Cossa Polimeri ESTACARB 1560 V0 Flame Retardant Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTACARB |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTACARB 1560 V0 Flame Retardant Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant class V0, antimony and PBDE free, opaque, high melt flow, high impact strength, high thermal resistanceInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 15 g/10 min @Load 1.20 kg, Temperature 300 °C |
15 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ASTM D 638 |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM D 638 |
| Elongation at Break | >= 50 % | >= 50 % | ASTM D 638 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ASTM D 790 |
| Izod Impact, Notched | 5.00 J/cm @Temperature 0.000 °C |
9.37 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
| 5.50 J/cm @Temperature 23.0 °C |
10.3 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 135 °C | 275 °F | I.E.C. 335-1 |
| Vicat Softening Point | 145 °C @Load 5.00 kg |
293 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| 148 °C @Load 0.999 kg |
298 °F @Load 2.20 lb |
50°C/hr; ASTM D 1525 | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Glow Wire Test | 960 °C | 1760 °F | I.E.C. 695-2-1 |
Users viewing this material also viewed the following:
- Indium Corp. Indalloy 78 Bismuth-Lead-Tin Solder Alloy
- Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F)
- DuPont™ Fusabond® E100 Polymer Modifier
- Eurotec® Tecomid® NA40 NL IM PA6.6, impact modified, natural
- Abatron AboWeld 8708-8 One-Component Structural/Dielectric Epoxy
- Ametek AM 388™ Alloy (UNS C72650) TS03
- Adamas Adalon® 503 PTFE, 0.1% MoS2
- Covestro Apec® 1805 Polycarbonate (discontinued **)
- Fainplast Compounds AP 90/2 Flexible PVC, Flame Retardant Insulation
Copyright © lookpolymers.com All Rights Reserved