- RheTech Products M40P100-01 40% Mica Reinforced Polypropylene, Black
RheTech Products M40P100-01 40% Mica Reinforced Polypropylene, Black
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Mica Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products M40P100-01 40% Mica Reinforced Polypropylene, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Structural componentsAir ducts and dampenersFunctional supportsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 40 % | 40 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 230 °C |
14 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 73 | 73 | ASTM D2240 |
| Tensile Strength at Break | 26.9 MPa | 3900 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 4.93 GPa | 715 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Temperature 23.0 °C |
0.500 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 0.565 J | 0.417 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 269 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Middle Barrel Temperature | 216 - 243 °C | 420 - 470 °F | |
| Front Barrel Temperature | 221 - 249 °C | 430 - 480 °F | |
| Nozzle Temperature | 227 - 238 °C | 440 - 460 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Packaging PK8-1080 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Ovation Polymers OpteSTAT™ NC TPU 9020 Polyurethane-based Carbon Nanotube Compound
- LATI Larpeek 10 G/60 PEEK, 60% Glass Fiber Reinforced
- Techmer ES HiFill FR® PA6 GF33 FR HS L 33% Glass Filled (Conditioned)
- Ashley Polymers Ashlene® 261WO PPO
- 3M 856 General Purpose Polyester Tape
- 3M Scotch-Weld™ DP420 LH Epoxy Adhesive
- A. Schulman ComAlloy Lubrilon® 606 Nylon 6/6, PTFE Filled, Flow Enhanced
- Gouda Vuurvast CURON 185 T Dense Refractory Castable
Copyright © lookpolymers.com All Rights Reserved