Lanxess Durethan® BM 240 H3.0 000000 Nylon 6, 40% Mineral
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BM 240 H3.0 000000 Nylon 6, 40% Mineral.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 40% mineral, injection molding, heat-ageing stabilized, low tendency to warp, isotopic properties
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ISO 1183 |
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ISO 60 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 6.0 % | 6.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Thickness 2.00 mm |
0.0080 in/in @Thickness 0.0787 in |
Mold Temp 80°C; Melt Temp 280°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 2.00 mm |
0.0080 in/in @Thickness 0.0787 in |
Mold Temp 80°C; Melt Temp 280°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Conditioned; ISO 527-1,-2 |
| 85.0 MPa | 12300 psi | ISO 527-1,-2 | |
| Elongation at Break | 6.0 % | 6.0 % | ISO 527-1,-2 |
| 40 % | 40 % | Conditioned; ISO 527-1,-2 | |
| Tensile Modulus | 2.20 GPa | 319 ksi | Conditioned; ISO 527-1,-2 |
| 5.80 GPa | 841 ksi | ISO 527-1,-2 | |
| Flexural Strength | 65.0 MPa @Strain 8.00 % |
9430 psi @Strain 8.00 % |
Conditioned; ISO 178 |
| 130 MPa @Strain 5.50 % |
18900 psi @Strain 5.50 % |
ISO 178 | |
| Flexural Yield Strength | 60.0 MPa @Strain 3.50 % |
8700 psi @Strain 3.50 % |
Conditioned; ISO 178 |
| 140 MPa @Strain 3.50 % |
20300 psi @Strain 3.50 % |
ISO 178 | |
| Flexural Modulus | 2.00 GPa | 290 ksi | Conditioned; ISO 178 |
| 5.50 GPa | 798 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1U |
| 85.0 kJ/m² @Temperature -30.0 °C |
40.4 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1U | |
| 100 kJ/m² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Conditioned; ISO 180-1U | |
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eU | |
| 14.0 J/cm² @Temperature 23.0 °C |
66.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Conditioned; ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
Conditioned; ISO 179-1eA | |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179-1eA | |
| Puncture Energy | 65.0 J @Temperature 23.0 °C |
47.9 ft-lb @Temperature 73.4 °F |
ISO 6603-2 |
| 3.00 J @Load <=74.2 kg, Temperature -30.0 °C |
2.21 ft-lb @Load <=164 lb, Temperature -22.0 °F |
ISO 6603-2 | |
| 20.0 J @Load <=309.1 kg, Temperature 23.0 °C |
14.8 ft-lb @Load <=681.4 lb, Temperature 73.4 °F |
ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1,-2 |
| Melting Point | 222 °C | 432 °F | ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75-1,-2 |
| Vicat Softening Point | >= 200 °C @Load 5.10 kg |
>= 392 °F @Load 11.2 lb |
120°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Oxygen Index | 27 % | 27 % | Method A; ISO 4589-2 |
| Glow Wire Test | 650 °C @Diameter 2.00 mm |
1200 °F @Diameter 0.0787 in |
IEC 60695-2-12 |
| Shrinkage | 0.30 % @Temperature 120 °C, Time 14400 sec |
0.30 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| 0.30 % @Temperature 120 °C, Time 14400 sec |
0.30 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.5 @Frequency 100 Hz |
4.5 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm @Thickness 1.00 mm |
889 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.024 @Frequency 1.00e+6 Hz |
0.024 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.025 @Frequency 100 Hz |
0.025 @Frequency 100 Hz |
IEC 60250 | |
| Comparative Tracking Index | 550 V | 550 V | Solution A, Rating; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 °C | 554 °F | Processing conditions for test specimens; ISO 294 |
| 280 - 300 °C | 536 - 572 °F | Recommended | |
| Mold Temperature | 80.0 °C | 176 °F | Processing conditions for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | Recommended | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 1.12 % | 0.030 - 1.12 % | Residual; Acc. To Karl Fischer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flammability | Passed US-FMVSS302 | ISO 3795 |
| ISO Shortname | ISO 1874-PA 6,GHR,14-060,MD40 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics EXTEM VH1003M PEI Copolymer (Asia Pacific)
- SABIC Innovative Plastics Cycoloy® CX2142ME PC+ABS (Europe-Africa-Middle East)
- Momentive Performance Materials RTV6428 Dark Gray General Purpose Potting/Encapsulating Compound
- SABIC Innovative Plastics ULTEM HU1010 PEI
- Teknor Apex APEX® 82-E211-B Polyvinyl Chloride, Flexible
- Styrolution Terblend® N NG-02 UV ABS / PA, 8% Glass filled
- Teknor Apex Uniprene® UN-1373G Thermoplastic Vulcanizate
- Diamond Polymers ASA S950
- DuPont Teijin Films Mylar® M461 Polyester Film, 60 Gauge
- 3M Scotchcal™ 8662 Graphic Film
Copyright © lookpolymers.com All Rights Reserved