3M Scotch-Weld™ DP110 Translucent Epoxy Adhesive

Category Polymer , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ DP110 Translucent Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M
Physical Properties Metric English Comments
Viscosity 30000 - 70000 cP
30000 - 70000 cP
Base
30000 - 70000 cP
30000 - 70000 cP
Accelerator
Mechanical Properties Metric English Comments
Hardness, Shore D 40
40
Elongation at Break 40 %
40 %
Shear Strength 0.276 - 0.414 MPa
40.0 - 60.0 psi
Overlap, Neoprene Rubber/Steel
0.552 - 0.689 MPa
80.0 - 100 psi
Overlap, SBR/Steel
1.03 MPa
150 psi
Overlap, Abraded Aluminum, 14 days in 5% salt spray @ 35°C
1.72 MPa
250 psi
Overlap, Acrylic/Acrylic
2.76 MPa
400 psi
Overlap, PVC/PVC, Rigid
3.45 MPa
500 psi
Overlap, ABS/ABS Plastic
3.45 MPa
500 psi
Overlap. PC/PC
3.45 MPa
500 psi
Overlap, Etched Aluminum, 14 days in 5% salt spray @ 35°C
4.83 MPa
700 psi
Overlap, Abraded Aluminum, 3 days, 71°C, 100% RH
6.89 MPa
1000 psi
Overlap, Al/Al
6.89 MPa
1000 psi
Overlap, Abraded Aluminum, Initial
8.27 MPa
1200 psi
Overlap, Etched Aluminum, 3 days, 71°C, 100% RH
8.62 MPa
1250 psi
Overlap, Abraded Aluminum, 30 days tap water @ RT
9.65 MPa
1400 psi
Overlap, Fiber Reinforced Polyester/Fiber Reinforced Polyester
10.3 MPa
1500 psi
Overlap, CRS/CRS
10.3 MPa
1500 psi
Overlap, Stainless Steel/Stainless Steel
10.3 MPa
1500 psi
Overlap, Galvanized Steel/Galvanized Steel
10.3 MPa
1500 psi
Overlap, Copper/Copper
10.3 MPa
1500 psi
Overlap, Brass/Brash
15.9 MPa
2300 psi
Overlap, Etched Aluminum, 30 days tap water @ RT
17.2 MPa
2500 psi
Overlap, Etched Aluminum, Initial
1.38 MPa

@Temperature 82.0 °C
200 psi

@Temperature 180 °F
Overlap
1.86 MPa

@Temperature 71.0 °C
270 psi

@Temperature 160 °F
Overlap
17.2 MPa

@Temperature -55.0 °C
2500 psi

@Temperature -67.0 °F
Overlap
17.2 MPa

@Temperature 24.0 °C
2500 psi

@Temperature 75.2 °F
Overlap
Peel Strength 3.51 kN/m
20.0 pli
T-Peel
Thermal Properties Metric English Comments
CTE, linear 80.0 µm/m-°C

@Temperature -50.0 - 0.000 °C
44.4 µin/in-°F

@Temperature -58.0 - 32.0 °F
200 µm/m-°C

@Temperature -50.0 - 110 °C
111 µin/in-°F

@Temperature -58.0 - 230 °F
Thermal Conductivity 0.183 W/m-K

@Temperature 45.0 °C
1.27 BTU-in/hr-ft²-°F

@Temperature 113 °F
Glass Transition Temp, Tg 13.0 °C
55.4 °F
Electrical Properties Metric English Comments
Volume Resistivity 4.50e+10 ohm-cm
4.50e+10 ohm-cm
Dielectric Strength 20.5 kV/mm
520 kV/in
Descriptive Properties Value Comments
Appearance Light Yellow
Accelerator
Translucent White
Base
Yellow Translucent