Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 164 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
ASTM D648
Network Polymers Kepital® F20-25
Description: Natural Acetal Copolymer, 25% Glass Reinforced GradeInformation provided by Network Polymers Inc.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
ASTM D648
Polymer Resources AH-GP1-[color]-H Acetal Homopolymer, Low Flow, High Melt Strength, Heat Stabilized
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics Lexan® XHT3141 PC Copolymer (Asia Pacific)
XHT3141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics Lexan® XHT3141 PC Copolymer (Europe-Africa-Middle East)
XHT3141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics Lexan® EXRL0627 PC Copolymer
EXRL0627 is a high flow, UV stabilized, high heat polycarbonate copolymer. It is available in a range of opaque and transparent colors.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
ISO 75-1/-2
DuPont Performance Polymers Delrin® 500AL NC010 Acetal Homopolymer  (Unverified Data**)
Delrin® 500AL is a medium viscosity acetal homopolymer, with an advanced system of lubrication for applications requiring low wear and/or coefficient of friction against steel, itself or other plas..
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
ISO 75-1/-2
DuPont Performance Polymers Delrin® FG500AL NC010 Acetal Homopolymer  (Unverified Data**)
Delrin® FG500AL is a medium viscosity acetal homopolymer, lubricated for low wear and /or coefficient of friction. It has been developed for consideration into applications such as parts for the fo..
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
ASTM D648
Kolon KOCETAL® CF702 Conductive Grade Acetal Resin
Carbon fiber added, high stiffness and conductive grade. Applications: Conductive products. Information provided by API-Kolon.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP Lubricomp RL001 PA 66
LNP Lubricomp* RL001 is a Nylon 6/6 base resin containing PTFE lubricant. Characteristics are internally lubricated.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics ULTEM STM1700 PEI Copolymer
Siltem STM1700 is a flexible copolymer designed for wire and cable applications. It offers a halogen free (according VDE 0472) flame retardant solution that also offers low smoke emission and toxici..
Deflection Temperature at 0.46 MPa (66 psi) 164 °C

@Thickness 3.20 mm
327 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP KF002 Acetal Copolymer
LNP THERMOCOMP* KF002 is a compound based on Acetal Copolymer resin containing 10% Glass Fiber.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP VERTON MV008S PP
LNP VERTON* MV008S is a compound based on Polypropylene resin containing 40% Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, Structural.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP VERTON MV008S PP (Europe-Africa-Middle East)
LNP VERTON* MV008S is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled, Heat Stabilized.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP VERTON MV008SU PP
LNP VERTON* MV008SU is a compound based on Polypropylene resin containing 40% Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, UV Stabilized, Structur..
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP VERTON MV008SU PP (Asia Pacific)
LNP VERTON* MV008SU is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics ULTEM STM1700 PEI Copolymer (Europe-Africa-Middle East)
Siltem STM1700 is a flexible copolymer designed for wire and cable applications. It offers a halogen free (according VDE 0472) flame retardant solution that also offers low smoke emission and toxici..
Deflection Temperature at 0.46 MPa (66 psi) 164 °C

@Thickness 3.20 mm
327 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP KF002XXP Acetal Copoly
LNP* Thermocomp* KF002XXP is a compound based on Acetal Copolymer resin containing 10% Glass Fiber. Added features of this material include: Chemically Coupled.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP VERTON MV00ASXP PP (Europe-Africa-Middle East)
LNP VERTON* MV00AS is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP Verton MV00CS PP (Europe-Africa-Middle East)
LNP* VERTON* MV00CS is a compound based on PP resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C

@Thickness 3.17 mm
327 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Chase Plastics CP Pryme® AC125G Acetal Copolymer, 25% Glass Fiber Reinforced
Information provided by Chase Plastics.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
ISO 75-1/-2
DuPont Performance Polymers Delrin® FG500AL NC010 Acetal (POM)  (Unverified Data**)
Lubricated Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction Developed for Food Contact Applications Delrin FG500AL is a medium viscosity acetal homopolymer lubricated for low wear ..
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80x10x4, sp=64 mm; ISO 75/Bf
Eurostar Starflam PX06012 PA6, Flame Retardant, Injection Molded
Starflam PX06012 is an Unfilled, Halogen Free and Red Phosphorous Free, Flame Retardant, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
ASTM D648
Ashley Polymers Ashlene® 981S Nylon 612
A general purpose heat stabilized 612 Nylon for extrusion. These resins are noted for their low moisture absorption and excellent dimensional stability.Data provided by the manufacturer
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
ASTM D648
A. Schulman ComAlloy Hiloy® 102 Polypropylene, Glass Reinforced
Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
ASTM D648
A. Schulman ComAlloy Hiloy® 123 Polypropylene, Glass Reinforced, Chemically Coupled, UL
Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
328 °F
ASTM D648
Aaron Industries AAROPRENE® GFIPP 2040 High Impact Glass Filled Polypropylene
AAROPRENE® GFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified.
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
ASTM D648
A. Schulman ComAlloy Aqualoy® 150 Polypropylene, Glass Reinforced, Chemically Coupled NSF
Data provided by the manufacturer, ComAlloy International Company.50% Glass Reinforced. In Aqualoy® materials, carefully selected base resins and proprietary additives meld hydrolytic stability an..
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
ASTM D648
Cheng Yu Plastic FV30G20 POM, 20% Glass Fiber
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
ISO 75-1/-2
DuPont Performance Polymers Delrin® 577 BK000 Acetal Homopolymer  (Unverified Data**)
Delrin® 577 BK000 is a medium viscosity acetal homopolymer containing 20% glass fiber filler, with high stiffness, low warpage and low creep for superior performance at elevated temperature. It con..
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP THERMOCOMP KF006 POM (Europe-Africa-Middle East)
LNP* THERMOCOMP* KF006 is a compound based on Acetal Copolymer resin containing Glass Fiber