ExxonMobil Bicor™ 15MB440 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor™ 15MB440 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor 15MB440 is a biaxially oriented transparent polypropylene film designed to be the outside web of a laminate.Availability: Arica & Middle East, Asia Pacific, Europe, Latin America, North America and South AmericaKey Features:Very good sealability of the untreated surface with a wide range of polyethylene for lap seal applicationsExcellent jaw releaseOutstanding optical properties, stable in time. Features:In Lamination Lap SealableLap Sealable to PEApplications:BakeryBiscuits/Cookie/Crackers Fresh ProduceFrozen FoodHealth and Beauty CareHousehold and DetergentsIce Cream Pet FoodUses:Pre-made Bags – Flexible Packaging VFFS Flexible PackagingProcessing Method: Outer Web Adhesive Lamination, Outer Web Extrusion Lamination, Solvent Flexographic Printing and Solvent Rotogravure PrintingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 1.40 g/m²/day @Temperature 23.0 °C |
0.0900 g/100 in²/day @Temperature 73.4 °F |
85% RH; ExxonMobil Method |
| 6.98 g/m²/day @Temperature 38.0 °C |
0.450 g/100 in²/day @Temperature 100 °F |
90% RH; ExxonMobil Method | |
| Thickness | 15.0 microns | 0.590 mil | ExxonMobil Method |
| Coating Weight | 13.4 g/m² | 8.40 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 160 % | 160 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 40 % | 40 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 1.80 GPa | 261 ksi | MD; ExxonMobil Method |
| 3.50 GPa | 508 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.40 | 0.40 | Untreated Surface; ExxonMobil Method |
| Seal Strength | 510 g/25 mm @Pressure 0.276 MPa, Temperature 140 °C |
510 g/in @Pressure 40.0 psi, Temperature 284 °F |
Otto Bruger, 0.2 sec; ExxonMobl Method |
| 510 g/25 mm @Pressure 0.276 MPa, Temperature 140 °C |
510 g/in @Pressure 40.0 psi, Temperature 284 °F |
Otto Bruger, 0.2 sec; ExxonMobl Method | |
| Film Tensile Strength at Break, MD | 130 MPa | 18900 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 285 MPa | 41300 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 5.0 % @Temperature 135 °C |
5.0 % @Temperature 275 °F |
ExxonMobil Method |
| Shrinkage, TD | 5.0 % @Temperature 135 °C |
5.0 % @Temperature 275 °F |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.0 % | 2.0 % | ExxonMobil Method |
| Gloss | 85 % | 85 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Seal Range | 15°C | UT/LLDPE, 36.3 psi (0.25 MPa), 0.2 sec |
| 25°C | UT/LLDPE, 36.3 psi (0.25 MPa), 0.2 sec | |
| Yield | 51500 in2/lb |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 7727 BLK
- SABIC Innovative Plastics LNP Lubricomp CI001 PS
- Huntsman AroCy B-10 Monomeric Bisphenol-A Dicyanate
- Lanxess Durethan® BKV 115 H3.0 000000 Nylon 6-Copolymer, Glass Fiber Reinforced
- Lanxess Durethan® BKV 30 N1 000000 Nylon 6, 30% Glass Fiber
- Schott D 263 Thin Borosilicate Glass
- Techmer ES HiFill® HDPE E GF15 15% Glass Filled
- Dow Corning 3-0135 Cosmetic Fluid
Copyright © lookpolymers.com All Rights Reserved