SABIC Innovative Plastics LNP Lubricomp GFL14 PSU

Category Polymer , Thermoplastic , Polysulfone (PSU)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp GFL14 PSU.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* GFL14 is a compound based on Polysulfone containing Glass Fiber and PTFE Lubricant.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
ISO 1183
1.44 g/cc
0.0520 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.29 %
0.29 %
23°C / 50% RH; ISO 62
0.18 %

@Time 86400 sec
0.18 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Time 86400 sec
0.0040 - 0.0060 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
Type I, 5 mm/min; ASTM D 638
95.0 MPa
13800 psi
5 mm/min; ISO 527
Tensile Strength, Yield 98.0 MPa
14200 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 2.2 %
2.2 %
5 mm/min; ISO 527
2.3 %
2.3 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 6.82 GPa
989 ksi
1 mm/min; ISO 527
6.91 GPa
1000 ksi
50 mm/min; ASTM D 638
Flexural Strength 146 MPa
21200 psi
ISO 178
151 MPa
21900 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 6.20 GPa
899 ksi
2 mm/min; ISO 178
6.60 GPa
957 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.720 J/cm

@Temperature 23.0 °C
1.35 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 5.05 J/cm

@Temperature 23.0 °C
9.46 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
14.0 J

@Temperature 23.0 °C
10.3 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Coefficient of Friction, Dynamic 0.48
0.48
ASTM D 3702 Modified
Coefficient of Friction, Static 0.62
0.62
ASTM D 3702 Modified
K (wear) Factor 46.3 x 10-8 mm³/N-M
23.0 x 10-10 in³-min/ft-lb-hr
Ring; ASTM D 3702 Modified
266 x 10-8 mm³/N-M
132 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.3 µm/m-°C

@Temperature -30.0 - 30.0 °C
16.8 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D 696
CTE, linear, Transverse to Flow 46.3 µm/m-°C

@Temperature -30.0 - 30.0 °C
25.7 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 185 °C
365 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
185 °C

@Thickness 3.20 mm
365 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 180 °C
356 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
181 °C

@Thickness 3.20 mm
358 °F

@Thickness 0.126 in
unannealed; ASTM D 648