RheTech Products CC20P100-01 20% Calcium Carbonate Reinforced Polypropylene, Black
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products CC20P100-01 20% Calcium Carbonate Reinforced Polypropylene, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: ElectronicsConsumer GoodsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 20 % | 20 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 230 °C |
19 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 72 | 72 | ASTM D2240 |
| Tensile Strength at Break | 28.3 MPa | 4100 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.65 GPa | 240 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Temperature 23.0 °C |
0.500 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 6.78 J | 5.00 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C | 225 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Middle Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Front Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Nozzle Temperature | 216 - 227 °C | 420 - 440 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Nye Lubricants NYOSIL-M25UV Oil
- NIZHNEKAMSKNEFTEKHIM PE 2062x (62135) High Density Polyethylene
- SABIC Innovative Plastics PC1000R PC (Europe-Africa-Middle East)
- Techmer ES HiFill® PA6 GF33 L UV BK 33% Glass Filled
- Polyram RamSter RF350M3 PBT, 15% Mineral Filled
- Fainplast Compounds CL 87/T Flexible PVC, Sheathing
- Arlon LW201Xxx-P0 0.020" (0.508 mm) Self-Fusing Silicone Tape (Triangular, Unsupported) with Poly Interleave
- Asahi Kasei Thermofil P-20CC-0734A 20% Calcium Carbonate Reinforced
- Henkel Hysol EA 960F Paste Adhesive System
Copyright © lookpolymers.com All Rights Reserved