DuPont Performance Polymers Hytrel® 4068FG Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® 4068FG Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
40 Shore D High Performance Polyester Elastomer Developed for Food Contact ApplicationsInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Water Absorption 0.70 %

@Thickness 2.00 mm
 0.70 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.300 %

@Thickness 2.00 mm
 0.300 %

@Thickness 0.0787 in
 Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.0080 cm/cm
0.0080 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4 2577
Melt Flow 8.5 g/10 min

@Load 2.16 kg,
Temperature 220 °C
 8.5 g/10 min

@Load 4.76 lb,
Temperature 428 °F
 ISO 1133
9.0 g/10 min

@Load 2.16 kg,
Temperature 220 °C
 9.0 g/10 min

@Load 4.76 lb,
Temperature 428 °F
 cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 33
33
15s; ISO 868
<= 37
<= 37
ISO 868
Tensile Strength at Break 29.0 MPa
4210 psi
ISO 527-1/-2
Tensile Stress 2.40 MPa

@Strain 5.00 %
 348 psi

@Strain 5.00 %
 ISO 527-1/-2
3.50 MPa

@Strain 10.0 %
 508 psi

@Strain 10.0 %
 ISO 527-1/-2
6.70 MPa

@Strain 50.0 %
 972 psi

@Strain 50.0 %
 ISO 527-1/-2
1.40 MPa

@Strain 7.05 %,
Temperature 120 °C
 203 psi

@Strain 7.05 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.61 MPa

@Strain 6.85 %,
Temperature 100 °C
 234 psi

@Strain 6.85 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
1.66 MPa

@Strain 6.61 %,
Temperature 90.0 °C
 241 psi

@Strain 6.61 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
2.16 MPa

@Strain 7.12 %,
Temperature 60.0 °C
 313 psi

@Strain 7.12 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
2.20 MPa

@Strain 16.44 %,
Temperature 120 °C
 319 psi

@Strain 16.44 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.38 MPa

@Strain 7.13 %,
Temperature 40.0 °C
 345 psi

@Strain 7.13 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
2.39 MPa

@Strain 5.61 %,
Temperature 0.000 °C
 347 psi

@Strain 5.61 %,
Temperature 32.0 °F
 TPE; ISO 11403-1 -2
2.60 MPa

@Strain 26.51 %,
Temperature 120 °C
 377 psi

@Strain 26.51 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.66 MPa

@Strain 16.95 %,
Temperature 100 °C
 386 psi

@Strain 16.95 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
2.81 MPa

@Strain 36.58 %,
Temperature 120 °C
 408 psi

@Strain 36.58 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.81 MPa

@Strain 16.36 %,
Temperature 90.0 °C
 408 psi

@Strain 16.36 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
2.93 MPa

@Strain 45.98 %,
Temperature 120 °C
 425 psi

@Strain 45.98 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.03 MPa

@Strain 8.37 %,
Temperature 23.0 °C
 439 psi

@Strain 8.37 %,
Temperature 73.4 °F
 TPE; ISO 11403-1 -2
3.05 MPa

@Strain 59.4 %,
Temperature 120 °C
 442 psi

@Strain 59.4 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.14 MPa

@Strain 72.15 %,
Temperature 120 °C
 455 psi

@Strain 72.15 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.16 MPa

@Strain 27.05 %,
Temperature 100 °C
 458 psi

@Strain 27.05 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.22 MPa

@Strain 85.58 %,
Temperature 120 °C
 467 psi

@Strain 85.58 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.31 MPa

@Strain 98.33 %,
Temperature 120 °C
 480 psi

@Strain 98.33 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.40 MPa

@Strain 26.8 %,
Temperature 90.0 °C
 493 psi

@Strain 26.8 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
3.43 MPa

@Strain 37.15 %,
Temperature 100 °C
 497 psi

@Strain 37.15 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.44 MPa

@Strain 117.8 %,
Temperature 120 °C
 499 psi

@Strain 117.8 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.54 MPa

@Strain 131.22 %,
Temperature 120 °C
 513 psi

