Asahi Kasei Leona® 90G50 50% Glass Filled Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | Asahi Kasei |
| Trade Name | Leona® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Leona® 90G50 50% Glass Filled Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Enhanced strength and stiffness; with 50% GF. Excellent appearance.Applications:Office furnitureInformation provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | Dry; ASTM D792 |
| Water Absorption | 1.1 % | 1.1 % | Wet |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | Dry; ASTM D2863 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 90 | 90 | Dry; ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | Dry; ASTM D785 |
| Tensile Strength, Yield | 196 MPa | 28400 psi | Wet; ASTM D638 |
| 235 MPa | 34100 psi | Dry; ASTM D638 | |
| Elongation at Break | 2.5 % | 2.5 % | Dry; ASTM D638 |
| 3.0 % | 3.0 % | Wet; ASTM D638 | |
| Flexural Strength | 304 MPa | 44100 psi | Wet; ASTM D790 |
| 373 MPa | 54100 psi | Dry; ASTM D790 | |
| Flexural Modulus | 12.1 GPa | 1750 ksi | Wet; ASTM D790 |
| 15.5 GPa | 2250 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 1.27 J/cm | 2.38 ft-lb/in | Dry; ASTM D256 |
| 1.33 J/cm | 2.49 ft-lb/in | Wet; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C |
11.1 µin/in-°F @Temperature 68.0 °F |
Dry; ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | Dry; ASTM D648 |
| Flammability, UL94 | HB | HB | Dry |
Users viewing this material also viewed the following:
- Omnia Plastica PE 500 - Polyethylene 500
- Iran Petrochemical (PCC) X 30 S Polypropylene Film
- SABIC Innovative Plastics LNP LUBRICOMP OCL36XXP PPS - Linear (Europe-Africa-Middle East)
- STAR Thermoplastic Alloys & Rubbers StarTUFF TF 55-HR-9 TPE
- SMAC CABLE® 2514S-10-10 Damping Material
- Zylog Hipolyene® 7151 M1 HF Thermoplastic Polyolefin & PP Compound
- Elastocon TPE Technologies Elastocon® CLR40 Thermoplastic Elastomer
- Arlon 55578XC028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Bhansali Engineering Abstron HR-59 ABS Heat Resistant
- Premix Premi-Glas® 1281-32 VE Glass Reinforced Vinyl Ester SMC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved