Polymer Property : Tensile Strength at Break = 12300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	85.0 MPa	12300 psi	STN EN ISO 527-2
Plastcom PLASTAMID® 66 BT N 27 B PA66 PA66 for compounding, modified for general use, with excellent manufacturing properties. Use: automotive, engineering, electrical and consumer-goods industry - electrical tools, fasteners, clamps, h..
Tensile Strength at Break	85.0 MPa	12300 psi
Plastcom SLOVALEN PH 49 GF 25 PP, 25% glass fibre, mod. of mech. properties FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 25 % glass fibre, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP..
Tensile Strength at Break	84.8 MPa	12300 psi	Type I, 5.1 mm/min; ASTM D638
PolyOne Nymax™ 600 A Zip 23 Natural 1 Polyamide 6 Alloy (Nylon 6 Alloy) The Nymax® 600 Blend Series of nylon 6 materials are salt-and-pepper pelletized blends combining select nylon resins and process aids, performance modifiers, and color concentrates. These materials..
Tensile Strength at Break	85.0 MPa	12300 psi	50 mm/min; ASTM D638
Ovation Polymers Opnyl OP6GF15 Nylon 6, 15% Glass Reinforced, Conditioned Nylon 6 - Glass reinforced (15 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the m..
Tensile Strength at Break	85.0 MPa @Temperature 23.0 °C	12300 psi @Temperature 73.4 °F	ISO 527-2/5
PolyOne Bergadur™ PB400 G30 H UF UV Polybutylene Terephthalate (PBT) Information provided by PolyOne
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527-2
Pasargad Polymer Peyvand Pasamid 3P-H2000W Nylon 66 Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Electrical PartsFastenerHousingInformation provided by Pasargad Polymer Peyvand Co
Tensile Strength at Break	85.0 MPa	12300 psi	cond.; ISO 527-1, -2; 5 mm/min
Lanxess DurethanÂ® AM 40 X H2.0 901510 Nylon 66, Glass Fiber/Mineral Reinforced PA 66, 40% glass fibers/mineral, injection molding, heat-aging stabilized, low tendency to warpInformation provided by LANXESS.
Tensile Strength at Break	85.0 MPa	12300 psi	d.a.m.; ISO 527-1, -2; 5 mm/min
Lanxess DurethanÂ® BKV 215 000000 Nylon 6-Copolymer, Glass Fiber Reinforced, Impact Modified PA 6-Copolymer, 15% glass fibers, injection molding impact modifiedInformation provided by LANXESS.
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527-1,-2
Lanxess DurethanÂ® BM 240 H3.0 000000 Nylon 6, 40% Mineral PA 6, 40% mineral, injection molding, heat-ageing stabilized, low tendency to warp, isotopic properties
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527 Type 1A
Solvay TECHNYLÂ® B 218L V20 Black 44 N PA66, 25% glass fiber, Conditioned Description: Copolyamide 66/6, reinforced with 20% of glass fiber, for injection molding, heat stabilized with improved UV ageing resistanceAvailable in: Asia Pacific and EuropeProduct Applications:..
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RAL23S PA 66 (Asia Pacific) LNP LUBRICOMP* RAL23S is a compound based on Nylon 66 resin containing Aramid Fiber, PTFE. Added features of this material include: Heat Stabilized.
Tensile Strength at Break	85.0 MPa	12300 psi	50 mm/min; ISO 527
SABIC Innovative Plastics ULTEM 1010F PEI (Europe-Africa-Middle East) Transparent, enhanced flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 and 5VA listing. US FDA and EU Food Contant compliant. Effective June, 2007 this grade will no longer be support..
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Ultem 1010KM PEI (Europe-Africa-Middle East) Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Ultem 1010RV PEI (Europe-Africa-Middle East) Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card.This data was supplied by SABIC-IP for the Europe-Afr..
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Ultem 1010V PEI Transparent, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card. US FDA and EU Food Contact compliant, NSF 51 listing.This data wa..
Tensile Strength at Break	85.0 MPa	12300 psi	50 mm/min; ISO 527
SABIC Innovative Plastics ULTEM 1100 PEI (Europe-Africa-Middle East) Standard flow Polyetherimide (Tg 217C). UL94 V0, V2 and 5VA listing.
Tensile Strength at Break	85.0 MPa	12300 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem 1100EF PEI (Asia Pacific) Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, U.S. FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Ultem 1100FV PEI Standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card. US FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for th..
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM 1100V PEI (Asia Pacific) Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 VO and 5VA listing; color dependant, see UL Yellow Card.
Tensile Strength at Break	85.0 MPa	12300 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem 1100V PEI (Europe-Africa-Middle East) Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 VO and 5VA listing; color dependant, see UL Yellow Card.This data was supplied by SABIC-IP for the Europe-Africa-Middle Eas..
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM CRS5011R PEI (Asia Pacific) Enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming.
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM HU1000 PEI Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI)..
Tensile Strength at Break	85.0 MPa	12300 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM HU1110 PEI Enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contac..
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® 815UX PBT (Europe-Africa-Middle East) VALOX 815UX is a 15% glass reinforced PBT+PET blend with improved surface appearance and excellent UV performance.
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527-93
Wellman Wellamid® NY1718-N1 General Purpose Nylon 6 Description: General Purpose Nylon 6Information provided by Wellman.
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
CP-Polymer-Technik Wellamid® 6600 MRGV 25/15 HWCP 25% Mineral and 15% Glass Fiber Nylon 66, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Strength at Break	85.0 MPa	12300 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® TSG-15/4 PA666-GF15 Information provided by EMS Grivory
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527-1/-2
DSM Akulon® K224-PG6 Impact Modified Nylon 6-30% Glass Reinforced (European and Asian Grade) (Cond) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier ..
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527-1/-2
BASF Ultradur® B 4300 G2 FC 10% Glass Filled PBT Description: The BASF Ultradur® FC (Food Contact) grades enable the industry to develop products for food contact applications which are in compliance with multiple regional food contact regulation..
Tensile Strength at Break	85.0 MPa	12300 psi
LATI Latilub 88/50-30GRT PEEK, Graphite/PTFE Filled Self-lubricating product based on Polyetheretherketone (PEEK). Graphite / PTFE.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indu..