BASF Luranyl® KR 2454/3 G4 Polyphenylene Ether + Styrene-Butadiene Blend, 20% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled , Styrene-Butadiene
Manufacturer BASF
Trade Name Luranyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Luranyl® KR 2454/3 G4 Polyphenylene Ether + Styrene-Butadiene Blend, 20% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Glass fiber reinforced grade containing halogen-free flame-retardant; for moldings with high heat resistance and stiffness (e.g. relay parts, controller and switch housings).Data was collected by ISO methods and provided by BASF.
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
Water Absorption 0.40 %
0.40 %
Moisture Absorption at Equilibrium 0.15 %
0.15 %
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
High Load Melt Index 15 g/10 min

@Load 21.6 kg,
Temperature 250 °C
15 g/10 min

@Load 47.6 lb,
Temperature 482 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 90.0 MPa
13100 psi
Elongation at Break 3.0 %
3.0 %
Tensile Modulus 6.50 GPa
943 ksi
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
4.00 J/cm²

@Temperature -30.0 °C
19.0 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
1.20 J/cm²

@Temperature -30.0 °C
5.71 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 35.0 µm/m-°C

@Temperature 20.0 °C
19.4 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Deflection Temperature at 1.8 MPa (264 psi) 135 °C
275 °F
Vicat Softening Point 142 °C
288 °F
Flammability, UL94 V-1

@Thickness 3.20 mm
V-1

@Thickness 0.126 in
Oxygen Index 29 %
29 %
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Constant 3.0

@Frequency 100 Hz
3.0

@Frequency 100 Hz
3.0

@Frequency 1e+6 Hz
3.0

@Frequency 1e+6 Hz
Dielectric Strength 85.0 kV/mm
2160 kV/in
Dissipation Factor 0.0030

@Frequency 1e+6 Hz
0.0030

@Frequency 1e+6 Hz
Comparative Tracking Index 225 V
225 V