Polymer Property : Flexural Modulus = 2.00 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	2.00 GPa	290 ksi	ASTM D790
Polymer Resources PC-IM1-UV Polycarbonate, Impact Modified, Low Flow, UV-stabilized Polycarbonate, Impact Modified, Low Flow, UV-stabilizedProcess: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inform..
Flexural Modulus	2.00 GPa @Temperature 23.0 °C	290 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB POLYfill PPH BK901213 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Modulus	2.00 - 2.90 GPa	290 - 421 ksi	Average value: 2.54 GPa Grade Count:5
Overview of materials for Polycarbonate/Styrenic Alloy This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/Styrenic Alloy". Each property range of values reported is minimum and maximum values of a..
Flexural Modulus	2.00 GPa	290 ksi	2mm/min; ASTM D790
Kingfa FRHIPS-960PC Flame Retardant Polystyrene Features:UL 94 V-0 @ 3.2mmNon-DPO, UV stabilityExcellent heat stabilityExcellent electrical propertiesApplications:Injection moldingGas moldingTV and audio housingElectrical appliance housingInforma..
Flexural Modulus	2.00 GPa	290 ksi	2 mm/min; ISO 178
Inno-Comp INNOPOLÂ® CS 2-9110 10% Talc-Filled Polypropylene Block-Copolymer INNOPOLÂ® CS 2-9110 is a 10% talc-filled compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOLÂ® CS 2-9110 is developed for producing..
Flexural Modulus	2.00 GPa	290 ksi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DL004 PC (Asia Pacific) LNP* Lubricomp* DL004 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated.
Flexural Modulus	2.00 GPa	290 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® 357 PBT+PC PC/PBT, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures.
Flexural Modulus	2.00 GPa	290 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics XenoyÂ® CL101 PBT+PC (Europe-Africa-Middle East) Xenoy CL101 is an unfilled, impact modified PC/PBT blend with excellent solvent resistance and low-temperature ductility. It has a proven track record in off-line painted exterior automotive applica..
Flexural Modulus	2.00 GPa	290 ksi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics XenoyÂ® IQ1103R PBT+PC Xenoy* Resin iQ1103R - Environmetally responsible, sustainable, and low carbon footprint resin. Xenoy iQ1103R is an unreinforced, impact modified PC + iQ-PBT alloy with excellent low temperature im..
Flexural Modulus	2.00 GPa	290 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics XYLEX X7300 PC+POLYESTER PC+POLYESTER unreinforced alloy. High flow, chemically resistant with excellent optical quality. UV-stabilized.
Flexural Modulus	2.00 GPa	290 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics XYLEX X7300 PC+POLYESTER (Europe-Africa-Middle East) PC+POLYESTER unreinforced alloy. High flow, chemically resistant with excellent optical quality. UV-stabilized.
Flexural Modulus	2.00 GPa	290 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics XYLEX X8409AC PC+POLYESTER (Europe-Africa-Middle East) PC + Polyester, Injection (Blow) Molding, or Extrusion Blow molding grade, Chemical Resistance and Transparency
Flexural Modulus	2.00 GPa	290 ksi	ASTM D790
Techmer ES PlaslubeÂ® PC-50/TF/13/SI/2 BK3585 Polycarbonate
Flexural Modulus	2.00 GPa	290 ksi	ISO 178
SABIC Innovative Plastics LNP Thermotuf R1000EI2 PA 66 (Asia Pacific) High Impact Nylon 66 compound containing Impact Modifier.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Modulus	2.00 GPa	290 ksi	ISO 178
SABIC Innovative Plastics LNP Thermotuf U1000AIS PPA LNP* Thermotuf* U1000AIS is a compound based on Polyphthalamide resin. Added features of this material include: High Impact, Heat Stabilized.This data was supplied by SABIC-IP for the Americas regi..
