RheTech Products HP513-00A High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products HP513-00A High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Interior trimI/P componentsCenter consolesInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 0.00 % | 0.00 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0145 cm/cm | 0.0145 in/in | ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength at Break | 25.2 MPa | 3650 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.03 GPa | 150 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 1.39 J/cm @Temperature 23.0 °C |
2.60 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 22.6 J | 16.7 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.6 °C | 123 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 188 - 216 °C | 370 - 420 °F | |
| Middle Barrel Temperature | 193 - 221 °C | 380 - 430 °F | |
| Front Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Nozzle Temperature | 204 - 216 °C | 400 - 420 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- PolyOne Versaflex™ HC MT224 Thermoplastic Elastomer (TPE)
- Park Electrochemical Nelcote® E-765 Epoxy Prepreg, T300 6K 5HS Reinforced
- Fainplast Compounds RI 52 Rigid PVC, Injection Molding
- Fiberfil® M-2500 BK Nylon 6, 15% Glass Reinforced, 25% mineral Filled, post industrial
- Samsung Cheil Industries Starex® GR-4020L ABS, Glass Filled
- Cossa Polimeri ESTAPROP 1540 TG V0 H Flame Retardant Polypropylene, 20% Mineral Filled
- 3M Scotchcal™ 50-79 Graphic Film
- Resinlab® RC8009 Anaerobic Retaining Compound
- Henkel Hysol EA 9825 Paste Adhesive System
Copyright © lookpolymers.com All Rights Reserved