Polymer Property : Flexural Modulus = 1.65 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	1.65 GPa	240 ksi	Tangent; ASTM D790
RheTech Products T10P250-00 10% Talc Reinforced Polypropylene Copolymer, Natural Applications: Fan shroudsCenter consolesAir ductsInjection molding conditions reported in table.Information provided by RheTech Products.
Flexural Modulus	1.65 GPa	239 ksi	ASTM D790
NatureWorks® Ingeo™ AW 240D Biopolymer for Food Serviceware NatureWorks® PLA polymer AW 240D is a thermoplastic resin derived from annually renewable resources. PLA polymer 2003D processes easily on conventional extrusion equipment. Specifically designed ..
Flexural Modulus	1.65 GPa @Thickness 3.20 mm	240 ksi @Thickness 0.126 in	At 1.27 mm/min, 1% secant, injection molded ASTM Type 1 specimen; ASTM D790A
Pinnacle Polymers 1220 Polypropylene Homopolymer, Injection Molding Grade This Pinnacle Polymers Polypropylene is made via UNIPOL™ PP technology, which utilizes gas-phase fluidized bed reactors with a high activity catalyst system to ensure uniform physical properties an..
Flexural Modulus	1.65 GPa @Thickness 3.20 mm	240 ksi @Thickness 0.126 in	At 1.27 mm/min, 1% secant, injection molded ASTM Type 1 specimen; ASTM D790A
Pinnacle Polymers 1517 Polypropylene Homopolymer, Fiber Spinning Grade This Pinnacle Polymers Polypropylene is made via UNIPOL™ PP technology, which utilizes gas-phase fluidized bed reactors with a high activity catalyst system to ensure uniform physical properties an..
Flexural Modulus	1.65 GPa	239 ksi	80x10x4 mm specimen, 2 mm/min; ISO 178
Solvay Engineered Polymers SEQUEL® 1402 TPO  (discontinued **) Description: SEQUEL® 1402 engineered polyolefin material is designed for large automotive exterior applications that require high melt flow, excellent paintability, and processability. Applications..
Flexural Modulus	1.65 GPa	239 ksi	1% secant; ASTM D790A
Reliance Industries Repol H030SG Polypropylene REPOL Polypropylene H030SG is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly..
Flexural Modulus	1.65 GPa	239 ksi	1% secant; ASTM D790A
Reliance Industries Repol H200MA Polypropylene REPOL Polypropylene H200MA is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly..
Flexural Modulus	1.65 GPa	239 ksi	1% secant; ASTM D790A
Reliance Industries Repol H250FG Polypropylene REPOL Polypropylene H250FG is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly..
Flexural Modulus	1.65 GPa	240 ksi	ASTM D790
Ravago Manufacturing Americas Hysun™ 383 ASA  (discontinued **) Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Rava..
Flexural Modulus	1.65 GPa	240 ksi	ASTM D790
Global CPP-110 10% CaC03 Filled Polypropylene Information provided by Global Polymers Corporation.
Flexural Modulus	1.65 GPa	239 ksi
KratonÂ® FG1901 + PBT blend (30/70) Blending KRATON FG polymers with PBT significantly improves the toughness. KRATON polymers are block segments of styrene and rubber monomers (A-B, A-B-A, or [A-B]n). The KRATON G series are second ..
Flexural Modulus	1.65 GPa	239 ksi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics XenoyÂ® X6800BM PBT Blow moldable, impact modifed XENOYThis data was supplied by SABIC-IP for the Americas region.
Flexural Modulus	1.65 GPa	239 ksi	ISO 178
Borealis HC110BF Polypropylene Homopolymer HC110BF is a polypropylene homopolymer intended for injection molding and extrusion. Applications: HC110BF has been developed especially for applications like: co-extrusion applications, print lami..
