Kingfa HF-618 Flame Retardant ABS

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer Kingfa Sci. & Tech. Co.
Trade Name
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Kingfa HF-618 Flame Retardant ABS.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Features:UL 94 V-0 @ 1.6-3.0mmHigh toughnessEasy flowApplications:Injection moldingShell of applianceCD-ROMPower switchInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
<br>@Temperature 23.0 °C
 1.18 g/cc
<br>@Temperature 73.4 °F
 ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
<br>@Temperature 23.0 °C
 0.0040 - 0.0070 in/in
<br>@Temperature 73.4 °F
 ASTM D955
Melt Flow 3.5 g/10 min
<br>@Load 5.00 kg,<br> Temperature 200 °C
 3.5 g/10 min
<br>@Load 11.0 lb,<br> Temperature 392 °F
 ASTM D1238
40 g/10 min
<br>@Load 10.0 kg,<br> Temperature 220 °C
 40 g/10 min
<br>@Load 22.0 lb,<br> Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 100
100
ASTM D785
Tensile Strength at Break 40.0 MPa
5800 psi
50mm/min; ASTM D638
Elongation at Break 15 %
15 %
50mm/min; ASTM D638
Flexural Strength 60.0 MPa
8700 psi
2mm/min; ASTM D790
Flexural Modulus 2.00 GPa
290 ksi
2mm/min; ASTM D790
Izod Impact, Notched 1.85 J/cm
<br>@Thickness 6.40 mm,<br> Temperature 23.0 °C
 3.47 ft-lb/in
<br>@Thickness 0.252 in,<br> Temperature 73.4 °F
 ASTM D256
2.03 J/cm
<br>@Thickness 3.20 mm,<br> Temperature 23.0 °C
 3.80 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 87.0 °C
<br>@Thickness 6.40 mm
 189 °F
<br>@Thickness 0.252 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 77.0 °C
<br>@Thickness 6.40 mm
 171 °F
<br>@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 85.0 °C
<br>@Load 5.00 kg
 185 °F
<br>@Load 11.0 lb
 50°C/min; ASTM D1525
95.0 °C
<br>@Load 1.00 kg
 203 °F
<br>@Load 2.20 lb
 120°C/min; ASTM D1525
Flammability, UL94 V-0
<br>@Thickness 1.60 mm
 V-0
<br>@Thickness 0.0630 in
V-0
<br>@Thickness 3.00 mm
 V-0
<br>@Thickness 0.118 in
5VB
<br>@Thickness 2.00 mm
 5VB
<br>@Thickness 0.0787 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
ASTM D257
Dielectric Strength 23.0 kV/mm
584 kV/in
ASTM D149
Processing Properties Metric English Comments
Processing Temperature <= 230 °C
<= 446 °F
Rear Barrel Temperature 160 - 180 °C
320 - 356 °F
Start Point: 170°C
Middle Barrel Temperature 170 - 190 °C
338 - 374 °F
Start Point: 180°C
Front Barrel Temperature 180 - 210 °C
356 - 410 °F
Start Point: 190°C
Melt Temperature 170 - 210 °C
338 - 410 °F
Start Point: 190°C
Mold Temperature 30.0 - 60.0 °C
86.0 - 140 °F
Start Point: 50°C
Drying Temperature 70.0 - 80.0 °C
<br>@Time 7200 - 14400 sec
 158 - 176 °F
<br>@Time 2.00 - 4.00 hour
 Pre-dry
Back Pressure 0.000 - 1.00 MPa
0.000 - 145 psi
Descriptive Properties Value Comments
Injection Speed Slow to Moderate