Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D412 |
Polimeri Europa Europrene® SOL T 6306 Styrene - Butadiene Block Copolymer Europrene® SOL T 6306 is a radial block copolymer obtained by anionic polymerization. The polymer is based on styrene and butadiene, where bound styrene is 37% weight. A non-staining antioxidant .. |
|||
Tensile Strength at Break | <= 29.0 MPa | <= 4210 psi | ISO/R527 |
Polykemi AB POLYfill PP CIM9040 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 29.0 - 38.0 MPa | 4210 - 5510 psi | ASTM D638-03 |
Proto3000 Objet Digital Materials™ DM_8430 Polypropylene-like Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide.. |
|||
Tensile Strength at Break | <= 29.0 MPa | <= 4210 psi | ISO/R527 |
Polykemi AB POLYfill PPH T15040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 29.0 MPa | <= 4210 psi | ISO/R527 |
Polykemi AB POLYfill PPH T15040CR Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D638 |
SABIC PS 330 High Impact Polystyrene for Sheet Extrusion Product Description: High Impact Polystyrene PS 330 is manufactured by continuous mass polymerization of styrene monomer. An elastomer is incorporated during polymerization to achieve impact resis.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics GELOY CR7520 ASA General purpose ASA. Excellent weatherability, good flow/aesthetics and high impact. Rated F2 by UL. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D638 |
Albis Plastics Cellulose Acetate Propionate CP800 (Base Grade), 17% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Propionate (CAP)Characteristics: Strength, Hardness, Stiffness, Weatherability and Dimensional StabilityApplications: Brush Handles, Safety Glasses, Optical Products and .. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp FFL21 PE LNP* Lubricomp* FFL21 is a compound based on Polyethylene resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for t.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics SABIC PPCOMPOUND 19T1020 PP SABIC® PPcompound 19T1020 is a general purpose, talc filled, heat stabilized homopolymer polypropylene compound. This compound exhibits high flow and is suitable for injection molding application.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON AX00756 ABS LNP STAT-KON* AX00756 is a compound based on ABS resin containing Stainless Steel. Added feature of this material is: Electrically Conductive. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® IQ325 PBT (Asia Pacific) PBT resin, using chemically recycled post consumer PET Bottles. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY A3000 ABS (Europe-Africa-Middle East) LNP* Stat-loy* A3000 is a compound based on Acrylonitrile Butadiene Styrene resin. Added features of this material include: Antistat. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON AD000 ABS LNP* STAT-KON* AD000 is a compound based on ABS containing Carbon. Added feature of this grade is: Electrically Conductive. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D638 |
SCG Chemicals EL-Leneâ„¢ H6240B High Density Polyethylene Blow Molding Key Characteristics:Good stiffnessGood environmental stress cracking resistance (ESCR)High compressive and impact strengthGood appearanceOdorlessSafe for food contactGood printabilityRecommended App.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | |
UBE UBEPOL BR15HL HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %) Description: UBEPOL-BR15HL is a linear type of polymer with the high solution viscosity. In case of enlarging the dispersed rubber particle size in |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ISO 527-2 |
Tisan TISOPLEN® 40% Talc Filled Heat Stabilized Homopolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ISO 527-2 |
Tisan TISOPLEN® 20% Talc Filled Heat Stabilized Copolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ISO 527-2/50 |
ExxonMobil Exxtral™ HMT 402 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin with very high stiffness, high heat ageing resistance and detergent resistance designed for electrical applications such as washing ma.. |
|||
Tensile Strength at Break | 29.0 MPa @Temperature 23.0 °C |
4210 psi @Temperature 73.4 °F |
ASTM D638, ISO 527-2 |
DuPont™ Surlyn® 8528 Sodium Ionomer Surlyn® 8528 is a sodium ionomer thermoplastic resin. It is available for use in conventional extrusion and injection equipment, to create various sheets or shapes. Surlyn® 8528 thermoplastic resi.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ISO 527-1/-2 |
DuPont Performance Polymers Hytrel® 4068FG Polyester Elastomer TPC-ET
(Unverified Data**) 40 Shore D High Performance Polyester Elastomer Developed for Food Contact ApplicationsInformation provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ISO R 527 |
Fainplast Compounds MRT 256/G Medical Rigid PVC, Injection Molding Beta and gamma resistant connectors |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D638 |
Azdel SuperLite® SL550800-100 PP Resin Matrix / 55% Glass Fiber (2 mm Molded Thickness) AZDEL SuperLite® SL550800-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ISO R 527 |
Addiplast Addilene J 110 Polypropylene Copolymer UnreinforcedInformation provided by Addiplast. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D638 Die C |
3M Scotch-Weld™ EZ250060 Polyurethane Reactive (PUR) Easy 250 Wood Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive (PUR) Easy 250 Wood Adhesive is 100% solid, warm temperature applied, moisture curing urethanes. This product bonds well to wood and wood bases surfaces as w.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D638 Die C |
3M Scotch-Weld™ TE100 Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as .. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D638 |
3M Dyneon™ THV 815GZ Fluorothermoplastic Granules Dyneon THV 815 GZ provides a balance of low permeation, thermal stability, and melt processability. IT can be used to prepare molded parts and extruded films, tubes, profiles, and wire coatings. It .. |
|||
Tensile Strength at Break | <= 29.0 MPa | <= 4210 psi | ISO/R527 |
Polykemi AB POLYfill PPH DNH15025 GF10 Polypropylene Homopolymer, Flame Retardant, Halogen Free, Glass Fibre-Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 29.0 MPa @Temperature 150 °C |
4210 psi @Temperature 302 °F |
ISO 527-2 |
Solvay Specialty Polymers Amodel® A-1240 L Polyphthalamide (PPA)
(discontinued **) Amodel A-1240 L is a 40% mineral filled polyphthalamide (PPA) that offers low warpage and excellent dimensional stability. This resin also has a high deflection temperature, flexural modulus and ten.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D638 |
Braskem BU004 Blow Molding High Density Polyethylene Containers for lubricating oils, alcohol, cosmetics and yots; Toys.Information provided by Braskem. |