DuPont Performance Polymers Delrin® 500AL NC010 Acetal Homopolymer  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 500AL NC010 Acetal Homopolymer  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Delrin® 500AL is a medium viscosity acetal homopolymer, with an advanced system of lubrication for applications requiring low wear and/or coefficient of friction against steel, itself or other plastics.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.39 g/cc
1.39 g/cc
ASTM D792
Density 1.39 g/cc
0.0502 lb/in³
ISO 1183
Linear Mold Shrinkage 0.017 - 0.020 cm/cm

@Thickness 3.20 mm
 0.017 - 0.020 in/in

@Thickness 0.126 in
 Flow, 24h; ASTM D955
0.017 - 0.020 cm/cm

@Thickness 3.20 mm
 0.017 - 0.020 in/in

@Thickness 0.126 in
 Transverse, 24h; ASTM D955
Linear Mold Shrinkage, Flow 0.018 cm/cm

@Thickness 2.00 mm
 0.018 in/in

@Thickness 0.0787 in
 ISO 294-4
0.019 cm/cm

@Thickness 4.00 mm
 0.019 in/in

@Thickness 0.157 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.017 cm/cm

@Thickness 2.00 mm
 0.017 in/in

@Thickness 0.0787 in
 ISO 294-4
0.019 cm/cm

@Thickness 4.00 mm
 0.019 in/in

@Thickness 0.157 in
 ISO 294-4
Melt Flow 6.0 g/10 min

@Load 1.05 kg,
Temperature 190 °C
 6.0 g/10 min

@Load 2.31 lb,
Temperature 374 °F
 ASTM D1238
14 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 14 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Melt Index of Compound 12 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 12 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength 66.0 MPa

@Temperature 23.0 °C
 9570 psi

@Temperature 73.4 °F
 5mm/min (0.2in/min); ASTM D638
Tensile Strength, Yield 65.0 MPa

@Temperature 23.0 °C
 9430 psi

@Temperature 73.4 °F
 ISO 527
66.0 MPa

@Temperature 23.0 °C
 9570 psi

@Temperature 73.4 °F
 5mm/min (0.2in/min); ASTM D638
Elongation at Break 23 %

@Temperature 23.0 °C
 23 %

@Temperature 73.4 °F
 nominal; ISO 527
30 %

@Temperature 23.0 °C
 30 %

@Temperature 73.4 °F
 5mm/min (0.2in/min); ASTM D638
35 %

@Temperature 23.0 °C
 35 %

@Temperature 73.4 °F
 50mm/min; ISO 527
Elongation at Yield 10 %

@Temperature 23.0 °C
 10 %

@Temperature 73.4 °F
 5mm/min (0.2in/min); ASTM D638
11 %

@Temperature 23.0 °C
 11 %

@Temperature 73.4 °F
 ISO 527
Tensile Modulus 3.00 GPa

@Temperature 23.0 °C
 435 ksi

@Temperature 73.4 °F
 ISO 527
3.17 GPa

@Temperature 23.0 °C
 460 ksi

@Temperature 73.4 °F
 5mm/min (0.2in/min); ASTM D638
Flexural Strength 88.0 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 12800 psi

@Strain 5.00 %,
Temperature 73.4 °F
 ASTM D790
Flexural Modulus 2.80 GPa

@Temperature 23.0 °C
 406 ksi

@Temperature 73.4 °F
 ISO 178
2.97 GPa

@Temperature 23.0 °C
 431 ksi

@Temperature 73.4 °F
 ASTM D790
Izod Impact, Notched 0.580 J/cm

@Temperature 23.0 °C
 1.09 ft-lb/in

@Temperature 73.4 °F
 ASTM D256
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -40.0 °C
 2.38 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1A
6.00 kJ/m²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A
Charpy Impact Unnotched 13.0 J/cm²

@Temperature -30.0 °C
 61.9 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
16.0 J/cm²

@Temperature 23.0 °C
 76.1 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
0.700 J/cm²

@Temperature 23.0 °C
 3.33 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Tensile Creep Modulus, 1 hour 2400 MPa

@Temperature 23.0 °C
 348000 psi

@Temperature 73.4 °F
 ISO 899
Tensile Creep Modulus, 1000 hours 1600 MPa

@Temperature 23.0 °C
 232000 psi

@Temperature 73.4 °F
 ISO 899
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature 23.0 - 55.0 °C
 278 µin/in-°F

@Temperature 73.4 - 131 °F
 ASTM E 831
500 µm/m-°C

@Temperature -40.0 - 23.0 °C
 278 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
500 µm/m-°C

@Temperature 23.0 - 55.0 °C
 278 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
500 µm/m-°C

@Temperature 55.0 - 100 °C
 278 µin/in-°F

@Temperature 131 - 212 °F
 ISO 11359-1/-2
CTE, linear, Transverse to Flow 100 µm/m-°C

@Temperature -40.0 - 23.0 °C
 55.6 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
116 µm/m-°C

@Temperature 23.0 - 55.0 °C
 64.4 µin/in-°F

@Temperature 73.4 - 131 °F
 ASTM E 831
120 µm/m-°C

@Temperature 23.0 - 55.0 °C
 66.7 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
170 µm/m-°C

@Temperature 55.0 - 100 °C
 94.4 µin/in-°F

@Temperature 131 - 212 °F
 ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
178 °C
352 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
ISO 75-1/-2
169 °C
336 °F
Not Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 97.0 °C
207 °F
ISO 75-1/-2
108 °C
226 °F
Not Annealed; ASTM D648
UL RTI, Electrical 50.0 °C

@Thickness 0.750 mm
 122 °F

@Thickness 0.0295 in
 UL 746B
110 °C

@Thickness 1.50 mm
 230 °F

@Thickness 0.0591 in
 UL 746B
110 °C

@Thickness 3.00 mm
 230 °F

@Thickness 0.118 in
 UL 746B
UL RTI, Mechanical with Impact 50.0 °C

@Thickness 0.750 mm
 122 °F

@Thickness 0.0295 in
 UL 746B
85.0 °C

@Thickness 1.50 mm
 185 °F

@Thickness 0.0591 in
 UL 746B
90.0 °C

@Thickness 3.00 mm
 194 °F

@Thickness 0.118 in
 UL 746B
UL RTI, Mechanical without Impact 50.0 °C

@Thickness 0.750 mm
 122 °F

@Thickness 0.0295 in
 UL 746B
90.0 °C

@Thickness 1.50 mm
 194 °F

@Thickness 0.0591 in
 UL 746B
95.0 °C

@Thickness 3.00 mm
 203 °F

@Thickness 0.118 in
 UL 746B
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 7.00e+14 ohm-cm

@Temperature 23.0 °C
 7.00e+14 ohm-cm

@Temperature 73.4 °F
 ASTM D257
Surface Resistance 4.00e+15 ohm

@Temperature 23.0 °C
 4.00e+15 ohm

@Temperature 73.4 °F
 ASTM D257
Dielectric Constant 3.6

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 3.6

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 ASTM D150
Dielectric Strength 17.7 kV/mm

@Thickness 3.20 mm,
Temperature 23.0 °C
 450 kV/in

@Thickness 0.126 in,
Temperature 73.4 °F
 Short Time; ASTM D149
Dissipation Factor 0.0060

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 0.0060

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 ASTM D150
Comparative Tracking Index 600 V

@Thickness 3.00 mm,
Temperature 23.0 °C
 600 V

@Thickness 0.118 in,
Temperature 73.4 °F
 UL 746A