Flexural Modulus	2.00 GPa	290 ksi	ISO 178
SABIC Innovative Plastics LNP Thermotuf U1000AIS PPA (Asia Pacific) LNP* Thermotuf* U1000AIS is a compound based on Polyphthalamide resin. Added features of this material include: High Impact, Heat Stabilized.This data was supplied by SABIC-IP for the Asia Pacific ..
Flexural Modulus	2.00 GPa	290 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM STM1700 PEI Copolymer (Europe-Africa-Middle East) Siltem STM1700 is a flexible copolymer designed for wire and cable applications. It offers a halogen free (according VDE 0472) flame retardant solution that also offers low smoke emission and toxici..
Flexural Modulus	2.00 GPa	290 ksi	ISO 178
Styrolution TerblendÂ® N NM-21 XP ABS+PA (Dry) Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
Flexural Modulus	2.00 GPa	290 ksi	ASTM D790
A. Schulman POLYFORT™ FPP 4020 20% Mineral-Filled Polypropylene DescriptionPolyfort® FPP 4020 is a 20% mineral-filled polypropylene designed for use when improved heat resistance and high stiffness is needed.Information provided by A. Schulman.
Flexural Modulus	2.00 GPa	290 ksi	ASTM-D790
Polyram PlusTek PA810 Nylon 6.6, Impact Modified Impact modified polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Modulus	2.00 GPa	290 ksi	ASTM-D790
Polyram RamTough RZ309G18 Polycarbonate, 18% Glass Fiber 18% glass fiber reinforced polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Modulus	2.00 GPa	290 ksi	ASTM D790
Clariant Renol PCSP0007 Polycarbonate/Polyester Alloy Data provided by Clariant Masterbatches
Flexural Modulus	2.00 GPa	290 ksi
CMW® 3950 AMS-T-21014 ASTM B777 High Density Machinable Tungsten Uses: Radiation Shielding, High Mass, Gyro, Ordnance. Machinability is similar to gray iron.Information provided by CMW Inc.
Flexural Modulus	2.00 GPa	290 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP CL002 PS (Europe-Africa-Middle East) LNP* LUBRICOMP* CL002 is a compound based on Polystyrene resin containing PTFE. Added features include: Internally Lubricated.
Flexural Modulus	2.00 - 24.1 GPa	290 - 3500 ksi	Average value: 7.17 GPa Grade Count:230
Overview of materials for Polyethersulfone (PES) This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone". Each property range of values reported is minimum and maximum values of appropriate M..
Flexural Modulus	2.00 GPa	290 ksi	2 mm/min; ISO 178
Sax Polymers SAXALEN PPC339T20 Polypropylene Copolymer, 20% Talc Filled SAXALEN PPC339T20 is a 20% mineral filled Polypropylene - Copolymer intended for injection molding with good flow properties und higher stiffness. The PP-Copolymer has low warpage behaviors and good..
Flexural Modulus	2.00 GPa	290 ksi	ASTM D790
A. Schulman POLYFORT™ FXP 1245U UV Stable Copolymer Polypropylene DescriptionPolyfort® FXP 1245U is a 40% CAC03 filled UV stable copolymer polypropylene product. Information provided by A. Schulman.
Flexural Modulus	2.00 GPa	290 ksi	STN EN ISO 178
Plastcom SLOVALEN PH 51 T 10 Polypropylene Homopolymer, 10% Mineral Filled FeaturesModified homopolymer PP for injection moulding with the content of 10% mineral filler. Increased rigidity, strength and thermal use up to 120°C. Decreased shrinkage. General application ..
Flexural Modulus	2.00 GPa	290 ksi	ASTM D790
Rochling Engineered Plastics Polystone® PVDF Extruded Sheet Information provided by Röchling Engineered Plastics.
Flexural Modulus	2.00 GPa	290 ksi	ASTM D 790
Shakespeare Isocor™ HW29TL Nylon 610 Isocor™ HW29TL is an ultra low viscosity PA-610 with excellent melt flow characteristics. Isocor™ HW29TL is specifically formulated for thin wall or high speed injection molding applications. ..