@Strain 131.22 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.54 MPa

@Strain 16.62 %,
Temperature 60.0 °C
 513 psi

@Strain 16.62 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
3.60 MPa

@Strain 47.25 %,
Temperature 100 °C
 522 psi

@Strain 47.25 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.67 MPa

@Strain 147.33 %,
Temperature 120 °C
 532 psi

@Strain 147.33 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.73 MPa

@Strain 36.55 %,
Temperature 90.0 °C
 541 psi

@Strain 36.55 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
3.74 MPa

@Strain 60.23 %,
Temperature 100 °C
 542 psi

@Strain 60.23 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.86 MPa

@Strain 73.94 %,
Temperature 100 °C
 560 psi

@Strain 73.94 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.87 MPa

@Strain 170.15 %,
Temperature 120 °C
 561 psi

@Strain 170.15 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.92 MPa

@Strain 46.3 %,
Temperature 90.0 °C
 569 psi

@Strain 46.3 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
3.93 MPa

@Strain 16.63 %,
Temperature 40.0 °C
 570 psi

@Strain 16.63 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
3.98 MPa

@Strain 86.92 %,
Temperature 100 °C
 577 psi

@Strain 86.92 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
4.08 MPa

@Strain 6.86 %,
Temperature -20.0 °C
 592 psi

@Strain 6.86 %,
Temperature -4.00 °F
 TPE; ISO 11403-1 -2
4.10 MPa

@Strain 100.63 %,
Temperature 100 °C
 595 psi

@Strain 100.63 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
4.11 MPa

@Strain 58.83 %,
Temperature 90.0 °C
 596 psi

@Strain 58.83 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
4.15 MPa

@Strain 196.33 %,
Temperature 120 °C
 602 psi

@Strain 196.33 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
4.25 MPa

@Strain 72.06 %,
Temperature 90.0 °C
 616 psi

@Strain 72.06 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
4.27 MPa

@Strain 120.1 %,
Temperature 100 °C
 619 psi

@Strain 120.1 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
4.30 MPa

@Strain 26.8 %,
Temperature 60.0 °C
 624 psi

@Strain 26.8 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
4.39 MPa

@Strain 85.28 %,
Temperature 90.0 °C
 637 psi

@Strain 85.28 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
4.40 MPa

@Strain 133.81 %,
Temperature 100 °C
 638 psi

@Strain 133.81 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
4.53 MPa

@Strain 98.51 %,
Temperature 90.0 °C
 657 psi

@Strain 98.51 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
4.54 MPa

@Strain 14.19 %,
Temperature 0.000 °C
 658 psi

@Strain 14.19 %,
Temperature 32.0 °F
 TPE; ISO 11403-1 -2
4.58 MPa

@Strain 150.4 %,
Temperature 100 °C
 664 psi

@Strain 150.4 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
4.70 MPa

@Strain 36.29 %,
Temperature 60.0 °C
 682 psi

@Strain 36.29 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
4.72 MPa

@Strain 118 %,
Temperature 90.0 °C
 685 psi

@Strain 118 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
4.77 MPa

@Strain 26.81 %,
Temperature 40.0 °C
 692 psi

@Strain 26.81 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
4.85 MPa

@Strain 173.48 %,
Temperature 100 °C
 703 psi

@Strain 173.48 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
4.88 MPa

@Strain 131.23 %,
Temperature 90.0 °C
 708 psi

@Strain 131.23 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
4.93 MPa

@Strain 20.43 %,
Temperature 23.0 °C
 715 psi

@Strain 20.43 %,
Temperature 73.4 °F
 TPE; ISO 11403-1 -2
4.96 MPa

@Strain 45.79 %,
Temperature 60.0 °C
 719 psi

@Strain 45.79 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
5.06 MPa

@Strain 147.24 %,
Temperature 90.0 °C
 734 psi

@Strain 147.24 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2