- Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled
- Ravago Manufacturing Americas Hylac® GP74G30 ABS, 30% Glass Fiber Reinforced
Ravago Manufacturing Americas Hylac® GP74G30 ABS, 30% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylac® GP74G30 ABS, 30% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | 0.125 in; ASTM D955 |
| Melt Flow | 1.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 65.5 MPa | 9500 psi | ASTM D638 |
| Elongation at Break | 1.0 % | 1.0 % | ASTM D638 |
| Flexural Yield Strength | 114 MPa | 16500 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 109 °C | 228 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 191 - 199 °C | 375 - 390 °F | |
| Middle Barrel Temperature | 204 - 221 °C | 400 - 430 °F | |
| Front Barrel Temperature | 210 - 224 °C | 410 - 435 °F | |
| Nozzle Temperature | 210 - 229 °C | 410 - 445 °F | |
| Melt Temperature | 241 °C | 465 °F | |
| Mold Temperature | 48.9 - 60.0 °C | 120 - 140 °F | |
| Moisture Content | <= 0.10 % | <= 0.10 % | |
| Injection Pressure | 7.24 - 8.27 MPa | 1050 - 1200 psi | |
| Back Pressure | 0.483 - 0.827 MPa | 70.0 - 120 psi | |
| Shot Size | 40 - 80 % | 40 - 80 % | |
| Screw Speed | 50 - 70 rpm | 50 - 70 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure | 900 to 1000 psi | |
| Injection Rate | Slow-Moderate |
Users viewing this material also viewed the following:
- Dow Isoplast® 151 Polyurethane (PUR-RT), Impact Modified (discontinued **)
- PolyOne Geon™ Vinyl Flexible B5D02 Polyvinyl Chloride, Flexible (PVC, Flexible)
- DuPont Elvax® 462 Ethylene-Vinyl Acetate Copolymer Resin (discontinued **)
- Stir SpA FB 70 E (PVC)
- Samsung Cheil Industries Infino® LB-3150GW PC, 15% Glass Filled High Impact
- Solvay MACKADET® CA-ND Surfactant
- Colorite Polymers Elastichem 8011TX-02 Vinyl Compound
- Dow Corning 37 EMULSION
- DuPont Appeel® LSR11D625 Lidding Sealant Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved