Polymer Property : Tensile Stress = 1.64 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Stress	1.64 MPa @Strain 100 %	238 psi @Strain 100 %	ASTM D412
Polymax® Maxelast® P1945 TPE, PP Overmold or Standalone use Polymax's TPE material complies with UL, VDE, FDA, RoHS and PAH's standards.Uses:Consumer ProductsToys & NoveltiesAuto PartsTool Hand GripsSporting GoodsWire & Cable ElectronicsMedical DevicesPlasti..
Tensile Stress	1.64 MPa @Strain 18.07 %, Temperature 90.0 °C	238 psi @Strain 18.07 %, Temperature 194 °F	TPE; ISO 11403-1 -2
DuPont Performance Polymers Hytrel® 3078 Polyester Elastomer TPC-ET (Unverified Data**) 30 Shore D High Performance Polyester Elastomer with Non-discoloring Stabilizer Hytrel 3078 is a very low modulus grade with nominal hardness of 30D. It contains non-discoloring stabilizer. It can b..
Tensile Stress	1.64 MPa @Strain 0.000 %, Temperature 90.0 °C	238 psi @Strain 0.000 %, Temperature 194 °F	50%RH; ISO 11403-1/-2
DuPont Performance Polymers Zytel® PLUS PLS95G50DH2 BK261 Nylon (Unverified Data**) Zytel® PLS95G50DH2 BK261is a high flow 50% glass reinforced PA nylon resin using SHIELD Technology, only from DuPont providing exceptional Heat Resistance & High stiffness for automotive under hood..
Tensile Stress	1.64 MPa @Strain 18.07 %, Temperature 90.0 °C	238 psi @Strain 18.07 %, Temperature 194 °F	TPE; ISO 11403-1 -2
DuPont Performance Polymers Hytrel® 3078FG Polyester Elastomer TPC-ET (Unverified Data**) 30 Shore D High Performance Polyester Elastomer Developed for Food Contact ApplicationsInformation provided by DuPont Performance Polymers
Tensile Stress	1.64 MPa @Strain 3.22 %, Temperature 40.0 °C	238 psi @Strain 3.22 %, Temperature 104 °F	ISO 527
DuPont Performance Polymers Hytrel® G4078W TPC-ET (Unverified Data**) Hytrel® G4078W is a low modulus grade with nominal hardness of 40D. It contains non-discoloring stabilizer. It can be processed by many conventional thermoplastic processing techniques like inject..