11403-1/-2
6.19 MPa

@Strain 0.0500 %,
Temperature 90.0 °C
 898 psi

@Strain 0.0500 %,
Temperature 194 °F
 DAM; ISO 11403-1/-2
6.36 MPa

@Strain 0.0400 %,
Temperature 60.0 °C
 922 psi

@Strain 0.0400 %,
Temperature 140 °F
 50%RH; ISO 11403-1/-2
6.81 MPa

@Strain 0.0400 %,
Temperature 40.0 °C
 988 psi

@Strain 0.0400 %,
Temperature 104 °F
 50%RH; ISO 11403-1/-2
7.14 MPa

@Strain 0.130 %,
Temperature 200 °C
 1040 psi

@Strain 0.130 %,
Temperature 392 °F
 DAM; ISO 11403-1/-2
7.46 MPa

@Strain 0.0500 %,
Temperature 60.0 °C
 1080 psi

@Strain 0.0500 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
7.67 MPa

@Strain 0.180 %,
Temperature 220 °C
 1110 psi

@Strain 0.180 %,
Temperature 428 °F
 DAM; ISO 11403-1/-2
7.94 MPa

@Strain 0.110 %,
Temperature 150 °C
 1150 psi

@Strain 0.110 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
8.13 MPa

@Strain 0.0400 %,
Temperature 23.0 °C
 1180 psi

@Strain 0.0400 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1/-2
8.27 MPa

@Strain 0.120 %,
Temperature 180 °C
 1200 psi

@Strain 0.120 %,
Temperature 356 °F
 DAM; ISO 11403-1/-2
8.29 MPa

@Strain 0.0400 %,
Temperature 40.0 °C
 1200 psi

@Strain 0.0400 %,
Temperature 104 °F
 DAM; ISO 11403-1/-2
8.38 MPa

@Strain 0.0400 %,
Temperature 23.0 °C
 1220 psi

@Strain 0.0400 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
8.68 MPa

@Strain 0.0500 %,
Temperature 0.000 °C
 1260 psi

@Strain 0.0500 %,
Temperature 32.0 °F
 DAM; ISO 11403-1/-2
8.85 MPa

@Strain 0.110 %,
Temperature 120 °C
 1280 psi

@Strain 0.110 %,
Temperature 248 °F
 50%RH; ISO 11403-1/-2
9.66 MPa

@Strain 0.130 %,
Temperature 150 °C
 1400 psi

@Strain 0.130 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
9.75 MPa

@Strain 0.120 %,
Temperature 120 °C
 1410 psi

@Strain 0.120 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
9.79 MPa

@Strain 0.240 %,
Temperature 220 °C
 1420 psi

@Strain 0.240 %,
Temperature 428 °F
 DAM; ISO 11403-1/-2
10.02 MPa

@Strain 0.190 %,
Temperature 200 °C
 1453 psi

@Strain 0.190 %,
Temperature 392 °F
 DAM; ISO 11403-1/-2
10.15 MPa

@Strain 0.100 %,
Temperature 90.0 °C
 1472 psi

@Strain 0.100 %,
Temperature 194 °F
 50%RH; ISO 11403-1/-2
10.86 MPa

@Strain 0.110 %,
Temperature 90.0 °C
 1575 psi

@Strain 0.110 %,
Temperature 194 °F
 DAM; ISO 11403-1/-2
10.88 MPa

@Strain 0.0800 %,
Temperature 0.000 °C
 1578 psi

@Strain 0.0800 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1/-2
11.02 MPa

@Strain 0.100 %,
Temperature 60.0 °C
 1598 psi

@Strain 0.100 %,
Temperature 140 °F
 50%RH; ISO 11403-1/-2
11.02 MPa

@Strain 0.180 %,
Temperature 150 °C
 1598 psi

@Strain 0.180 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
11.11 MPa

@Strain 0.100 %,
Temperature -20.0 °C
 1611 psi

@Strain 0.100 %,
Temperature -4.00 °F
 DAM; ISO 11403-1/-2
11.34 MPa

@Strain 0.0800 %,
Temperature -20.0 °C
 1645 psi

@Strain 0.0800 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1/-2
11.57 MPa

@Strain 0.180 %,
Temperature 180 °C
 1678 psi

@Strain 0.180 %,
Temperature 356 °F
 DAM; ISO 11403-1/-2
11.89 MPa

@Strain 0.100 %,
Temperature 40.0 °C
 1725 psi

@Strain 0.100 %,
Temperature 104 °F
 50%RH; ISO 11403-1/-2