Category	Polymer , Thermoplastic , Nylon , Polypropylene (PP)
Manufacturer	Multibase
Trade Name	Nylex™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Multibase Nylex™ 2185 R15 Polyamide + PP.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Glass fiber reinforcement, 15% Filler by Weight. Features: Crack Resistance, GoodDimensional Stability, GoodImpact Resistance, GoodMoisture ResistantProcessability, GoodForms:PelletsProcessing Methods:Injection MoldingUses: Electrical PartsHousing, Electrical Safety EquipmentInformation provided by Multibase

Physical Properties	Metric	English	Comments
Specific Gravity	1.06 g/cc	1.06 g/cc	ASTM 792
Water Absorption	0.65 %	0.65 %	ASTM D570
Linear Mold Shrinkage	0.012 cm/cm	0.012 in/in	ASTM D955
Melt Flow	2.25 g/10 min	2.25 g/10 min	Cond. Q; ASTM D1238
	3.9 g/10 min @Load 2.16 kg, Temperature 230 °C	3.9 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	30.4 MPa	4410 psi	ASTM D638
Elongation at Break	20 %	20 %	ASTM D638
Flexural Strength	33.2 MPa	4820 psi	ASTM D790
Flexural Modulus	1.84 GPa	267 ksi	Tangent; ASTM D790
Izod Impact, Notched	2.03 J/cm	3.80 ft-lb/in	73°F; ASTM D256
Gardner Impact	9.717 J	7.167 ft-lb	ASTM D3029

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	132 °C	270 °F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	86.1 °C	187 °F	Unannealed; ASTM D648

Processing Properties	Metric	English
Rear Barrel Temperature	205 °C	401 °F
Middle Barrel Temperature	208 °C	406 °F
Front Barrel Temperature	213 °C	415 °F
Nozzle Temperature	213 °C	415 °F
Mold Temperature	13.0 - 47.8 °C	55.4 - 118 °F
Injection Pressure	2.41 - 8.27 MPa	350 - 1200 psi
Back Pressure	0.345 - 1.03 MPa	50.0 - 150 psi

Descriptive Properties	Value	Comments
Injection Rate	Moderate-Fast