LG Chemical LUPOL GP3300 PP+MF30%
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | LG Chemical |
| Trade Name | LUPOL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOL GP3300 PP+MF30%.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PP+MF30%, General PurposeApplication: Electrical & Electronic, Automotive PartsCAS: 9003-07-0 and 14807-96-6Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.012 cm/cm @Thickness 3.20 mm |
0.0070 - 0.012 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.3 MPa @Thickness 3.20 mm |
4980 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 20 % @Thickness 3.20 mm |
20 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 54.9 MPa @Thickness 6.40 mm |
7970 psi @Thickness 0.252 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 3.43 GPa @Thickness 6.40 mm |
498 ksi @Thickness 0.252 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.294 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
>= 0.551 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 65.0 °C @Thickness >=1.50 mm |
149 °F @Thickness >=0.0591 in |
|
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness >=1.50 mm |
149 °F @Thickness >=0.0591 in |
|
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness >=1.50 mm |
149 °F @Thickness >=0.0591 in |
|
| Flammability, UL94 | HB @Thickness >=1.50 mm |
HB @Thickness >=0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Middle Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Front Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Nozzle Temperature | 210 - 230 °C | 410 - 446 °F | Injection Molding |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- M Chemical GUARD DOGâ„¢ UV5411 Benzotriazole UV Absorber, Powder and LD Pellet
- Materion Beryllium Copper Alloy M25 Rod and Bar; H (TD04) Temper; over 25.4 to 76 mm (UNS C17300)
- Styron CALIBREâ„¢ 201-15 Polycarbonate Resin
- A. Schulman SCHULADUR® B GF30 30% Glass Fiber Reinforced PET
- Borealis Borpeel™ WD255CF PO Compound for Non Sterilizable Peelable Film Applications
- CIMBAR BARA 200 Barium Sulfate (BaSO4)
- Techmer ES Luriblend® HTN 01400 BK
- American Elements Cobalt Iron Nanopowder
Copyright © lookpolymers.com All Rights Reserved