Flexural Modulus	1.65 GPa	239 ksi	2mm/min; ISO 178
Borealis HC207TF Polypropylene Homopolymer HC207TF is a special nucleated polypropylene homopolymer intended for thermoforming packaging. Applications: HC207TF is recommended for in-line and off line thermoforming, high transparent trays, c..
Flexural Modulus	1.65 GPa	240 ksi	ASTM D790
A. Schulman POLYFORT™ FPP 2067HU UV Stabilized, High Heat Resistant Impact Polypropylene DescriptionPolyfort® FPP 2067HU is a unique high flow, UV stabilized high heat resistant impact polypropylene available in matched automotive colors. It molds to a fine appearance with good scrat..
Flexural Modulus	1.65 GPa	239 ksi	1.3 mm/min, tangent; ASTM D790
A. Schulman PP 3466-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3466-01 is a homopolymer polypropylene with the addition of antistatic. This product enhances processing with fast cycle times in injection molding.ApplicationPP 3466-01..
Flexural Modulus	1.65 GPa	239 ksi	1.3 mm/min, tangent; ASTM D790
A. Schulman PP 3466-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3466-01 is a homopolymer polypropylene with the addition of antistatic. This product enhances processing with fast cycle times in injection molding.ApplicationPP 3466-01..
Flexural Modulus	1.65 GPa	240 ksi	1% Secant; ASTM D790
Washington Penn Homopolymer Polypropylene 10% Calcium Carbonate Filled Calcium carbonate-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug pa..
Flexural Modulus	1.65 GPa	240 ksi	ASTM D790
A. Schulman POLYTROPE™ TPP 524 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 524 is an injection molding grade olefinic thermoplastic elastomer. This mineral filled product is recommended for applications requiring high stiffness and low thermal exp..
Flexural Modulus	1.65 GPa	239 ksi	ASTM D790
Total PPC 4481WZ Polypropylene, Impact Copolymer TOTAL Petrochemicals Polypropylene 4481WZ is a nucleated impact copolymer with a Melt Flow index of 4.0 g/10 min.TOTAL Polypropylene 4481WZ is characterized by a good stiffness/impact balance couple..
Flexural Modulus	1.65 GPa	240 ksi	ASTM D790
Total PSI 960E Polystyrene Polystyrene 960E is a high impact polystyrene designed for extrusion/thermoforming applications that require exceptional resistance to attack from fats and oils. This ESCR material is used for lids ..
Flexural Modulus	1.65 GPa	240 ksi	ASTM D790
A. Schulman COMTUF® 420 Impact Modified PBT Information provided by A. Schulman.
Flexural Modulus	1.65 GPa	240 ksi	1.3mm per min, 1% secant; ASTM D790
Formosa Plastics Formolene® 5142K Extrusion - Sheet - Thermoforming Polypropylene HomopolymerApplications: Extrusion, Sheet and Thermoforming ApplicationsFormolene 5142K is a high viscosity homopolymer designed primarily for thermoformed cups and container applications. It contai..
Flexural Modulus	1.65 GPa	239 ksi	1.3 mm/min, tangent; ASTM D790
A. Schulman PP 3466-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3466-01 is a homopolymer polypropylene with the addition of antistatic. This product enhances processing with fast cycle times in injection molding.ApplicationPP 3466-01..
Flexural Modulus	1.65 GPa	239 ksi	ASTM D790
Teknor Apex Sinpolene CPP1020 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Calcium Carbonate Filler, 20% Filler by Weight Features: Homopolymer Uses: Appliance Components; Furniture; Housings F..
Flexural Modulus	1.65 GPa	240 ksi	ASTM D790
Amco PRIMATOP HDPE 006964 Blow Molding Polyethylene HDPE 004955HP features excellent stiffness to ESCR ratio and good impact resistance. Applications include oil bottles, household and industrial chemical containers, and personal care products.Former..
Flexural Modulus	1.65 GPa	239 ksi	SAE J949
Azdel SuperLite® SL551600-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness) AZDEL SuperLite® SL551600-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic..